1,4-Selective Polymerization of 1,3-Cyclohexadiene and Copolymerization with Styrene by Cationic Half-Sandwich Fluorenyl Rare Earth Metal Alkyl Catalysts

Gaixia Du,Yingyun Long,Jiaping Xue,Shaowen Zhang,Yuping Dong,Xiaofang Li
DOI: https://doi.org/10.1021/acs.macromol.5b00037
IF: 5.5
2015-01-01
Macromolecules
Abstract:The regioselective coordinationinsertion polymerization of 1,3-cyclohexadiene (CHD) and copolymerization with styrene (S) could be achieved by cationic half-sandwich fluorenyl rare earth metal alkyl catalysts generated by treating half-sandwich fluorenyl rare earth metal dialkyl complexes Flu'Ln(CH2SiMe3)(2)(THF)(n) (1-10) with an activator (such as [Ph3C][B(C6F5)(4)] (A), [PhNHMe2][B(C6F5)(4)] (B), or B(C6F5)(3) (C)) and (AlBu3)-Bu-i. The homopolymerization of CHD afforded poly(CHD)s with complete 1,4 selectivity (1,4 selectivity up to 100%). The copolymerization of CHD with styrene gave new random CHD-S copolymers with CHD content ranging from 22 to 74 mol % containing 1,4-linked CHD-CHD, alternating CHD-S, and syndiotactic SS sequences unavailable previously. The activity of the copolymerization and the comonomer compositions and sequences of the resulting CHD-S copolymers could be easily controlled by changing the substituted fluorenyl ligand, the metal center, the activator, the temperature, and the molar ratio of comonomers. The residual C-C double bonds of the random CHD-S copolymers could be further epoxidized by meta-chloroperoxybenzoic acid (mCPBA) at room temperature to prepare high-performance polymers with polar groups and reactive sites in the polymer backbone. Such functionalization could improve the solubility, dying, acidity, and surfactivity of these copolymer materials.
What problem does this paper attempt to address?