Preparation and properties of BiFeO 3 /LDPE nanocomposite

wei song,bai han,dong zhang,zhi sun,xuan wang,qingquan lei

DOI: https://doi.org/10.1109/icpadm.2015.7295393

2015-01-01

Abstract:BiFeO 3 /LDPE nano-dielectric films of different BiFeO 3 nanoparticles percentages including 0.5%, 1%, and 2% have been successfully prepared using solution-melt blending method in the spiral double pole rheometer. The BiFeO 3 /LDPE nanocomposite films were characterized by SEM (scanning electron microscopy), FT-IR (Fourier transform infrared), and XRD (X-ray diffraction). The dielectric properties were tested by the broadband dielectric spectrometer. The experimental results show that BiFeO 3 nanoparticle fillers are homogeneous dispersion in LDPE matrix and the structure of LDPE has not been changed even after doping with BiFeO 3 nanoparticles. It can be seen that dielectric constants of all samples have small extent of variation with frequency from 100 to 105 Hz. Except 0.5 wt.%, dielectric constants are increase with increased of contents of BiFeO 3 , and dielectric constant increases up to 2.6 which is increased 16% than that of the pristine LDPE. The dielectric loss of BiFeO 3 /LDPE nanocomposites indicate that they have a low dielectric loss in the range of 100 to 105 Hz and the variation of dielectric loss is very small even when contents of BiFeO 3 with 0.5 wt.% and 1 wt.% than pristine LDPE, but a increase was obversed when content of BiFeO 3 nanoparticles reached 2 wt.%. The variation tendency is because of different polarization mechanisms.