Abstract:The effect of the retained austenite (RA) stability on mechanical properties of a medium-carbon transformation-induced-plasticity (TRIP) steel at different deformation temperatures was studied. Two steels were obtained by adjusting the annealing temperature from 780 °C to 820 °C and controlling the isothermal bainitic process, and the carbon content of RA in the steels was 1.2% and 1.4%, respectively. At 25 °C, ultimate tensile strength, yield strength and total elongation of the steel after intercritical annealing at 780 °C were 1390 MPa, 870 MPa and 40%, respectively. When the deformation temperature increased to 200 °C, yield strength nearly kept constant (860 MPa) while total elongation significantly increased to 73%. The stability of RA had a significant influence on the deformation mechanisms of the steel, hence leading to the distinct variation of the mechanical properties. The RA stability increased with increasing deformation temperature to 200 °C, reducing the rate of transformation from RA to martensite and making the TRIP effect more persistently. Meanwhile, due to low solubility of Cu atom and the large number of dislocations acting as fast diffusion channels for Cu and C atoms in transformed martensite, the joint action of the increasing temperature and the continuous TRIP effect promoted the formation of numerous nanosized precipitates including η carbides and Cu particles in the newly formed martensite. As a result, the work hardening rate was significantly increased, improving the ductility without sacrificing the strength. This study provides a strategy to control the deformation mechanisms of medium-carbon TRIP steel, which can tailor the stability of RA according to the requirement of application, so as to obtain a good combination of strength and ductility.

Multi-phase microstructure design of a novel high strength TRIP steel through experimental methodology

Microstructure and dynamic deformation behavior of high strength TRIP steel

Investigate on Ultrahigh-Strength TRIP-aided Autosteel Plate under the Framework of ICME

Microstructures and stability of retained austenite in TRIP steels

Characterization of Microstructures and Tensile Properties of TRIP-aided Steels with Different Matrix Microstructure

Microstructure Control of Hot Rolled Trip Steel Based on Dynamic Transformation of Undercooled Austenite I. Prior Austenite Grain Size

A Novel Mo and Nb Microalloyed Medium Mn TRIP Steel with Maximal Ultimate Strength and Moderate Ductility

A High-Performance TRIP Steel Enhanced by Ultrafine Grains and Hardening Precipitates

Role of Martensite/austenite Constituents in Novel Ultra-High Strength TRIP-assisted Steels Subjected to Non-Isothermal Annealing

Microstructure Evolution During The Production Of Dual Phase And Transformation Induced Plasticity Steels Using Modified Strip Casting Simulated In The Laboratory

Micromechanical behavior of TRIP-assisted multiphase steels studied with in situ high-energy X-ray diffraction

Influence of Original Microstructure on the Transformation Behavior and Mechanical Properties of Ultra-High-strength TRIP-aided Steel

Effects of Retained Austenite Volume Fraction, Morphology, and Carbon Content on Strength and Ductility of Nanostructured TRIP-assisted Steels

Effect of Isothermal Bainitic Processing on Microstructures and Mechanical Properties of Novel Mo and Nb Microalloyed TRIP Steel

Microstructure Evolution and Strain Behavior of a Medium Mn TRIP/TWIP Steel for Excellent Combination of Strength and Ductility

Interplay Between Deformation Behavior and Mechanical Properties of Intercritically Annealed and Tempered Medium-Manganese Transformation-Induced Plasticity Steel

Microstructure and Mechanical Properties of Microalloyed High-Strength Transformation-Induced Plasticity Steels

Optimizing strength & ductility combination of medium-carbon TRIP steel via multi-stage work hardening

Microstructure Evolution and Mechanical Behavior of A Hot-Rolled High-Manganese Dual-Phase Transformation-Induced Plasticity/Twinning-Induced Plasticity Steel

Improving the Stretch Flangeability of Ultra-High Strength TRIP-assisted Steels by Introducing Banded Structure

Multiscale mechanics of TRIP-assisted multiphase steels: I. Characterization and mechanical testing