Pulse Electrodeposition and Corrosion Behavior of Ni–W/MWCNT Nanocomposite Coatings

Han Li,Yi He,Yi Fan,Wei Xu,Qiangbin Yang

DOI: https://doi.org/10.1039/c5ra09462c

IF: 4.036

2015-01-01

RSC Advances

Abstract:In this study, Ni–W/multiwalled carbon nanotube (MWCNT) composite coatings were successfully deposited on the surface of a C45 steel sheet by pulse current electrodeposition.

What problem does this paper attempt to address?

Preparation of Electrodeposited Ni-CNTs Nanocomposite Coatings with Highly Wear and Corrosion Resistance Properties

W. Shao,D. Nabb,N. Renevier,I. Sherrington,J.K. Luo

DOI: https://doi.org/10.4028/www.scientific.net/amr.548.101

2012-01-01

Advanced Materials Research

Abstract:Ni-carbon nanotubes nanocomposite coatings were obtained from a Watts bath containing uniformly dispersed carbon nanotubes (CNTs). The surface morphology was investigated by the SEM images of coatings. The mechanical property and corrosion resistance of the nanocomposite coatings were investigated. This study revealed these CNTs reinforced Ni nanocoatings have improved mechanical and corrosion property.
The Influence of Pulse Plating Parameters on the Structure and Corrosion Behavior of Ni-W-TiC Nanocomposite Coatings

Atefe Allahdadi,Saeed Rastegari,Nazanin Jalalian Karazmoudeh

DOI: https://doi.org/10.1007/s11665-024-09562-9

IF: 2.3

2024-05-17

Journal of Materials Engineering and Performance

Abstract:In this study, Ni-W-TiC nanocomposite coatings were fabricated successfully on low-carbon steel via electrodeposition. The effect of duty cycle, frequency, current type (pulse or direct current), and the presence of TiC nanoparticles on the microstructure, composition, and electrochemical behavior were investigated. Scanning electron microscope, energy-dispersive spectroscopy, x-ray diffraction technique (XRD), polarization, and electrochemical impedance spectroscopy were used to characterize and evaluate the prepared coatings. Based on the XRD spectra of the different coatings, altering the plating parameters does not affect the phase structure, and the main phase of the coatings was Ni(W) solid solution. The results revealed that the optimal conditions in terms of the highest corrosion resistance were achieved under the pulse current with a duty cycle of 80%, pulse frequency of 1000 Hz, an average current density of 10 A/dm 2 , and TiC nanoparticle concentration of 5 g/L. The presence of TiC nanoparticles in the Ni-W alloy coating caused the morphology to change from cauliflower to turtle-shell and increased the coating thickness. The amount of TiC nanoparticles incorporated into the coating produced under the optimal condition was 3.5 wt.%, which plays an important role in the enhancement of the electrochemical behavior of the nanocomposite coating.

materials science, multidisciplinary
Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Z. H. Li,X. Q. Wang,M. Wang,F. F. Wang,H. L. Ge

DOI: https://doi.org/10.1016/j.triboint.2005.10.001

IF: 5.62

2006-01-01

Tribology International

Abstract:A method to prepare the carbon nanotubes (CNTs)–Ni–P composite coating with different mass content of CNTs on the surface of 45# steel by electroless plating was proposed. The transmission electron microscopy (TEM) and the scanning electron microscopy (SEM) were used to observe the appearance of the as-prepared CNTs and the CNTs–Ni–P composite coating, and then the roughness of the coating surface was also analyzed by atomic force microscopy (AFM). Furthermore, the wear and friction behavior of the CNTs–Ni–P composite coating were investigated under oil-lubricated condition, Due to the self-lubrication property and the unique antifriction structure, CNTs can greatly improve the wear resistance of the CNTs–Ni–P composite coating, where the wear resistance of the CNTs–Ni–P composite coating is optimized with the intermediate mass content of 2kg/m3 CNTs.
Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

王新庆,李振华,朱海滨,王幼文,何少龙,王淼

DOI: https://doi.org/10.3969/j.issn.1671-4776.2002.03.007

2002-01-01

Abstract:In this paper the technique and conditions of the synthesis of CNTs-Ni-P composite coating with electroless com posite plating have been studied.We also discussed the influence on the wear-re-sis tance and anti-corrasion of the Ni-P com posite coating with the CNTs .We found the best conditions to synthesize the CNTs-Ni-P composite coating from all above.At the same time after annealed in high temperature,the hardness of the composite coating has been observed.The SEM and the TEM were used to analyze the structure characters of the CNTs-Ni-P composite coating and the morphology of the CNTs respectively.
SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Xinqing Wang,Miao Wang,Zhenhua Li

