Abstract:Failure response of the modern high strength steel grades shows a diverse pattern compared to the conventional highly ductile steels. In automotive sheet forming applications of the high strength steels, fracture could be observed prior to necking or the post necking deformation is very limited. The differences in the underlying damage mechanisms contribute to the different ways of damage development and the interaction of damage with plastic localization and strain hardening creates various failure patterns. Therefore, it is critical to clearly identify the phase for damage initiation and understand the relation between plastic localization, damage and fracture, as these patterns significantly influence the safety assessment in the forming process of steels. Inverse modelling approaches are being used to bridge the gap between experiments and numerical simulations. However, this technique shows significant discrepancies when strain heterogeneity is experienced, especially since the determination of the material parameters is based on comparison on a global scale with force and elongation measurements. An iterative finite element model update (FEMU) procedure integrated with optical full field measurement technique was executed which extended the possibilities to identify the material ductile damage and fracture behavior on a local level with significantly higher accuracy. To identify the material plastic and damage behavior of the automotive dual phase steel (DP-K1000) under study, experiments are conducted on dog-bone, notched tensile, central hole and shear specimens at various strain rates. Full field deformation data was obtained by digital image correlation (DIC). A vigorous and general framework for the inverse identification of the strain hardening behavior up to fracture of the automotive high strength steel was studied. A hybrid damage mechanics model (extended Modified Bai-Wierzbicki) that combines a phenomenological criterion for damage initiation related to the microstructure degradation of materials and a continuum damage mechanics based damage evolution law for progressive damage accumulation till final fracture is employed using a VUMAT in the finite element (FE) scheme. To exclude the convergence (plastic instability) problems, a displacement driven finite element simulation was used while minimizing the discrepancy between the experimental and numerical surface strain fields and force values. A visual mapping procedure was adopted to realize identical reference frames and therefore identical peripheries for the specimen in DIC and FE model. This mapping includes a transformation and interpolation function from FE results to the DIC datum points. Successful identification of the material parameters was achieved based on a combined Gauss-Newton and Levenberg-Marquardt algorithm which require the evaluation of the gradient of the objective function to update the unknown parameters in an appropriate direction. The optimization problem of the inverse modelling in the current work was described by a cost function based on the least square norm of the differences of the surface strain fields. Overall cost function formulation is not dependent on the experimental or finite element meshes and includes rigid body motions. The residual was minimized at once for all the displacements by Gauss-Newton scheme in space-time, which is defined by spatial domain and temporal domain. The optimization of the constitutive parameters was directly achieved by minimizing this image residual in an iterative manner. The adopted methodology helped in determining macroscopic crack initiation instant and location from experiments. Local variables such as equivalent plastic strain, stress triaxiality and Lode angle parameter were evaluated from the critical element for the determination of the damage initiation locus which was then fitted by a non-linear least squares method with a trust-region algorithm in Matlab. The identified damage initiation locus and plastic localization phenomena served as an evaluation criteria for the formability of the dual phase automotive steel.

Interaction Effect of Cracks and Anisotropic Influence on Degradation of Edge Stretchability in Hole-Expansion of Advanced High Strength Steel

A Method for Evaluating the Degradation of Edge Stretchability Incorporating Punching Damage Based on Marciniak and Kuczynski Model

Study of Curvature and Pre-Damage Effects on the Edge Stretchability of Advanced High Strength Steel Based on a New Simulation Model

Experiments and FE Simulation of Edge Cracking Considering Prehardening after Blanking Process

Influence of Sheet Metal Pre-forming on Edge Crack Sensitivity using an AHSS Steel Grade

Influence of Curvature Variation on Edge Stretchability in Hole Expansion and Stretch Flanging of Advanced High-Strength Steel

Damage Evolution in Complex-Phase and Dual-Phase Steels during Edge Stretching

Predicting edge fracture in dual-phase steels: significance of anisotropy-induced localization

Numerical Simulation on Edge Crack of Advanced High-Strength Steel Considering Blanking Induced Damage

Prediction of edge fracture during hole-flanging of advanced high-strength steel considering blanking pre-damage

A New Ductile Fracture Model for Edge Cracking Prediction of Ultra-High Strength Steel Considering Damage Accumulation in Blanking Process

Study of fracture damage criteria and influence of process parameters on punching of hot stamped ultra-high strength steel

Investigations on the Flanging Characteristics of Advanced High-Strength Sheet Metals with Different Sheared Edge Quality

Investigations on Edge Quality and Its Effect on Tensile Property and Fracture Patterns of QP980

Prediction of Hole Expansion Ratio for Advanced High-Strength Steel with Image Feature Analysis of Sheared Edge

Revealing plastic localization and ductile damage initiation features with integrated DIC and FEM

Stamping Failure Analysis of Advanced High Strength Steel Sheet Based on Non-Uniform Local Deformation Through Thickness

Die Structure Analysis Of Stress Distribution During High-Strength Steel Stamping Process And Experimental Validation

Anisotropic Fracture of Advanced High Strength Steel Sheets: Experiment and Theory

Sheet metal forming limits under stretch-bending with anisotropic hardening

Investigation on Wear-Induced Edge Passivation of Fine-Blanking Punch