Abstract:Ethanol as a precursor has proven effective in the chemical vapor deposition (CVD) synthesis of graphene on both Ni foils and Cu capsule substrates. For applications of graphene in field effect transistors or as transparent conducting electrodes, larger singe-crystal graphene without any grain boundaries shows superior electrical performance and has attracted enormous interests. Here we report a protocol to synthesize large graphene single crystals (up to 600 μm) using ethanol as precursor on commercially-available polycrystalline Cu foils. We explored the mechanism by studying the influences of different growth parameters such as pressure, flow rate and temperature. Low partial pressure and low flow rate of ethanol is essential in achieving low nucleation density over the metal surface and therefore large graphene grains can be obtained. We found that growth temperature dramatically affects the crystallinity and the growth rate of graphene grains. Moreover, this CVD growth of large graphene single crystals involves no electro-polishing or annealing treatments to the metal surface, presenting a significant simplification to the current graphene synthesis process.

Selective fabrication of carbon nanowires, carbon nanotubes, and graphene by catalytic chemical liquid deposition

Large‐Scale Synthesis of Rings of Bundled Single‐Walled Carbon Nanotubes by Floating Chemical Vapor Deposition

Synthesis of Carbon Nanotubes by Decomposing Alcohol

The influence of ethanol on the growth and structure of carbon nanotubes

Controllable Synthesis of Carbon Nanotubes with Ultrafine Inner Diameters in Ethanol Flame

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Gas-phase synthesis of carbon nanotube-graphene heterostructures

Chemical Vapor Deposition Growth of Large Grapheme Single Crystal from Ethanol

Catalyst-free Growth of Single- to Few-Layered Graphene and Carbon Nanotubes on an Ionic Liquid Surface

Large-Scale Synthesis Of Carbon Nanotubes By An Ethanol Thermal Reduction Process

Selective Synthesis of Carbon Nanofibers with Various Structures Through the Catalytic Pyrolysis of Ethylene

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

Large-Scale and Controllable Synthesis of Metal-Free Carbon Nanofibers and Carbon Nanotubes over Water-Soluble Na2co3

Controllable and Large-Scale Synthesis of Carbon Nanofibers, Bamboo-Like Nanotubes, and Chains of Nanospheres over Fe/Sno2 and Their Microwave-Absorption Properties

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Carbon Nanotubes Synthesized By Rapid Quenching Of Red-Hot Graphite Rod In Ethyl Alcohol

Controlling the Catalytic Synthesis of SiC Nanowires, Carbon Nanotubes, and Graphene from a Multilayer Film Precursor

Synthetic Hierarchical Nanostructures: Growth of Carbon Nanofibers on Microfibers by Chemical Vapor Deposition

Chemical Vapor Deposition Growth of Graphene using Other Hydrocarbon Sources

Chemical vapor deposition of carbon nanotubes on monolayer graphene substrates: reduced etching via suppressed catalytic hydrogenation using C2H4

Controllable bulk growth of few-layer graphene/single-walled carbon nanotube hybrids containing Fe@C nanoparticles in a fluidized bed reactor