2003-01-01

Abstract:The CNTs-(Ni-P) composites were prepared by electroless plating on 45~# steel substrate, and the optimum composition and operating conditions were obtained. The TEM was used to observe the CNTs' structure,the SEM was used to observe the appearance and distribution of the CNTs in the composites and the AFM(atomic force microscopy) was used to analyze the roughness status of the composite surface. The influence of the CNTs on the tribological performance of the composites is discussed. The results show that the CNTs-(Ni-P) composites have better wear-resistance than the uncoated substrate and the substrate coated with nikel.
Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Chunyang Ma,Hongxin He,Fafeng Xia,Mengyu Cao

DOI: https://doi.org/10.3390/coatings14111384

IF: 3.236

2024-11-01

Coatings

Abstract:Mild steel is a kind of material commonly used in the chemical industry and to manufacture machinery, farm tools, and other parts in order to improve the surface performance of the parts and prolong their service life. The Ni-TiN composite coating was fabricated through ultrasonic electroplating using a Ni-based sulfamic acid bath with added nano-TiN particles. The effects of three distinct current modes, direct current (DC), positive pulse current (PC), and positive–negative pulse current (PNPC), on various aspects of the coating, including surface morphology, TiN content and distribution, interface bonding strength, microhardness, friction and wear properties, as well as corrosion resistance, were investigated. The findings demonstrated that, in comparison to DC electroplating, PC electrodeposited Ni-TiN composite coatings yielded finer grains, smoother surfaces, reduced surface cracks, increased interface bonding strength, and enhanced corrosion resistance. Furthermore, PNPC electrodeposited Ni-TiN composite coatings showed higher interface bonding strength than those of PC electrodeposited Ni-TiN coatings and had the densest structure, leading to the best corrosion resistance. Pulse current electroplating enhanced the incorporation of nano-TiN particles, with a higher deposition rate observed in positive–negative pulse current electroplating compared to positive pulse current electroplating. Furthermore, the PNPC electrodeposited coating displayed improved microhardness and demonstrated the best friction and wear properties, while the DC electroplated coating displayed the least favorable performance in these aspects.

materials science, multidisciplinary,physics, applied, coatings & films
Preparation and Corrosion Resistance of Ni-W-CF Composite Coating on P110 Steel

Qiuli Zhang,Yi Feng,Zhaoyang Chen,Wenzhi Liao,Shuo Zhang,Jun Zhou,Lei Wu

DOI: https://doi.org/10.3390/coatings12020231

IF: 3.236

2022-02-11

Coatings

Abstract:Metal matrix composites have become a research hotspot due to their unique properties. In this paper, Ni-W-Carbon fiber (CF) composite coating was prepared by electrodeposition method, and the effects of CF content on the microstructure, composition, and corrosion resistance of the coating were studied by means of Scanning Electron Microscope (SEM), Energy Dispersive X-ray Spectrometer (EDS) and electrochemical testing by changing the concentration of CF in the plating solution. The results show that when 0.4 g/L nano-CF is added, the CF content in the composite coating is the largest and the distribution is uniform; the surface roughness Ra of the composite coating reaches a minimum of 14 nm. The electrochemical results show that the composite coating electrodeposited in the electrolyte containing 0.4 g/L nano-CF has the highest corrosion resistance. The Guglielmi model can be used to describe the co-deposition behavior. This study provides useful enlightenment for the further application of Ni-W-CF coating in harsh corrosive environments.

materials science, multidisciplinary,physics, applied, coatings & films
Influence of processing parameters on final characteristics of Ni-P-MWCNT coatings produced by pulsed electrodeposition

