Abstract:Gd3+/TiO2 and Gd2O3/TiO2 nanoparticles were prepared by ball milling method. The effects of Gd3+ ion and Gd2O3 on the structure and optical property of TiO2 were studied by XRD and UV-vis DRS. Specific surface area was determined by Brunauer-Emmett-Teller (BET) method. The morphology and elemental composition were characterized by SEM-EDS. XPS was used to determine the surface compositions and chemical character of elements. The sample sizes and microstructures were observed by TEM. The photocatalytic activities of TiO2 nanoparticles modified with rare earth metal gadolinium (Gd3+ ion or Gd2O3) were evaluated by degradation of methylene blue (MB) under UV light. Experimental results indicate that 2.5 mol% Gd3+/TiO2 shows the best photocatalytic activity compared with Gd2O3/TiO2 and pure TiO2. The existence of gadolinium can exhibit the aggregation and induce lattice distortion of TiO2 obtained from XRD, SEM and TEM results. The band gap energy of 2.5 mol% Gd3+/TiO2 decreases to 3.07 eV and it leads to visible light absorption response which can be seen from UV-vis absorption spectra. The surface area of 2.5 mol% Gd3+/TiO2 equals to 85.8 m(2)/g and average crystal size is 21.1 nm. EDS and XPS analyses reveal that gadolinium can be introduced either into TiO2 lattice or adsorbed on the surface of TiO2. The content of surface OH groups in 2.5 mol% Gd3+/TiO2 is 50.88% (1.55 times higher than that of pure TiO2) and the content of lattice oxygen decreases to 11.26%. The MB (25 mg/L) degradation reaction rate constants of 2.5 mol% Gd3+/TiO2, 0.5 mol% Gd3+/TiO2 and pure TiO2 were 0.0713, 0.0588 and 0.0263 min(-1), respectively. The degradation rates of rhodamine B (30 mg/L) in 60 min are 97.9%, 90.1% and 84.6% for 2.5 mol% Gd3+/TiO2, 0.5 mol% Gd2O3/TiO2 and pure TiO2, respectively. (C) 2019 Chinese Society of Rare Earths. Published by Elsevier B.V. All rights reserved.

Enhanced photocatalytic activity for the degradation of rhodamine B by TiO2 modified with Gd2O3 calcined at high temperature

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

Enhanced Photocatalytic Activity for Degrading Rhodamine B Solution of Commercial Degussa P25 Tio2 and Its Mechanisms

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Enhanced Photocatalytic Activity of Gd3+ Doped TiO2 and Gd2O3 Modified TiO2 Prepared Via Ball Milling Method

Crystallite Size, Surface Properties and Photocatalytic Activity of Gd3+-doped TiO2 Nano-Powder

Photodegradation Of Rhodamine B In Water Assisted By Titania Nanorod Thin Films Subjected To Various Thermal Treatments

Photocatalytic and photoelectrocatalytic degradation of aqueous Rhodamine B by low-temperature deposited anatase thin films

Solar photocatalytic degradation of dye wastewater in the presence of heat‐treated anatase TiO<sub>2</sub>powder

Improvement in Structure and Visible Light Catalytic Performance of g-C3N4 Fabricated at a Higher Temperature

Photocatalytic Degradation of Rhodamine B on Co-doped TiO_2 Thin Film under Visible Light

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

Effect of Nd2O3 Addition on the Surface Phase of TiO2 and Photocatalytic Activity Studied by UV Raman Spectroscopy

Enhanced activity of bismuth-compounded TiO2 nanoparticles for photocatalytically degrading rhodamine B solution

Synthesis of Nanocrystalline Anatase TiO2 by One-Pot Two-Phase Separated Hydrolysis-Solvothermal Processes and Its High Activity for Photocatalytic Degradation of Rhodamine B.

Influences of Gd Substitution on the Crystal Structure and Visible-Light-Driven Photocatalytic Performance of Bi2WO6

The effects of calcination on sol–gel synthesized Gd2Ti2O7 photocatalyst for degradation of Reactive Brilliant Red X-3B

Sol-gel synthesis of porous gadolinium titanate photocatalyst for improved activity

Solvothermal synthesis of nanoscale disc-like gadolinium doped magnesium zirconate for highly efficient photocatalytic degradation of rhodamine B in water

Photocatalytic degradation of Rhodamine B over TiO2/g-C3N4 and immobilized TiO2/g-C3N4 on stainless steel wire gauze under UV and visible light: A detailed kinetic analysis and mechanism of degradation