The Microstructure and Magnetization Behaviors of (pr8.2fe86.1−xcoxb5.7)0.99zr0.01 (x = 0–10) Nanocomposite Magnets
Renjie Chen,Shuai Guo,Jinzhi Wang,Don Lee,Aru Yan
DOI: https://doi.org/10.1063/1.3566074
IF: 2.877
2011-01-01
Journal of Applied Physics
Abstract:Nanocomposite (Pr8.2Fe86.1−xCoxB5.7)0.99Zr0.01 (x = 0–10) ribbons consisting of Pr2(Fe,Co)14B and α-(Fe,Co) phases were prepared by a melt-spun technique. The microstructure and magnetic properties were studied. The results show that the Curie temperature increases drastically with increasing Co content. The optimal permanent magnetic properties are obtained at x = 2, and the value of Hci, Ms, Mr, and (BH)max are 6.52 kOe, 150.2 emu/g, 120.9 emu/g, and 22.34 MGOe, respectively. Typical magnetization behaviors of nanocomposite magnets are found in these ribbons. The significant remanence enhancement indicates that a strong intergrain exchange coupling exists in all ribbons studied in this work. By Co substitution, the intergrain exchange coupling is enhanced significantly. The study of microstructure shows that the larger grains of Pr2(Fe,Co)14B hard phase are surrounded by the smaller grains of α-(Fe,Co) soft phase with size about 10–20 nm in the ribbon with Co substitution. This kind of microstructure is in favor of exchange coupling between magnetically hard and soft phases and results in excellent magnetic properties.