B. Sajedi,A. Rasooli

DOI: https://doi.org/10.1080/00202967.2022.2034345

2022-02-28

Transactions of the IMF

Abstract:The aim of the present work is to study the effects of multi-walled carbon nanotubes (MWCNT) concentration and current density on the surface morphology, microhardness, and corrosion resistance of pulsed electrodeposited Ni-P-MWCNT composite coatings. Ni-P-MWCNT composite coatings were deposited on low-carbon steel substrates using different MWCNT concentrations, namely 0.5, 1.0, and 1.5 g L−1 under various current densities of 3, 4, and 5 A dm−2. The as-produced coatings were characterised using field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), Vickers microhardness measurement, and electrochemical impedance spectroscopy (EIS). To determine the impact of post-heat treatment on the microstructure and microhardness of the coatings, the composite coatings were heat-treated at 400°C for 1 h. Change in the studied variables profoundly altered the final characteristics of the Ni-P deposits. While the incorporation of 1.0 g L−1 MWCNT enhanced the microhardness of the alloy deposit by 560 HV, the microhardness of the composite coating was further increased by 405 HV when it underwent post deposition-heat treatment. The corrosion resistance of the composite coating is about 4 times higher than that of alloy deposits. The optimum mechano-corrosion results were obtained for Ni-P-1.0 g L−1 MWCNT coating fabricated under current density of 4 A dm−2.
Synthesis and Evaluation of Pulse Current and Direct Current Electroplating Ni-W Coatings on Steel

Wang Meiling,Yang Zhigang,Liu Dianlong,Zhang Chi,Wang Zhenqiang

2012-01-01

Rare Metal Materials and Engineering

Abstract:Pulse current (PC) and direct current (DC) electroplating Ni-W coatings have been prepared and the composition, morphology, and structure of these coatings were investigated by energy dispersive spectroscopy (EDS), scanning electron microscopy (SEM), X-ray diffraction (XRD), respectively. It is verified that the PC Ni-W coatings present uniform surface and dense structure, as well as higher hardness and corrosion resistance than DC electroplating Ni-W coatings. PC Ni-W coatings with more than 20at% W yield a nanocrystalline structure. The maximum HV hardness of PC Ni-W coatings achieves 7.26 GPa for the sample with the highest W content. Moreover, the corrosion rate of PC Ni-W coating after neutral salt spray test for 120 h is comparable with that of DC electroplating Cr coatings, which is better than that of DC electroplating Ni-W coatings.
Preparation and Characterization of Pulse Electrodeposited Ni/W-SiC Nanocomposite Coating on Mild Steel Substrate

Zhaoge Zhu,Longqing Zou,Huaxing Li,Hongbin Zhang

DOI: https://doi.org/10.3390/coatings13030484

IF: 3.236

2023-02-22

Coatings

Abstract:In order to improve the performances of metal containers, furnace bodies and agricultural tools manufactured by mild steels, Ni/W-SiC nanocomposites are prefabricated on mild steel substrate by the pulse electrodeposition (PED) method. The morphology, texture, microstructure, microhardness, and wear performances of Ni/W-SiC nanocomposites are examined by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffraction (XRD), dispersive X-ray spectroscopy (EDX), hardness tester, and friction wear testing. The results indicate that the SiC size in nanocomposites is ~32.4 nm when its concentration in electrolytes is 7 g/L. The S1 and S4 nanocomposites' microstructures (the S1 composite was prefabricated at 4 g/L, and the S4 composite was deposited at 13 g/L) reveal many large cauliflower-shaped grains. However, the S2 nanocomposite (the S2 composite was obtained at 7 g/L) demonstrates the homogeneous, finest and smoothest surface morphology. The diffraction angles of S1 nanocomposite are 41.2°, 51.7°, and 71.2° depicting the sharpest diffraction peaks, corresponding to the (1 1 1), (2 0 0), and (2 2 0) crystal planes of Ni-W grains, respectively. Moreover, the S2 nanocomposite exhibits the lowest wear depth and width of 34.2 μm and 5.5 mm, respectively. Some shallow and fine scratches on the as-described nanocomposites' surface indicate its excellent tribological performance. However, the S4 nanocomposite exhibits a wear depth of 86.3 μm and a width of 11.9 mm.

materials science, multidisciplinary,physics, applied, coatings & films
Tribological properties of Ni–P-multi-walled carbon nanotubes electroless composite coating

W.X Chen,J.P Tu,Z.D Xu,W.L Chen,X.B Zhang,D.H Cheng

DOI: https://doi.org/10.1016/S0167-577X(02)00968-0

IF: 3

2003-01-01

Materials Letters

Abstract:Carbon nanotubes (CNTs) have super-strong mechanical characteristics and unique hollow nanotube structure and are believed as very ideal materials for fabricating the excellent composites. In this paper, tribological properties of Ni–P-CNTs composite coating prepared by electroless technique were investigated using a ring-on-block test rig. The results indicated that addition of CNTs would result in an increase in hardness of the composite coating. Due to reinforcement and reduced friction, the tribological properties of Ni–P-CNTs composite coating were greatly improved. The Ni–P-CNTs composite coating exhibited not only higher wear resistance but also lower friction coefficient than the Ni–P–SiC and Ni–P-graphite coatings. After treatment at 400 °C for 2 h, the wear resistance of the Ni–P-CNTs electroless composite coating improved because of the Ni3P precipitation in Ni-matrix.
Effect of SiC Nanoparticles on the Structure and Properties of Ni+W-SiC Nanocoatings

