Abstract:The microstructure, stress rupture properties and deformation mechanisms of a new alloy during long-term aging were investigated. The microstructure evolution mainly included the coarsening of gamma' phase and the precipitation of eta phase. During aging at 700 degrees C, 750 degrees C and 800 degrees C, the coarsening rate k of gamma' phase was about 7.818 nm(3)/h, 42.927 nm(3)/h and 178.226 nm(3)/h, respectively. The activation energy Q for gamma' coarsening was about 279.98 kJ/mol, which meant that element diffusion controlled the coarsening of gamma' phase. After aging at 750 degrees C for 3000 h and 800 degrees C for 2000 h, a new needle-like eta phase was precipitated near GBs and around MC carbides, then grew into the grain interiors. The quantity of eta phase increased with the increase of aging time. With the growth of eta phase, gamma' depleted zones were found around eta phase. This was principally because both gamma' phase and eta phase were enriched in Ni and Ti, and the growing up of I phase absorbed gamma' phase. After aging at 700 degrees C for 300-3000 h and 750 degrees C for 300-2000 h, the stress rupture life at 750 degrees C/430 MPa remained at a high level and most of them were higher than 100 h. That was because the slightly grown-up gamma' phase acted as strong obstacles to the dislocation motion, Orowan bypassing combing stacking fault shearing acted as the dominant mechanism during stress rupture deformation. After aging at 750 degrees C and 800 degrees C for 3000 h, the stress rupture life decreased to 45.7 h and 7.68 h, respectively. One reason was that the seriously grown-up gamma' phase was very hard to impede the dislocation motion, almost all gamma' phases were cut by dislocations with leaving stacking faults inside them during stress rupture deformation. The other reason was that needle-like eta phase promoted dislocation pile-up and contributed to the nucleation of micro-cracks, meanwhile the gamma' depleted zones could be conductive to the propagation of micro-cracks.

Study on the Ageing Process of a Super High-strength Cu-Ni-Si Alloy

The Effect of Al on Microstructure and Properties of Cu-15Ni-8Sn During the Aging

Transformation and Strengthening of Early Stage of Aging in Cu-3.2Ni-0.75Si Alloy

Aging transformation in Cu-3.2Ni-0.75Si alloy

Structure and strength of the age hardened Cu–Ni–Si alloy

Ageing Behavior of Cu-15Ni-8Sn Alloy Prepared by Mechanical Alloying

Microstructure and Mechanical Properties of Cast Cu-15Ni-8Sn Alloy

Microstructure and Precipitate Evolution in Cu-3.2Ni-0.75Si Alloy Processed by Twin-Roll Strip Casting

Microstructure evolution and aging hardening in a Cu-25Ni-25Mn alloy

Microstructure Evolution and Mechanical Property of Cu-15Ni-8Sn-0.2Nb Alloy During Aging Treatment

Spinodal Decompositions in Cu-15Ni-8Sn Alloys Prepared by Mechanical Alloying and Casting

Effects of Microstructure Evolution on the Deformation Mechanisms and Tensile Properties of a New Ni-base Superalloy During Aging at 800 °C

Study of Aging Temperature on the Thermal Compression Behaviors and Microstructure of a Novel Ni-Cr-Co-Based Superalloy

Effect of Aging Temperature on Microstructure and Properties of Cold-Rolled Cu-Ni-Si Alloy

Microstructure and Hardness of Cast Cu-15Ni-8Sn-xTi Alloys

Coarsening behavior of (Ni, Co)2Si particles in Cu–Ni–Co–Si alloy during aging treatment

Microstructure and Mechanical Properties of Cast Al-Si-Cu-Mg-Ni-Cr Alloys: Effects of Time and Temperature on Two-Stage Solution Treatment and Ageing

Microstructure evolution and precipitation behaviour of the Cu-Ni-Si-Cr alloy based on twin-roll strip casting

Effects of Ageing on Microstructure, Martensitic Transformation and Shape Memory Performance of a Ni-rich Ti49.5Ni34.5Cu11.5Pd4.5 Alloy

Microstructure and Precipitate's Characterization of the Cu-Ni-Si-P Alloy

Effect of Long-Term Aging on the Microstructure, Stress Rupture Properties and Deformation Mechanisms of a New Cast Nickel Base Superalloy