Syntheses and Lyotropic Liquid Crystal Properties of a Series of Sandwich-Type Tungstoarsenates Heteropoly Compounds with As/W Ratio of 4/30
Rudan Huang,Lihua Bi,Enbo Wang,Baoli Fei,Lin Xu,Changwen Hu
DOI: https://doi.org/10.1007/bf02887119
1999-01-01
Abstract:A series of sandwich-type tungstoarsenates heteropoly compounds with As/W ratio of 4/30, Na 16 [As 4 W 30 M 4 (H 2 O) 2 O 112 ].XH 2 O (M = Zn, Cu, Co, Ni, Mn and Cd), have been synthesized for the first time and structurally characterized by elemental analysis, IR and 183 W NMR spectra. The crystal structure of Na 16 [As 4 W 30 Cu 4 (H 2 O) 2 O 112 ] · 63H 2 O was determined to be a triclinic system, of P1 symmetry, a = 1.272 l(3) nm, b = 2.451 6(5) nm, c = 2.6.15 0(5) nm, α = 89.90(3)∘, β =77.32(3)∘, γ = 89.96(3)∘, Z = 2. Using tetrahepty lammonium bromide as a phase transfer reagent, [As 4 W 30 Cu 4 (H 2 O) 2 O 112 ] 16 ™was transferred from aqueous solution to organic phase (benzene), and the heteropolyanion lost the coordination water molecules to form the coordination-unsaturated ion. After lactic acid was added to the benzene solution, the coordination-saturation was recovered. By esterification reaction between lactic acid and cholesterin, the latter was attached to the heteropolyanion indirectly. Therefore, a new type of lyotropic liquid crystal was obtained, which was characterized by a polarimicroscope, DSC and variable temperature wide-angle X-ray diffraction.