Fafeng Xia,Peng Yan,Chunyang Ma,Yan Liu

DOI: https://doi.org/10.1007/s11665-024-09312-x

IF: 2.3

2024-03-27

Journal of Materials Engineering and Performance

Abstract:Generally, 45 steel is one of the materials commonly used in the manufacture of chemical, agricultural, mechanical, and military metal parts. However, the service life of the part is low due to its low hardness, and poor corrosion and wear resistances. To improve the surface characteristics of 45 steel substrates, Ni+W-SiC nanocoatings were applied to 45 steel samples utilizing magnetic field-assisted pulse electrodeposition (MPE). The composites were evaluated for their compositions, structures, and microhardness using several analytical techniques, including transmission electron microscopy (TEM), scanning electron microscopy (SEM), scanning probe microscopy (SPM), nano indenter, and x-ray diffraction (XRD). The NC30 nanocoatings exhibited fine, compact, and homogeneous structures due to the presence of fine Ni+W grains and SiC nanoparticles (NPs). The size of SiC NPs has a significant influence on the XRD spectra of nanocoatings. The diffraction peaks for Ni+W and SiC appeared to be relatively high and sharp for NC150. After conducting a subsequent examination into the wear and corrosion properties of Ni+W-SiC nanocoatings, the loss in weights of the NC30, NC50, and NC150 coatings was determined to be 0.51, 0.76, and 0.87 g, respectively, following a 36-hour corrosion test. During the process of wear testing, a limited number of minor pits were observed on the NC30 nanocoating surface, indicating that it possesses a high level of wear resistance.

materials science, multidisciplinary
Effect of Duty Cycle on the Corrosion Resistance and Hardness of Ni-WC Nano-composite Coatings

Yuan-fu LIU,Ji CHEN,Ye YUAN,Xiao-ming CHEN,Zhi-xian XU,Ao HUANG,Jian SONG

DOI: https://doi.org/10.3969/j.issn.1000-4742.2017.02.002

2017-01-01

Abstract:Ni-WC nano-composite coatings were prepared on 304 stainless steel substrate by using pulse electrodeposition.Effect of duty cycle on the corrosion resistance and hardness of Ni-WC nano-composite coatings was investigated.Results showed that,with the increasing of duty cycle,the average grain size of Ni-WC nano-composite coatings decrease first and then increase,while the hardness of Ni-WC nano-composite coatings increase first and then decrease.When duty cycle was 50％,the prepared Ni-WC nano-composite coating has the smallest average grain size,the corrosion resistance was best and the hardness was highest.
Friction and wear behaviors of electrodeposited Ni-P-CNTs composite coatings on Al-alloy substrate

CHEN Wei-xiang,TU Jiang-ping,WANG Lang-yun,WANG Yu-cong,LIU Xin-kuan,O. L K Charls

DOI: https://doi.org/10.3785/j.issn.1008-973X.2008.11.034

2008-01-01

Abstract:Ni-P-carbon nanotubes(CNTs) composite coatings were electrodeposited on Al-alloy substrate and characterized by X-ray diffraction(XRD) and scanning electron microscope(SEM).The effects of the current density and the mass concentration of CNTs in the bath on the composite coatings and their friction and wear behaviors were investigated.The composite coatings with smooth surface could be obtained at 3.0 A/dm2 of current density.The volume fraction of CNTs in the composite coatings increased with increasing of CNTs mass concentration in the bath. Ni-P-CNTs composite coatings exhibit higher microhardness,wear resistance and lower friction coefficient than those of Ni-P coatings.With increasing CNTs volume fraction in the composite coatings,the wear ratio and friction coefficient decreased.The improvement in the tribological performances of the composite coatings arises from the super-strong mechanical properties and good self-lubrication of CNTs.
Preparation and Properties of Ni–W Composite Coatings Reinforced by Graphene Nanoplatelets

