Modulate the Morphology and Spectroscopic Property of Gold Nanoparticle Arrays by Polymer-Assisted Thermal Treatment
Zibo Li,Jingjie Nan,Xuemin Zhang,Shunsheng Ye,Huaizhong Shen,Shuli Wang,Liping Fang,Peihong Xue,Junhu Zhang,Bai Yang
DOI: https://doi.org/10.1021/acs.jpcc.5b02263
2015-01-01
The Journal of Physical Chemistry C
Abstract:In this article, we report the morphology modulation of gold nanoparticle (NP) arrays by polymer-assisted thermal treatment. Simultaneously, localized surface plasmon resonance (LSPR) UV-vis extinction (absorption plus scattering) of gold NP arrays was monitored and analyzed. First, through horizontal lifting, gold NP monolayers were transferred from a water/hexane interface to glass slides. After thin polymer films were spin-coated on the gold NP monolayers, thermal: treatment was carried out, which results in apparent color changes in the obtained samples. The color changes could be attributed to the shift of the surface plasmon band (SPB), along with increasing gold NP size and interparticle distance. We found that different polymers show different effects on the modulation of gold NPs' morphology, accompanied by different shifts of the SPB. Polymers with relatively lower glass transition temperatures (T-g), such as poly(methyl methacrylate), promoted gold NPs to merge into spheres, while polymers with relatively higher T-g, such as polyphenylene sulfone resins, inhibited the fusion of gold NPs, which collapsed as a whole slice. We believe that the difference should be attributed to the polymer chain's ability to move during heating. Therefore, the temperature of thermal treatment and the T-g of the polymer play critical roles in the merging process of gold NPs. Moreover, through combining colloidal lithography technology, patterned gold NP monolayers have been fabricated. The current strategy is simple and facile to control the morphology of gold NP arrays, as well as to control their optical properties.