Crystallization, melting, and morphology of a poly(ethylene oxide) diblock copolymer containing a tablet-like block of poly{2,5-bis[(4-methoxyphenyl)oxycarbonyl]styrene}
Yun Huang,Jing Wang,Xuan-Bo Liu,Hai-Liang Zhang,Xiao-Fang Chen,Wen-Chang Zhuang,Xiao Chen,Chun Ye,Xin-Hua Wan,Er-Qaing Chen,Qi-Feng Zhou
DOI: https://doi.org/10.1016/j.polymer.2005.08.010
IF: 4.6
2005-01-01
Polymer
Abstract:A poly(ethylene oxide) diblock copolymer containing a short block of poly{2,5-bis[(4-methoxyphenyl)oxycarbonyl]styrene} (PEO-b-PMPCS) has been successfully synthesized via atom transfer radical polymerization (ATRP) method. The number average molecular weights (Mn) of the PEO and PMPCS blocks are 5300 and 2100g/mol, respectively. Combining the techniques of differential scanning calorimetry (DSC), optical microscopy (OM), wide angle X-ray diffraction (WAXD), and small angle X-ray scattering (SAXS), we have found that the PMPCS blocks, which are tablet-like, can significantly affect the crystallization and melting of the diblock copolymer. The sample studied can form the crystals with a monoclinic crystal structure identical to that of the homo-PEO. The melting temperature (Tm) of the diblock copolymer increases monotonically with crystallization temperature (Tc), which is remarkably similar to the behavior of long period. On the basis of Gibbs–Thomson relationship, the equilibrium Tm (Tm0) of the diblock copolymer is estimated to be 65.4°C. In a wide undercooling (ΔT) range (14°C<ΔT<30°C), the isothermal crystallization leads to square-shaped crystals. The PEO-b-PMPCS crystallization exhibits a regime I→II transition at ΔT of 19°C. The PEO blocks are non-integral folded (NIF) in the crystals, and the PMPCS blocks rejected to lamellar fold surfaces prevent the NIF PEO crystals from transforming to integral folded (IF) ones. Furthermore, the PMPCS tablets may adjust their neighboring positions up or down with respect to the lamellar surface normal, forming more than one PMPCS layer to accompany the increase in the PEO fold length with increasing Tc.