Composition Dependent Magnetism in Novel Triple Perovskite Sr3MFeMoO9 (m=mn, Co, Ni)
Jin-Feng Wang,Bin Hu,Ji Zhang,Zheng-Bin Gu,Shan-Tao Zhang
DOI: https://doi.org/10.1016/j.ceramint.2014.01.096
IF: 5.532
2014-01-01
Ceramics International
Abstract:Triple perovskite Sr3MFeMoO9 (M=Mn, Co, Ni) ceramics have been prepared under flowing N-2 steam. All compositions are single phase and have B-site cation ordering. However, the composition with M = Co shows denser microstructures with smaller grains, the average grain sizes are 700, 500 and 650 nm for M=Mn, Co, and Ni, respectively. The chemical states of the surface and interior Mn, Co, Ni, Fe, and Mo cations are analyzed carefully. Both the magnetization-magnetic field curves and magnetization-temperature curves confirm that all compositions show antiferromagnetic behaviors. The Neel temperature of M=Mn and Ni compositions are determined to be 24.4 and 49.5 K, respectively. However, M = Co composition shows two magnetic transition temperatures at 70.9 and 180.7 K, which is possibly attributed to that the Co cations have intermediate spin-state (3d(6), S=1) and high spin states (3d(6), S=2). Furthermore, the compositions show semiconductor-like behaviors and neglectable magnetoresistance in whole measuring temperature range. Our results may be helpful for designing novel magnetic materials and for understanding magnetic couplings in triple perovskites. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.