The effect of ageing on microstructure and mechanical properties of powder Ti-5Al-5Mo-5V-1Cr-1Fe alloy

m m z ahmed,dmytro g savvakin,o m ivasishin,elena v pereloma

DOI: https://doi.org/10.1016/j.msea.2014.03.030

2014-01-01

Abstract:The thermo-mechanically processed powder Ti–5Al–5V–5Mo–1Cr–1Fe alloy was aged at 923K for 1–8h in order to investigate the effect of ageing time on the microstructure–mechanical properties relationships. The microstructures of the alloy after ageing consist of the both primary and secondary α phases with retained β matrix phase. The shift of β peaks in X-ray pattern with ageing time indicates an increase in lattice parameter distortion due to diffusion into the retained β phase of more β stabilisers with smaller atomic radius compared to the elemental Ti. The tensile test results indicate that the sample aged for 1h has achieved the best combination of mechanical properties with ultimate tensile strength of 1194MPa and total elongation of 14.1% among all the experimented conditions. The modified Crussard–Jaoul method is applied to characterise the work hardening behaviour of the alloy.