Abstract:Carbon nanofiber (CNF) made of inexpensive and bio-renewable raw materials can provide a pathway to lowering manufacturing cost of CNFs for structural composite applications. In this study, lignin nanofiber (LNF) mats were fabricated by electrospinning of a blend solution of polyacrylonitrile (PAN), lignin, and 1 weight percent (wt.%) of polyethylene oxide (PEO) in N, N-dimethylformamide (DMF). The LNFs were then subjected to heat treatment processes including thermostabilization at 240 ◦ C and subsequent carbonization at 1000 ◦ C. The effects of the PAN/lignin mass ratio and the heating rate of thermostabilization on the fiber morphology, fiber diameter, and mechanical properties of the CNF mats were systematically investigated. The scanning electron microscopy (SEM) images showed that as the lignin content in the precursor decreased, the diameter of the as-spun LNFs increased. However, the diameter, surface, and structure of the CNFs did not change significantly. The diameter of CNFs was about 700 nm. The strength of CNF mats increased as the proportion of lignin decreased, for slow heating rates (0.5-2 ◦ C/min). However, with a faster heating rate (5 ◦ C/min), the strength of the CNF mats (with different PAN/lignin ratios) were identical. As the heating rate increased, the strength of the CNF mats increased greatly due to the fusing of the CNFs. The highest strength of the CNF mats was about 68.5 MPa. The diameter and surface features of the CNFs were found to be similar in all the samples (as a function of the heating rate). The strength of the PAN/lignin-based CNF mats was found to be much higher than that of pure PAN-based CNF mats at a fast heating rate (5 ◦ C/min). At slow heating rates of 0.5-2 ◦ C/min, the mechanical properties of PAN/lignin-based CNF and PAN-based CNF mats were similar.

Lignin-based carbon fibers: Carbon nanotube decoration and superior thermal stability

Carbon-nanotube-templated Carbon Nanofibers with Improved Mechanical Performance

Processing, Structure, and Properties of Lignin- and CNT-Incorporated Polyacrylonitrile-Based Carbon Fibers

Highly Strong and Conductive Carbon Fibers Originated from Bioinspired Lignin/Nanocellulose Precursors Obtained by Flow-Assisted Alignment and In Situ Interfacial Complexation

Structure and properties of lignin based carbon nanofibers

Conversion of Lignin-Nanofibers to CNFs

Simultaneously Enhanced Tenacity, Rupture Work, and Thermal Conductivity of Carbon Nanotubes Fibers by Increasing the Effective Tube Contribution

Porous Core-Shell Carbon Fibers Derived from Lignin and Cellulose Nanofibrils

Development of high stiffness carbon fibres from lignin

Preparation of Silver-Plated Carbon Nanotubes/carbon Fiber Hybrid Fibers by Combining Freeze-Drying Deposition with a Sizing Process to Enhance the Mechanical Properties of Carbon Fiber Composites

Single Carbon Fibers with a Macroscopic-Thickness, 3D Highly Porous Carbon Nanotube Coating

Dry-Jet Wet Spinning of Thermally Stable Lignin-Textile Grade Polyacrylonitrile Fibers Regenerated from Chloride-Based Ionic Liquids Compounds

Graphene Interlocking Carbon Nanotubes for High-Strength and High-Conductivity Fibers.

Carbon Nanotube Fibers with Excellent Mechanical and Electrical Properties by Structural Realigning and Densification

A Novel Continuous Carbon Nanotube Fiber/carbon Composite by Electrified Preform Heating Chemical Vapor Infiltration

Layer-by-layer grafting CNTs onto carbon fibers surface for enhancing the interfacial properties of epoxy resin composites

Preparation and Properties of Carbon Fiber/Carbon Nanotube Wet-Laid Composites

Influence of Lignin units on the properties of Lignin/PAN‐derived carbon fibers

Construction of cellulose nanofiber/carbon nanotube synergistic network on carbon fiber surface to enhance mechanical properties and thermal conductivity of composites

Synthesis and characterization of hierarchical suspended carbon fiber structures decorated with carbon nanotubes

Robust Carbon Nanotube Composite Fibers: Strong Resistivities to Protonation, Oxidation, and Ultrasonication