Amine-Assisted Delaminated 2D Ti 3 C 2 T x MXenes for High Specific Capacitance in Neutral Aqueous Electrolytes
Shan Ren,Jian-Long Xu,Liang Cheng,Xu Gao,Sui-Dong Wang
DOI: https://doi.org/10.1021/acsami.1c06161
2021-07-23
Abstract:Electrochemical capacitors using neutral aqueous electrolytes are safer and cheaper and allow diverse current collectors compared with the counterparts using organic or acidic/alkaline electrolytes. Two-dimensional (2D) MXenes have been demonstrated as the high-capacitive materials with high rate performance. However, MXene electrodes often exhibit a limited capacitance in neutral electrolytes, where the reversible electrochemical reactions rely greatly on the structural and surface properties of MXenes depending on their synthesis methods. Herein, a simple and highly efficient strategy, which combines HF etching of Ti3AlC2 powder and subsequent amine-assisted delamination at a low temperature, is developed to synthesize 2D Ti3C2Tx MXenes. The comprehensive results demonstrate that the enlarged interlayer spacing and the presence of more −O-containing functional groups synergistically contribute to the improvement of capacitive performance in neutral electrolytes. The 2D Ti3C2Tx MXenes show excellent electrochemical performance in various neutral electrolytes, and a high specific gravimetric capacitance of 149.8 F/g is achieved in 1.0 M Li2SO4. Furthermore, the flexible solid-state supercapacitors (SCs) with a neutral PVA/LiCl gel electrolyte possess a superior areal capacitance (163.1 mF/cm2) and high energy density (17.6 μWh/cm2 at 0.07 mW/cm2), together with high user safety. This work provides a promising guideline of synthesis strategy for high-capacitive MXenes used in neutral electrolytes, which may promote the development of safe and flexible power sources with a high energy density.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c06161.Fractions extracted from Ti 2p and O 1s XPS spectra for Ti3C2Tx-TMAOH and Ti3C2Tx-HF samples; SEM images of raw Ti3AlC2 crystals and multilayered Ti3C2Tx after diluted HF etching of Ti3AlC2 for 2 h; digital photographs showing Tyndall scattering effects of Ti3C2Tx-TMAOH nanosheets dispersed in NMP; SEM image of the Ti3C2Tx-HF sample; AFM image of Ti3C2Tx-TMAOH nanosheets; XPS Al 2p and F 1s spectra of Ti3AlC2, Ti3C2Tx-HF, and Ti3C2Tx-TMAOH; XPS C 1s spectra of Ti3C2Tx-HF and Ti3C2Tx-TMAOH and their component peak fitting; CV curves of Ti3C2Tx-HF and Ti3C2Tx-TMAOH samples at scan rates from 0.5 to 100 mV/s in 1.0 M Na2SO4, 0.65 M K2SO4, and 1.0 M MgSO4; GCD curves of Ti3C2Tx-HF and Ti3C2Tx-TMAOH samples at current densities from 0.5 to 50 A/g in 1.0 M Na2SO4, 0.65 M K2SO4, and 1.0 M MgSO4; electrochemical performance of the freestanding Ti3C2Tx-TMAOH film electrode including CV curves, specific capacitance vs scan rate, GCD curves, and EIS spectra in 1.0 M Na2SO4, 0.65 M K2SO4, and 1.0 M MgSO4 (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology