Abstract:Precursor powders of La0.6Sr0 4CoO3-delta (LSC) and composite powders of LSC precursor and Ce0.8Gd0 2O2-delta (CGO) were prepared by Sol-Gel process. The precursor powders of LSC were characterized by TGA, XRD, BET and exhibited homogeneity and high specific surface area. XRD analysis indicated that single phase of LSC can be formed after calcination at high temperature in Ar and annealing at 850 degrees C for 2 h in air, which corresponds to the fabrication and annealing condition of functionally graded cathode before SOFC stack operation. Functionally graded cathode of LSC/CGO precursor and LSC precursor were sintered at 900-1000 degrees C in Ar, which were deposited on NiO/YSZ anode supported half cell with YSZ as electrolyte layer and CGO as barrier layer. Microstructural analysis by SEM and EDX indicated that graded cathode contacted well with CGO layer. It was found that SrZrO3 was formed at the YSZ-CGO boundary. The test of single SOFC cells with in-situ formed LSC showed that cell performance was improved with decrease of the sintering temperature. In comparison, the best cell performance was achieved at the sintering temperature 900 degrees C.

Fabrication and Characterization of Functionally Graded Cathodes Based on In-Situ Formed La0.6sr0.4coo3-Delta for Intermediate Temperature Sofcs