In Situ Electrosynthesis of Hydrogen Peroxide with an Improved Gas Diffusion Cathode by Rolling Carbon Black and PTFE

Haijian Luo,Chaolin Li,Chiqing Wu,Xiaoqing Dong

DOI: https://doi.org/10.1039/c5ra09636g

IF: 4.036

2015-01-01

RSC Advances

Abstract:A simply structured gas diffusion electrode (GDE) was constructed by rolling carbon black and PTFE as a conductive catalyst layer to enhance the producibility of hydrogen peroxide.

What problem does this paper attempt to address?

In Situ Generation of Hydrogen Peroxide Using Polymetallic-Doped G-C3n4 for Pollutant Removal

Liyan Wang,Jianqing Ma,Qianhui Guo,Liang Liu,Jiangnan Shou,Aojie Sun,Liaoyuan Zhao

DOI: https://doi.org/10.3390/app112210797

2021-01-01

Applied Sciences

Abstract:Fenton reaction is a powerful technology for pollutants’ removal from water. However, the cost of H2O2 becomes one of the major stumbling blocks in its application. H2O2 has a relatively high price and is easily decomposed during transportation and use; therefore, in situ synthesis of H2O2 could improve economic benefits effectively. In this study, a Fe/Ni/Pd ternary metal-doped graphitic carbon nitride (FeNi-Pd@CN) is prepared, and in situ H2O2 generation using formic acid as hydrogen sources for organics removal was proved. The catalyst is advantageous, as H2O2 could accumulate to 1.69 mmol/L in 150 min when pumping air rather than oxygen gases in other studies. Furthermore, 92.0% of Acid Red 73 (200 mg/L) and 93.2% of tetracycline hydrochloride (10 mg/L) could be removed in 150 min without any pH adjustment. Characterization results show that the catalyst has good stability in metal leaching and reuse tests. It is proved that •OH and •O2− are the main reactive oxygen species, and a synergistic effect between Fe and Ni exists that enhances ROS generation for organics degradation. This work offers a promising method to remove refectory organic contaminants from industrial wastewater.
Novel Gas Diffusion Electrode System for Effective Production of Hydrogen Peroxide

Yan Hou,Fan Gong Kong,Shou Juan Wang,Gui Hua Yang

DOI: https://doi.org/10.4028/www.scientific.net/amm.496-500.159

2014-01-01

Applied Mechanics and Materials

Abstract:Hydrogen peroxide production via cathodic reduction of oxygen on self-made gas diffusion electrode was investigated in an undivided electrochemical system. The effects of mass ratio between graphite and PTFE in cathode, the calcination temperature, current density, pH, and plate distance on hydrogen peroxide generation were discussed. The results showed that the self-made gas diffusion cathode had high catalyze capacity for production of hydrogen peroxide using cathodic oxygen-reducing reaction. The hydrogen peroxide concentration could reach 80.52 mg·L - 1 within 2 h. The optimal conditions for this system are as follows: mass ratio of graphite to PTFE in cathode, 21, calcination temperature, 300 °C, current density,4.69mA/cm 2, pH 13.0, and the distance between anode and cathode, 8cm. The high concentration of hydrogen peroxide generated gives a promising application of this novel gas diffusion electrode system in pulp bleaching and waste-water treatment.
Solvent Engineering of Oxygen‐Enriched Carbon Dots for Efficient Electrochemical Hydrogen Peroxide Production (small 43/2023)

Xiaoyu Shen,Zeming Wang,Huazhang Guo,Zhendong Lei,Zheng Liu,Liang Wang

DOI: https://doi.org/10.1002/smll.202370357

IF: 13.3

2023-01-01

Small

Abstract:Carbon Dot Electrocatalysts In article number 2303156, Zhendong Lei, Zheng Liu, Liang Wang, and co-workers establish an innovative and scalable solvent engineering strategy to fabricate oxygen-doped carbon dots, resulting in an exceptional electrocatalysis H2O2 productivity yield of 111.18 mg h−1 cm−2 in a flow cell for a duration of 10 hours.
Electrogeneration of hydrogen peroxide in gas diffusion electrodes modified with tert-butyl-anthraquinone on carbon black support

Ricardo B. Valim,Rafael M. Reis,Pollyana S. Castro,Alex S. Lima,Robson S. Rocha,Mauro Bertotti,Marcos R.V. Lanza

