Chemically bonded multi-nanolayer inorganic aerogel with a record-low thermal conductivity in a vacuum
Hongxuan Yu,Menglin Li,Yuanpeng Deng,Shubin Fu,Jingran Guo,Han Zhao,Jianing Zhang,Shixuan Dang,Pengyu Zhang,Jian Zhou,Dizhou Liu,Duola Wang,Chuanwei Zhang,Menglong Hao,Xiang Xu
DOI: https://doi.org/10.1093/nsr/nwad129
IF: 20.6
2023-05-08
National Science Review
Abstract:Abstract Inorganic aerogels have exhibited many superior characteristics with extensive applications, but still plagued a nearly century-old tradeoff between their mechanical and thermal properties. When reducing the thermal conductivity by ultralow density, inorganic aerogels generally suffer from large fragility due to their brittle nature or weak joint crosslinking, while enhancing the mechanical robustness by material design and structural engineering, they easily sacrifice the thermal insulation and stability. Here, we report a chemically bonded multi-nanolayer design and synthesis of a graphene/amorphous boron nitride aerogel to address this typical tradeoff to further enhance the mechanical and thermal properties. Attributed to the chemically bonded interface and coupled toughening effect, our aerogels display a low density of 0.8 mg cm−3 with ultrahigh flexibility (elastic compressive strain up to 99% and bending strain up to 90%), and exceptional thermostability (strength degradation < 3% after sharp thermal shocks), as well as the lowest thermal conductivities in vacuum (only 1.57 mW m−1 K−1 at room temperature and 10.39 mW m−1 K−1 at 500°C) among solid materials to date. This unique combination of mechanical and thermal properties offers an attractive material system for thermal superinsulation at extreme conditions.
multidisciplinary sciences