Abstract:Titania nanotubes (TNTs) were synthesized by hydrothermal treatment of rutile-phase TiO2 nanoparticals in NaOH solution at 110 degrees C for 24 hours. After drying in aceton for 36 h, the TNTs were under vacuum drying for 24 h at room temperature. The Pt-inserted titania nanotubes (Pt/TNTs) were obtained by filling H2 PtCl6 ethanol solution into the TNTs after vacuum drying. The characterizations of the as-synthesized samples were confirmed by TEM, XRD, and UV-Vis. The photocatalytic activity of the Pt/TNTs was investigated by photo-induced decomposition of methyl orange(MO)under the main 365 nm UV-light. In order to comparison, the photocatalytic activity of both the rutile-phase TiO2 nanoparticles and pure TNTs were also investigated at the same time under the same experimental conditions. The TEM images show that the TNTs are hollow, a few hundred nanometers long, and the inner/outer diameter is about 6/10 nm. The crystal structure of TNTs is H2Ti2O5 x H2O with a little Na. Both the shape and the crystalline of the TNTs are not changed after the modification. The oval or round Pt0 nanoparticals, about 3 nm in diameter, are found only in the nanotubes. Pt/TNTs exhibit enhanced absorption at the visible range in the UV-Vis spectra and its start absorption band edge(lambda0 approximately 457 nm)is obviously redshifted compared to the rutile-phase TiO2 nanoparticals and pure TNTs. The Pt nanoparticles are found to significantly enhance the photocatalytic activity of TNTs. Pt/TNTs are demonstrated to be highly efficient for the UV-light induced photocatalytic decomposition of MO compared to both the rutile-phase TiO2 nanoparticals and pure TNTs. After irradiation for 60 min, the photocatalysis decomposition rate of MO in rutile-phase TiO2 nanoparticals, TNTs and Pt/TNTs are 46.8%, 57.2% and 84.6% respectively.

Effect of Oxygen Vacancies on Photocatalytic Efficiency of TiO 2 Nanotubes Aggregation

Effect of annealing ambience on the formation of surface/bulk oxygen vacancies in TiO2 for photocatalytic hydrogen evolution

Distribution And Concentration Of Surface Oxygen Vacancy Of Tio(2)And Its Photocatalytic Activity

Distribution and concentration of surface oxygen vacancy of TiO<sub>2</sub>and its photocatalytic activity

Electronic States And Photoluminescence Of Tio2 Nanotubes With Adsorbed Surface Oxygen

Preparation and Photocatalytic Performance of Titania Nanotubes Loaded with Ag Nanoparticles

Effect of Tin+ Defects on Electrochemical Properties of Highly-Ordered Titania Nanotube Arrays

Comparative study of photocatalytic performance on different TiO 2 nano-tubes arrays

Effect of Oxygen Vacancies on Electronic Structures and Field Emission Properties of TiO2 Nanotubes: A Density-Functional Theory Investigation

Origin Of Photocatalytic Activity Of Nitrogen-Doped Tio2 Nanobelts

Enhanced Photoelectrocatalytic Degradation of Organic Pollutants Using TiO2 Nanotubes Implanted with Nitrogen Ions

Effect of surface/bulk oxygen vacancies on the structure and electrochemical performance of TiO2 nanoparticles

Fabrication and Photocatalytic Activity of Pt-Inserted Titania Nanotubes

Synthesis and Photocatalytic Performance of Nitrogen and Nickel Codoped TiO2 Nanotubes

Characterisation of oxygen defects and nitrogen impurities in TiO2 photocatalysts using variable-temperature X-ray powder diffraction

Effect of TiO2 Nanotube Arrays Morphology/Structure on Photocatalytic Hydrogen Production

The Effects of Sintering on the Photocatalytic Activity of N-Doped TiO2 Nanoparticles

Photon Localization Effect and Surface Oxygen Vacancy Enhanced Photocatalytic Nitrogen Fixation Performance for Nanocrystalline Titanium Dioxide Film

Photon localization effect and surface oxygen vacancy enhanced photocatalytic nitrogen fixation performance for nanocrystalline titanium dioxide films

Hierarchical Nanotubular Anatase/Rutile/TiO2(B) Heterophase Junction with Oxygen Vacancies for Enhanced Photocatalytic H2 Production.

Effect of Post-Annealing Treatment on Photocatalytic and Photoelectrocatalytic Performances of TiO2 Nanotube Arrays Photoelectrode.