Wear Behaviour of a Plasma-Sprayed Al2O3-13%TiO2 Ceramic Coating/Steel Couple Under High Constant and Variable Loads
C. Soffritti,A. Fortini,M. Merlin,G. Garagnani,R. Aguilar
Abstract:INTRODUCTION Friction and wear are the major causes of loss of mechanical performances and energy dissipation in engine subsystems such as the engine block with pistons and cylinders, the transmission, the fuel system, the valve train and the exhaust system [1]. Concerning wear resistance of mechanical components, thermal-sprayed ceramic coatings on steel represent an efficient and economical alternative, when common thermo-mechanical processes and heat treatments are inadequate. These coatings may exhibit high hardness and chemical stability, are able to withstand high temperatures and are resistant to many corrosive environments. Some types of ceramics have already found application in engineering as tribological components, for example in cylinder head fire decks, piston crowns, exhaust valve faces and braking devices [2,3]. Among thermal-sprayed ceramic coatings, plasma-sprayed of Al2O3-TiO2 coatings provide protection against abrasive wear superior to that of traditional wear resistant hard chromium [4,5] and molybdenum [6,7] coatings. Under dry sliding conditions, plasma-sprayed Al2O3TiO2 coatings are known to form a porous tribofilm composed of plastically deformed wear debris, which does not protect the substrate from wear [4]. On these ceramic coatings, many different wear mechanisms are detected, involving abrasive wear [8], delamination and crack nucleation [9,10], and adhesive wear [9]. Several studies deal with the sliding wear resistance Wear Behaviour of a Plasma-Sprayed Al2O3-13%TiO2 Ceramic Coating/Steel Couple Under High Constant and Variable Loads
Engineering,Materials Science