Liquid/Liquid Interfacial Suzuki Polymerization Prepared Novel Triphenylamine-Based Conjugated Polymer Films with Excellent Electrochromic Properties
Ling Zhang,Wang Zhan,Yujie Dong,Tao Yang,Cheng Zhang,Mi Ouyang,Weijun Li
DOI: https://doi.org/10.1021/acsami.1c02745
2021-04-22
Abstract:Preparing conjugated polymer films via interfacial Suzuki polymerization is a promising method for obtaining desirable electrochromic materials with desired structures. Here, a series of aryl boronic esters and triphenylamine-based aryl bromides were applied as precursors, and several polymer films were finally obtained via the liquid/liquid interfacial Suzuki polymerization reaction under mild conditions. FT-IR, UV, and Raman as well as electrochemistry, SEM, and EDS results all provide strong evidence for the formation of the desired polymer structures. Among them, the <b>TPA-Wu (</b>containing triphenylamine and alkyl-fluorene) film exhibits the best film-forming quality. Besides, these polymer films were applied in electrochromic applications. The results show that electrochromic properties can be affected by the quality of film formation. It is worth mentioning that the <b>TPA-Wu</b> film could achieve excellent electrochromic properties with reversible multicolor changes from transparent yellow to orange-red to blue-green under varying potentials. Compared to other triphenylamine-based electrochromic materials, the <b>TPA-Wu</b> film possessed the most desirable coloring efficiency, higher optical contrast, and shorter switching time. This work provides an existing general approach of liquid/liquid interfacial Suzuki polymerization for constructing conjugated polymer films toward electrochromic applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02745?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02745</a>.Synthesis routes of the precursors; the picture before the addition of the organic phase; digital photograph of the reaction phenomenon at the initial state and final state after 24 h; Raman spectroscopy of <b>2TPA-4Br</b> precursor and <b>2TPA-B</b> and <b>2TPA-Wu</b>; cyclic voltammetry of <b>TPA-3Br</b> and <b>TPA-B</b>, <b>2TPA-B</b>, and <b>2TPA-Wu</b>; UV–vis absorbance spectroscopy of <b>TPA-3Br</b>, <b>TPA-B</b>, <b>2TPA-B</b>, and <b>2TPA-Wu</b>; cyclic voltammograms of the <b>TPA-B</b>, <b>2TPA-B</b>, and <b>2TPA-Wu</b> polymer film at different scan rates; scan rate vs anodic and cathodic current density graphs of the <b>TPA-B</b>, <b>2TPA-B</b>, and <b>2TPA-Wu</b> polymer films; optical contrast and switching time of <b>TPA-B</b>, <b>2TPA-B</b>, and <b>2TPA-Wu</b> (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02745/suppl_file/am1c02745_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology