Abstract:For the conventional Ni/SiO2 catalyst, it is a challenge to address the sintering problem of Ni particles, especially at high Ni loading. A series of Ni-phyllosilicate catalysts were prepared through the hydrothermal reaction of mesoporous SiO2 nanorods (SRs) and nickel nitrate, followed by an impregnation modification of CeO2. Hydrothermal temperature played an important role in the formation of nickel phyllosilicate. A small amount of Ni-phyllosilicate with a Ni content of 18.56 or 23.88 wt % was formed at a low hydrothermal temperature of 120 or 160 degrees C, and a large amount of nanosheet-like Ni-phyllosilicate with the Ni content as high as 31.65 wt % was obtained at a high hydrothermal temperature of 200 degrees C. The prepared Niphyllosilicate catalysts were beneficial to obtain Ni particles with small sizes (3.3-6.3 nm), even though they were reduced at 750 degrees C and possessed high Ni loadings (18.56-31.65 wt %) owing to the surface and interface confinement of nickel phyllosilicate. After the modification of CeO2 using an impregnation method, the CeO2 promoter could further reduce the Ni particle size and increase hydrogen and carbon dioxide uptakes. The CeO2-modified Niphyllosilicate catalyst (NPS-180-5C) was the best catalyst in this work, which could reach the thermodynamic equilibrium of CO methanation above 350 degrees C and exhibited high catalytic activity for CO2 methanation. In addition, for the 55 degrees C-100 h-lifetime test for CO2 methanation and 600 degrees C-6h-100% steam treatment tests, NPS-180-5C also showed an excellent antisintering property and higher hydrothermal stability than the impregnated one (N/SR-Im) owing to its special structure and confinement effect as well as promotion of CeO2 species. In all, the CeO2-modified SR-derived Ni-phyllosilicate catalyst could not only effectively suppress the problem of easy sintering of metallic Ni particles on the conventional Ni/SiO2 catalysts but also exhibit high catalytic activity and hydrothermal stability, which was a promising catalyst for both CO2 and CO methanation reactions.

Synthesis of High-Dispersed NiCoP/SiO2 and Hydrodesulfurization Performance

Synthesis of Novel NiMo Catalysts Supported on Highly Ordered TiO2-Al2O3 Composites and Their Superior Catalytic Performance for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

A Novel Route for Synthesis of NiCoP/SiO2 Hydrodesulfurization Catalysts with Active S Species

A New Preparation Approach for NiCoP/SiO2 Catalyst by Solid Phase Reaction of Nickel and Cobalt Cations with Potassium Dihydrogen Phosphate

Synthesis of Supported Bimetal Phosphide Catalysts Based on Red Phosphor and Hydrodesulfurization Property

In Situ Synthesis of Nb-modified AFI Topology Molecular Sieve and Its Modulation on the Formantion of High-Efficiency Catalyst for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

Synthesis of highly active and porous NiCoP catalysts via directly thermal treatment of a mechanical mixing of nickel, cobalt salts and sodium hypophosphite

A New Route for Synthesizing Nickel Phosphide Catalysts with High Hydrodesulfurization Activity Based on Sodium Dihydrogenphosphite

A Novel Synthesis of Ni 2 P Catalysts by Reducing Nickel Sulfide at Low Temperature

Application of a Response Surface Method for the Optimization of the Hydrothermal Synthesis of Magnetic NiCo2O4 Desulfurization Catalytic Powders

Preparation of Highly Dispersed Nickel Phosphide Catalyst Supported on Nano-Sized Y Zeolite and Its Hydrodesulfurization Performance

Nickel Cobalt Thiospinel Nanoparticles As Hydrodesulfurization Catalysts: Importance of Cation Position, Structural Stability, and Sulfur Vacancy.

Ni<sub>12</sub>P<sub>5</sub> Confined in Mesoporous SiO<sub>2</sub> with Near-Unity CO Selectivity and Enhanced Catalytic Activity for CO<sub>2</sub> Hydrogenation

A highly loaded and dispersed Ni2P/SiO2 catalyst for the hydrotreating reactions

Highly Efficient Ni-Phyllosilicate Catalyst with Surface and Interface Confinement for CO<sub>2</sub> and CO Methanation

Synthesis of Mesoporous Silica-Supported NiCo Bimetallic Nanocatalysts and Their Enhanced Catalytic Hydrogenation Performance

Preparation of NiWO4/g-C3 N4 and its ultra-deep desulfurization properties in ionic liquid

ABATEMENT OF HARMFUL CARBON MONOXIDE OVER THE NICKLE DOPED CO3 O4 CATALYST

PVP-assisted Synthesis of Unsupported NiMo Catalysts with Enhanced Hydrodesulfurization Activity

Synthesis of Pd Decorated Flower-Like NiO Composite and Its High Catalytic Performance for CO Oxidation under Ambient Conditions

An Approach to Preparing Highly Dispersed Ni2P/SiO2 Catalyst