Desen Cheng,Lan Zhang,Zhuoyi Zhan,Huimin Xia,Kaiqiang Ma,Huizhong Ma,Yuan Gao

DOI: https://doi.org/10.1002/adem.202001309

IF: 3.6

2021-05-05

Advanced Engineering Materials

Abstract:Metal enhancement is crucial for reducing energy use and material waste. Composite electrodeposition is an economic and efficient method of improving the surface properties of metals. In this study, Ni‐W matrix composite coatings reinforced with graphene nanoplatelets (GNPs) were prepared on 7075 aluminum (Al) alloy plates by the co‐deposition technique. Characterization results reveal that the mechanical properties and corrosion resistance of the coating can be improved by the successful embedding of GNPs. The Ni‐W/GNP coating exhibits rougher, cauliflower‐like morphology, higher microhardness (782.6 HV), lower wear rate (2.72 × 10‐5 mm3 N‐1 m‐1), and better corrosion current density (18.19 μA cm‐2) compared to the Ni‐W coating (578.2 HV, 7.43 × 10‐5 mm3 N‐1 m‐1, 25.16 μA cm‐2, respectively). Moreover, X‐ray diffraction spectroscopy and analysis verify that the grain size is decreased for GNP‐reinforced composite coatings with a typical Ni‐based solid‐solution phase.This article is protected by copyright. All rights reserved.

materials science, multidisciplinary
Electroless Preparation and Tribological Properties of Ni-P-Carbon Nanotube Composite Coatings under Lubricated Condition

WX Chen,JP Tu,HY Gan,ZD Xu,QG Wang,JY Lee,ZL Liu,XB Zhang

DOI: https://doi.org/10.1016/s0257-8972(02)00408-5

2002-01-01

Abstract:Ni-P-Carbon nanotube (CNT) composite coatings as well as Ni-P-SiC and Ni-P-graphite coatings were prepared by electroless plating. The tribological properties of these composite coatings were investigated using a ring-on-block test rig under lubricated condition. The Ni-P-CNT composite coatings exhibited not only high wear resistance but also low friction coefficient compared with the Ni-P-SiC and Ni-P-graphite composite coatings. The favorable effects of CNTs on the tribological properties of the electroless coatings are attributed to improved mechanical properties and unique topological structure of the hollow nanotubes. In addition to preventing the rough contact between the two mating metal surfaces, the shorter CNTs can easily slide or roll within the surfaces of friction pairs. Therefore, the wear rate and friction coefficient of Ni-P-CNT composite coatings can be substantially reduced.
Preparation and Investigation of Ni–Co–P Alloy Coatings Using Jet Electrodeposition with Varying Pulse Parameters

Yin Zhang,Nyambura Samuel Mbugua,Huawei Jin,Lingling Chen

DOI: https://doi.org/10.3390/cryst13020303

IF: 2.7

2023-02-12

Crystals

Abstract:Ni–Co–P alloy coatings were successfully fabricated by jet electrodeposition with varying pulse frequencies and duty cycles in order to prolong the longevity of steel C1045 substrates. The results showed that the microstructures and properties of samples were significantly affected by pulse frequencies and duty cycles. All the samples with varying pulse frequencies and duty cycles exhibited a face-centered cubic (FCC) structure. Additionally, the average grain size of the samples reached 20.6 nm. The microhardness of the coatings was observed to first increase, and then decrease, with a rise in pulse frequencies and duty cycles. The microhardness reached 656.2 HV0.1, and the wear scar width of the coatings reached 414.4 μm at 4 kHz pulse frequency and 80% duty cycle. Additionally, the corrosion current densities (Icorr) of samples reached a minimum value of 0.74 μA·cm−2, the corrosion rates (Rcorr) reached a minimum value of 8.9 μm·year−1, and the charge transfer resistance (Rct) reached a maximum value of 8.36 × 104 Ω·cm−2, which indicated the optimal seawater corrosion resistance of the deposited coatings.

materials science, multidisciplinary,crystallography
Fabrication and characterization of CNT-reinforced Ni-Co composite coatings: microstructural evolutions and corrosion behavior

Hassan Sharifi,Seyed Ali Erfani Mobarakeh

DOI: https://doi.org/10.1051/metal/2024028

IF: 0.9461

2024-05-06

Metallurgical Research & Technology

Abstract:In this study, Ni-Co coatings were synthesized on 304L stainless steel substrates using the spin coating method and the effects of adding multi-walled carbon nanotubes (MWCNTs) on the microstructural, mechanical and corrosion properties of the produced coatings have been investigated. The morphology of the synthesized coatings containing high amounts of nickel was observed to be spherical. With increasing the cobalt content, a change from spherical to needle-fibrous morphology occurred in the microstructure of the coatings. Carbon nanotubes caused the accumulation of dislocations and increased the hardness of the coatings by restricting the movement of dislocations and the slipping of grain boundaries. Moreover, by adding multi-walled nanotubes to the coating structure, the preferred nucleation sites for nickel and cobalt were increased and the resulting coating became finer in the microstructure. Therefore, the maximum hardness and corrosion resistance were observed in the CNT-reinforced coating of the lowest cobalt content.

