Mechanochemical Effect of Brucite Powder in A Wet Ultrafine Grinding Process
Gaoxiang Du,Qiang Xue,Hao Ding,Zhaohui Li
2013-01-01
Indian Journal of Engineering and Materials Sciences
Abstract:a In this paper, mechanochemical effect of brucite powder in a wet ultrafine grinding process is studied. The results show that fresh surfaces of brucite particles are formed during the grinding process. The solubility of Mg(OH)2 increases in the first 3 h of grinding. The crystal size and lattice deformation of brucite particles decrease in the first 3 h and are leveled off after 3 h. As the concentrations of Mg 2+ and OH - ions increase to a certain level, recrystallization would occur. The dominant face for comminution and recrystallizaiton of Mg(OH)2 occur mainly on the (001) and the newly formed crystals are easily maintained due to less comminution on (110) face. Regarding the activation of chemical reactions, thermochemistry, electrochemistry, and photochemistry were often emphasized, while the fourth way of chemical activation, mechanochemistry, was usually less well-known 1 . In mechanochemistry, various types of mills were used. Mechanochemical activation involved in the increase of internal and surface energy, increase of surface area, and decrease of the coherence energy of solids 2 . In addition, spontaneous aggregation, adsorption, or recrystallization may occur in the activated system during grinding or after grinding has been completed 1 . Thus, a series of physical and chemical transformation could be introduced during mechanical grinding processes. These changes include reduction of particle size, increase of specific surface area, disorder of partial crystal structure, deformation of lattice, and alteration of crystal size 3-5 . These changes could activate the particle surfaces and lower the reaction barrier between different types of particles in order to improve the performances of materials and to prepare composite materials. Through mechanochemistry, many materials could be compounded including C-containing LiFePO4