Charge Defects and Highly Enhanced Multiferroic Properties in Mn and Cu Co-Doped BiFeO3 Thin Films

Guohua Dong,Guoqiang Tan,Yangyang Luo,Wenlong Liu,Ao Xia,Huijun Ren

DOI: https://doi.org/10.1016/j.apsusc.2014.02.159

IF: 6.7

2014-01-01

Applied Surface Science

Abstract:Pure BiFeO3 (BFO) and Mn, Cu co-doped BiFeO3 (BFMCO) thin films were deposited on fluorine doped tin oxide (FTO) substrates by a chemical solution deposition method. Detailed investigations were made on the effects of Mn and Cu co-doping on the crystal structure, the defect chemistry, multiferroic properties of the BFO thin films. With the co-doping of Mn and Cu, a structural transition from the rhombohedral (R3c:H) to the biphasic structure (R(3)c:H +Pl) is confirmed by XRD, Rietveld refinement and Raman analysis. X-ray photoelectron spectroscopy (XPS) analysis shows that the coexistence of Fe2-7Fe3+ and Mn2+/Mn3+ ions in the co-doping films are demonstrated. Meanwhile, the way of the co-doping at B-sits is conducive to suppress Fe valence state of volatility and to decrease oxygen vacancies and leakage current. It's worth noting that the co-doping can induce the superior ferroelectric properties (a huge remanent polarization, 2Pr similar to 220 mu C/cm(2) and a relatively low coercive field, 2Ec -614 kV/cm). The introduction of Mn2+ and Cu2+ ions optimizes the magnetic properties of BFO thin films by the biphasic structure and the destruction of spin cycloid. (C) 2014 Elsevier B.V. All rights reserved.