Toward High-performance Polypropylene via Controlling Crystalline Morphology
Ke Wang,Yan-ling Zhu,Qiang Fu
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.17077
2017-01-01
Acta Polymerica Sinica
Abstract:Polypropylene (PP) is still one of the most important general plastics, and it is of great significance to achieve high-performance PP materials. As a semicrystalline polymer, PP is essentially polymorphism. At least five polymorphs have been identified, i.e., alpha, beta, delta, d and quasi-hexagonal form. Among them, beta form is highly desirable, due to its excellent physical properties. However, beta crystals are hard to be obtained via common crystalline condition. The polymorphic modification by adding beta-nucleator (beta-NA) is a powerful method for achieving dominant beta form and thus tailoring the toughness and thermal stability of PP. In contrast to many past researches which focused on the roles of crystallinity and beta-phase content, a new methodology has been recently suggested which optimized the physical properties of PP by controlling beta-crystalline morphology. Some relevant studies include: (1) to assess the solubility and self-assembly behavior of beta-NA by using temperature gradient (g-T) field; (2) to control the beta-crystalline morphology by processing varables and beta-NA content, and receive super-high toughness and good heat stability; (3) to reveal the rule of stretching-induced porosity in the beta-PP films with different crystalline morphologies. beta-NA of low-molecular-weight is soluble in the melt of PP, which will self-assemble into supermolecular structures prior to the primary crystallization of PP during the cooling process. Such supermolecular structures act as templates for the guidance of PP crystallization, resulting in special crystalline morphologies. By using the g-T technique, the dependence of beta-NA solubility on molten temperature and nucleator loading could be clarified readily. Thus the crystalline morphology of beta-PP is controllable, and different morphologies, such as spherulite, transcrystallinity and flower-like aggregations, are achievable through adjusting the solubility and self-assembly behavior of beta-NA. Special crystalline morphology leads to a significant increase in the tensile ductility of beta-PP. Meanwhile, the heat distortion temperature and homogeneity of microporosity are also strongly dependent on beta-crystalline morphology. Obviously, the manipulation of crystalline morphology is a promising pathway to realize high-performance in crystalline polymers.