WVOx Supported on Industrial Al2O3, SiO2, AC, TiO2–Al2O3 for Catalytic Dehydration of Gas-Glycerol to Acrolein
Xiansong Xia,Liangqi Li,Lin Chen,Qi Yao,Miao Liu,Hai Lan
DOI: https://doi.org/10.1007/s10562-024-04822-8
IF: 2.936
2024-09-14
Catalysis Letters
Abstract:WVO x bi-metal oxides supported on the cost-effective industrial mesoprous Al 2 O 3 , SiO 2 , active carbon (AC), and TiO 2 –Al 2 O 3 with different specific surface areas (WVO/Al 2 O 3 , WVO/SiO 2 , WVO/AC, and WVO/TiO 2 –Al 2 O 3 ) were designed and prepared through co-impregnation method for large-scale bio-glycerol dehydration to acrolein. The XRD, BET, SEM–EDS, XPS, and NH 3 -TPD characterization results revealed the WO 3 –VO x (V 4+ /V 5+ ) species existed with better dispersion, lower molar ratio of V 4+ /V 5+ , and enhanced strength of surface acid sites on the developed mesoporous TiO 2 –Al 2 O 3 in comparison with that on the mesoporous Al 2 O 3 , SiO 2 , and AC, demonstrating strong interaction of WO 3 –VO x species with the TiO 2 –Al 2 O 3 support and accounting for the acrolein selectivity over catalysts following the order of WVO/TiO 2 –Al 2 O 3 (75.8%) > WVO/AC (71.2%) > WVO/SiO 2 (55.3%) > WVO/Al 2 O 3 (42.8%). Over the WVO/TiO 2 –Al 2 O 3 , gas-glycerol conversion reached above 97.0% with acrolein selectivity of about 75.0% under the gas hourly space velocity (GHSV) of 120–360 h −1 , and maintained an improved catalytic stability.
chemistry, physical