metallurgy & metallurgical engineering
Tribological performance of Ni-W/PTFE composite coating via pulse electrodeposition

Arif Karadag,Erhan Duru,Mehmet Uysal,Hatem Akbulut,Aslan Coban

DOI: https://doi.org/10.2298/tsci2204885k

IF: 1.971

2022-01-01

Thermal Science

Abstract:The Ni-W/PTFE co-depositions were successfully prepared on steel via pulse electrodeposition methods. Electrodeposition was perform by dispersing 5-20 g/L PTFE particles from Ni-Watt bath. The surface morphology, phase analyses crstalytallite size, distorsion and hardness of the samples were characterized by SEM, XRD, and Vicker?s microhardness tester. The friction coefficient of the coatings were carried out using CSM microtester. As increasing with the concentration of the PTFE in the solution, the wear resistance properties of theco-depositions were increased. These experimental results determined that the PTFE concentration of 15 g/L in the electrolyte was the optimum content to obtain the best micro-structure and wear performance.

thermodynamics
Pulse electrodeposited Ni–C films and its performance

Zihan Liu,Haitao Cui,Jingyi Tan,Luyuan Chen,Zhen He,Yuxin Wang

DOI: https://doi.org/10.1142/s0217979225400399

2024-06-26

International Journal of Modern Physics B

Abstract:International Journal of Modern Physics B, Ahead of Print. In this study, Ni–C films have been fabricated via pulse electrochemical deposition and carbon sol reinforcement methods. The surfacing of prepared films significantly improved due to the uniform distribution of nanoparticles. Additionally, the maximum thickness is attained when the concentration of carbon sol is 15[math]ml/L. X-ray diffraction analysis of the Ni–C composite films reveals adding carbon sol effectively refines the grain size of prepared films. The highest film hardness, 420[math]HV, is achieved at a carbon sol concentration of 15[math]ml/L, corresponding to the best wear and corrosion resistance. Excessive carbon sol can lead to agglomeration of carbon particles, resulting in defects such as cracks and pores within the coating, thereby degrading its performance.

physics, condensed matter, applied, mathematical

Pulse Electrodeposition and Corrosion Behavior of Ni–W/MWCNT Nanocomposite Coatings

Preparation of Electrodeposited Ni-CNTs Nanocomposite Coatings with Highly Wear and Corrosion Resistance Properties

The Influence of Pulse Plating Parameters on the Structure and Corrosion Behavior of Ni-W-TiC Nanocomposite Coatings

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Preparation and Corrosion Resistance of Ni-W-CF Composite Coating on P110 Steel

Influence of processing parameters on final characteristics of Ni-P-MWCNT coatings produced by pulsed electrodeposition

Synthesis and Evaluation of Pulse Current and Direct Current Electroplating Ni-W Coatings on Steel

Preparation and Characterization of Pulse Electrodeposited Ni/W-SiC Nanocomposite Coating on Mild Steel Substrate

Tribological properties of Ni–P-multi-walled carbon nanotubes electroless composite coating

Effect of SiC Nanoparticles on the Structure and Properties of Ni+W-SiC Nanocoatings

Effect of Duty Cycle on the Corrosion Resistance and Hardness of Ni-WC Nano-composite Coatings

Friction and wear behaviors of electrodeposited Ni-P-CNTs composite coatings on Al-alloy substrate

Preparation and Properties of Ni–W Composite Coatings Reinforced by Graphene Nanoplatelets

Electroless Preparation and Tribological Properties of Ni-P-Carbon Nanotube Composite Coatings under Lubricated Condition

Preparation and Investigation of Ni–Co–P Alloy Coatings Using Jet Electrodeposition with Varying Pulse Parameters

Fabrication and characterization of CNT-reinforced Ni-Co composite coatings: microstructural evolutions and corrosion behavior

Tribological performance of Ni-W/PTFE composite coating via pulse electrodeposition

Pulse electrodeposited Ni–C films and its performance