Plasma Treatment on Sio2f/Sio2 Composites for Their Assisted Brazing with Nb

Jun Lei Qi,Jing Huang Lin,Jia Le Guo,Yu Lin Liu,Jian Cao,Li Xia Zhang,Ji Cai Feng

DOI: https://doi.org/10.1016/j.vacuum.2015.10.025

IF: 4

2016-01-01

Vacuum

Abstract:Brazing SiO2f/SiO2 composites with metals is often associated with the problems of poor wettability with active brazing alloy and poor mechanical properties of joints. To overcome these problems, we report the plasma treatment on SiO2f/SiO2 by PECVD for their assisted brazing with Nb. The O-Si-O bonding changed into Si-C bonding on the surface of SiO2f/SiO2 by the plasma treatment can improve the wettability of Ag-Cu-Ti brazing alloy on SiO2f/SiO2. Furthermore, SiO2f/SiO2 after the plasma treatment can contribute to the infiltration of brazing alloy into SiO2f/SiO2 to form the pinning structure and reducing the residual stress, which could strengthen the joint. The obtained joint has a high shear strength of 60.5 MPa, approximately 11 times higher than that without plasma treatment. (C) 2015 Elsevier Ltd. All rights reserved.