Abstract:Here, we report the successful development of reduced graphene oxide (rGO) (0.1, 0.3 and 0.9 wt.%) reinforced alumina (Al 2 O 3 ) novel nanocomposites by powder metallurgy route. The composite powder samples were prepared using a high-energy dry planetary ball mill for 2 h under an argon atmosphere. Then, the optimized compacted samples (at 170 MPa for 180 s) having high density were sintered at 1450 °C for 180 min. under an argon atmosphere. The characteristics of the materials have been evaluated to improve microstructure, microhardness, and Young's modulus of composites. rGO has 4-5 numbers of graphene sheets with an energy band gap of 2.28 eV and a specific surface area of 509.177 m 2 /g. The rGO retains structural quality before and after making composites with Al 2 O 3 samples. The purity of rGO and Al 2 O 3 /rGO composite samples was confirmed by EDS analysis. While rGO shows peaks of C and O, Al 2 O 3 /rGO (0.1, 0.3, and 0.9 wt.%) composite samples show peaks of Al, O, and C. Micro Raman analysis establishes the successful formation of composite between Al 2 O 3 and rGO. Al 2 O 3 /rGO (0.1, 0.3, and 0.9 wt.%) composite samples mostly show similar kinds of D, G, and 2D peaks as shown by pure rGO. The outstanding result achieved for the typical Al 2 O 3 /rGO (0.3 wt.%) sample showed significantly higher microhardness (2488 ± 12 VHN) and Young's modulus (520 ± 9 GPa) values compared to pure Al 2 O 3 . The microhardness and Young's modulus values of Al 2 O 3 /rGO (0.3 wt.%) composite are more than 79% and 31% compared to those observed for pure Al 2 O 3 . When the rGO amount further increased to 0.9 wt.% in Al 2 O 3 , agglomeration of graphene sheets developed, which caused degradation of the mechanical property of the composite. The excellent outcome of this work further advances critical applications of Al 2 O 3 in various industrial fields.

Mechanical and Thermal Properties of Reduced Graphene Oxide Reinforced Aluminum Nitride Ceramic Composites

Fabrication of Nanocrystalline Zro2 Particle Reinforced Aluminum Alloy Composite by Squeeze Casting Route

Mechanical and dielectric properties of reduced graphene oxide nanosheets/alumina composite ceramics

Study on the Microstructure and Microhardness Behavior of Reduced Graphene Oxide Reinforced Alumina Nanocomposites

Enhancement of Thermal Conductivity and Mechanical Properties of Cu-Reduced Graphene Oxide Composites by Interface Modification

Uniform dispersion of graphene oxide in aluminum powder by direct electrostatic adsorption for fabrication of graphene/aluminum composites.

Graphene oxide/Al composites with enhanced mechanical properties fabricated by simple electrostatic interaction and powder metallurgy

Three Dimensional AlN Skeleton-Reinforced Highly Oriented Graphite Flake Composites with Excellent Mechanical and Thermophysical Properties

Aluminum/graphene Composites with Enhanced Heat-Dissipation Properties by In-Situ Reduction of Graphene Oxide on Aluminum Particles

Nano/microstructures and mechanical properties of Al2O3–TiC ceramic composites reinforced with Al2O3@RGO nanohybrids

Graphene oxide and graphene nanosheet reinforced aluminium matrix composites: Powder synthesis and prepared composite characteristics

Mechanical Properties of Silicon Carbide Composites Reinforced with Reduced Graphene Oxide

Facile Preparation of High-Performance Reduced Graphene Oxide (RGO)/Copper (Cu) Composites Based on Pyrolysis of Copper Formate

Effect of interfacial features on the mechanical and electrical properties of rGO/Al composites

The Influence of Dispersion State of Graphene Sheets on the Microstructure and Thermal Conductivity of Free-Standing Reduced Graphene Oxide Films

Preparation and properties of Cu/RGO composites via H2 reduction and spark plasma sintering

Room and high-temperature mechanical behavior of reduced graphene oxide-aluminum (RGO-Al) composite wire conductors-A micro-mechanical investigation

Enhanced Physical Properties of Γ-Al2o3–rgo Hybrids Prepared by Solvothermal and Hot-Press Processing

Microstructural Evolution and Mechanical Properties of Graphene Oxide-Reinforced Ti6Al4V Matrix Composite Fabricated Using Spark Plasma Sintering

Effect of H 2 Reduction Temperature on the Properties of Reduced Graphene Oxide and Copper Matrix Composites

In situ thermally reduced graphene oxide/epoxy composites: thermal and mechanical properties