Experimental Study and FEM Analysis of Dynamic Response in Metals During Plate Impact

DB Wei,JT Han,AK Tieu,ZY Jiang

DOI: https://doi.org/10.1063/1.1766574

2004-01-01

AIP Conference Proceedings

Abstract:The method of plate impact was applied to produce internal crack at a predictable position in pure copper and 1045 steel at high strain rate. The size of targets was designed specially to produce three specimens that have the same state of damage at a predictable position within one test. Different scale of internal cracks can be obtained at different velocities of plate impact which is from 81.1 to 191.1m/s. Nondestructive test by the ultrasonic scanning method was used to inspect the internal cracks distribution in specimens to acquire the pseudo 3D images. The ratio of internal crack area to the whole specimen area on the projection was calculated. The morphology of cracks on the section plane of one target was observed under SEM. It shows that the spallation was made up of many discontinuous tiny cracks. Among these tiny cracks is the tearing steel matrix. The micro-cracks whose width is less than 1 Em exist at the tips of the spallation area. The FEM program for transient analysis was employed to simulate waves interaction in targets at the moment of plate impact at the velocity of 191.1m/s. The equivalent stress concentration area appears and moves to the free surface near the center of target at t=0.007s. The disturbance moves out from targets and the tensile stress concentration area is at the center of target at t=0.01s.