Growth and Electronic Transport Property of Layered BiOCl Microplates

Yangwei Zhang,Xianghan Xu,Ying Xing,Huichao Wang,Hailong Fu,Xi Lin,Jian Wang

DOI: https://doi.org/10.1002/admi.201500194

IF: 5.4

2015-01-01

Advanced Materials Interfaces

Abstract:We have developed a new way to fabricate size-controllable BiOCl samples ranging from a few hundred nanometers to several tens of micrometers by polymer-assisted hydrothermal method. For more details on the synthesis of BiOCl, see the Experimental Section. Figure 1 a shows a top-view morphology image of large quantity of uniform and well-defi ned BiOCl single-crystalline MPs. The in-plane size of the plates is around 1 μm. The high-magnifi cation SEM image in Figure 1 b shows a BiOCl MP with the width of 14.0 μm and the length of 20.6 μm. The X-ray diffraction (XRD) pattern (Figure 1 c) clearly exhibits that all the main diffraction peaks of the obtained plate-like microstructure samples are indexed to the tetragonal structure of BiOCl (JCPDS No. 6–249). Note that no diffraction peak corresponding to other impurities is detected, indicating that our simple hydrothermal reaction method has successfully generated plate-like BiOCl microstructures. The intense and sharp diffraction peaks suggest that the as-synthesized product is well-crystallized. The diffraction peak at around 32.5° corresponds to the (110) plane. Figure 1 d shows energydispersive X-ray spectroscopy (EDS) taken from the surface of the BOC MPs, which leads to the presence of Bi, Cl, and O, and the Bi:O:Cl atomic ratio about 1:1:1. The standard deviation of the 1:1:1 ratio of the synthesized BiOCl is 0.02:0.023:0.0098 (average of fi ve measurements). The crystalline structure and morphology of the BOC MPs are further demonstrated and analyzed by transmission electron microscopy (TEM) and high-resolution TEM (HRTEM). As shown in Figure 2 a, the BOC MPs are placed on the copper grid for TEM study. The HRTEM image of a single BiOCl MP (see Figure 2 b,c) shows highly crystalline nature and clearly two sets of lattice fringes with a lattice spacing of 0.275 nm corresponding to the (110) atomic planes. The corresponding selected-area electron diffraction (SAED) pattern (see Figure 2 d) exhibits the single-crystalline characteristic of the BOC MPs, which is consistent with the XRD result (Figure 1 c). The angle labeled in the SAED pattern is 45°, in good agreement with the theoretical value of the angle between the (110) and (200) planes. The set of diffraction spots can be indexed as the [001] zone axis of tetragonal BiOCl. Based on the above structural analysis, it is concluded that the bottom and top surfaces of the BOC MP are identifi ed as {001} facets (Figure 2 e), while the four major lateral surfaces are {110} facets (Figure 2 f). Recently, great progress has been witnessed in the research of layered materials such as Bi 2 Se 3 , [ 1–4 ] FeSe, [ 5–8 ] Bi O S system [ 9–11 ] at the frontiers of these areas: topological insulators, iron-based superconductors, and bismuth-based superconductors. [ 12–14 ] Similar to these important materials, bismuth oxychloride (BiOCl) is a layered structure consisting of [Cl Bi O Bi Cl] sheets stacked together by the nonbonding interaction through the Cl atoms along the c -axis. [ 15 ] BiOCl has received much attention because of its excellent performance in photonics and photocatalysis due to its unique layered structure and high chemical stability. [ 16 ] Besides the utilization in photonic and photocatalysis, BiOCl can also be widely used in inorganic pigments and high-quality cosmetics. [ 17 ]