Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Real Time Control Of Nanowire Formation

Optical Control with Large-Scale Assembly of Highly Aligned Silver Nanowires

In Situ Fabrication and Graphitization of Amorphous Carbon Nanowires and Their Electrical Properties

Fabrication of Stable Metallic Nanowires with Quantized Conductance

In Situ Observation of High Bending Strain Recoverability in Au Nanowires

Quantum Transport In Metallic Nanowires Fabricated By Electrochemical Deposition/Dissolution

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Controlled Formation of Metallic Nanowires Via Au Nanoparticle Ac Trapping

Formation and manipulation of a metallic wire of single gold atoms

J212015 Quantitative Evaluation of Conductivity of Metallic Nanowires by Microwave Atomic Force Microscopy

Electrochemical Fabrication of Atomically Thin Metallic Wires and Electrodes Separated with Molecular-Scale Gaps

Silver Nanowires Eelectrodeposited from Reverse Hexagonal Liquid Crystals

Formation of Magnetic Nanowire Arrays by Cooperative Lateral Growth.

Charge Transport in Nanocrystal Wires Created by Direct Electron Beam Writing

Structural and angular dependence of coercivity and magnetic remanence of electrochemical ferromagnetic nanowires

Direct momentum-resolved observation of one-dimensional confinement of externally doped electrons within a single subnanometre-scale wire

Real‐Time Probing of Nanowire Assembly Kinetics at the Air–Water Interface by in Situ Synchrotron X‐Ray Scattering

Fabrication and Characterization of Metallic Nanowires

A Study of Control Growth of Three-Dimensional Nanowire Networks of Tungsten Oxides: from Aligned Nanowires Through Hybrid Nanostructures to 3d Networks

Fabrication of Conducting Si Nanowire Arrays

Nanoscale Wire Bonding of Individual Ag Nanowires on Au Substrate at Room Temperature