DOI: https://doi.org/10.1016/j.carbon.2013.04.100

IF: 10.9

2013-09-01

Carbon

Abstract:Hydrogen peroxide (H2O2) is a versatile oxidizing agent that is synthesized commercially by the reduction of oxygen in organic medium. Electrochemical technology employing a modified gas diffusion electrode (MGDE) offers a viable alternative for the industrial-scale synthesis of the oxidant. Addition of 1% (w/w) of tert-butyl-anthraquinone (TBAQ) to carbon black deposited in the form of a microporous layer onto the disk of a rotating ring-disk electrode produced an increase in the ring current, which is directly related to H2O2 formation, and presented an efficiency of H2O2 generation of 89.6% compared with 76.6% for carbon black alone. No significant changes were detected in the number of electrons transferred in the presence of the catalyst suggesting an electrochemical/chemical mechanism for H2O2 formation. Analogous improvements in the generation of H2O2 were obtained with MGDEs comprising TBAQ on carbon black. The highest concentrations of H2O2 (301mgL−1) were produced at the fastest rate (5.9mgL−1min−1) with the lowest energy consumption (6.0kWhkg−1) when a potential of −1.0V vs SCE was applied to a MGDE containing 1.0% of TBAQ on carbon black. It is concluded that the application of MGDEs comprising TBAQ on carbon black support offers considerable advantages in the electrogeneration of H2O2.

materials science, multidisciplinary,chemistry, physical
High effective generation of hydrogen peroxide by adjusting three-phase interfaces of gas diffusion electrode during the oxygen reduction reaction

KwangChol Ri,Shaogui Yang,Dunyu Sun,Qiang Zhong,Leliang Wu,SongIl Sin,Chenmin Xu,Yazi Liu,Chengdu Qi,Huan He,Shiyin Li,Cheng Sun

DOI: https://doi.org/10.1016/j.seppur.2024.126351

IF: 8.6

2024-01-14

Separation and Purification Technology

Abstract:Mass transfer of oxygen is a critical issue in the two-electron oxygen reduction reaction (2e − ORR) for the generation of hydrogen peroxide (H 2 O 2 ). In this study, a novel constant velocity gas diffusion electrode (CVGDE) that can control the gas flow rate through the catalyst layer was fabricated, and the effect of the gas flow rate on three-phase interfaces (TPIs) formation and the mass transfer of oxygen in gas diffusion electrode (GDE) was investigated. In CVGDE, oxygen mass transfer was significantly improved, and the yield of H 2 O 2 reached up to 73.65 mg cm −2 h −1 at 200 mA cm −2 , which was 74.3 % higher than that of conventional GDE. Furthermore, the oxygen utilization efficiency of CVGDE reached 22.4 %, and the aeration energy consumption was decreased to 5.48 Wh kg −1 , which was 1000 times less than the energy consumption required for H 2 O 2 electrosynthesis. The experiments and theoretical calculations showed that the dynamic equilibrium state of TPI was achieved by the influence of both the electric field and air flow in the catalyst layer, which leading to a substantial increase in oxygen mass transfer and H 2 O 2 yield. Finally, CVGDE was utilized in the electro-Fenton process for the degradation of organic contaminants. This study will contribute to the understanding of the oxygen mass transfer process in GDE.

engineering, chemical
Improving the yield of hydrogen peroxide on gas diffusion electrode modified with tert-butyl-anthraquinone on different carbon support

Xiaoye Lu,Minghua Zhou,Yawei Li,Pei Su,Jingju Cai,Yuwei Pan

DOI: https://doi.org/10.1016/j.electacta.2019.07.063

IF: 6.6

2019-10-01

Electrochimica Acta

Abstract:Hydrogen peroxide (H2O2) is a green oxidant that widely used in environmental remediation and chemical industries, hence the exploration of suitable modified cathode for the cost-effective electrochemical synthesis of H2O2 is of great importance. In this work, tert-butyl-anthraquinone (TBAQ) was attempted to modify four kinds of typical carbon materials (carbon aerogel, carbon nanotube (CNT), carbon black and graphene-doped carbon black) to fabricate gas diffusion electrode (GDE) to improve H2O2 production for potential use in electro-Fenton process. It was found that CNT-GDE containing 2% TBAQ had the highest H2O2 production (150.6 mg/L) with a high current efficiency (95%) and low energy consumption (2.43 kWh/(kg H2O2)) among four carbon materials because of the redox of TBAQ and more active sites (C–C sp3 carbon and oxygen-containing functional groups). The effects of TBAQ addition amount, current and initial pH on H2O2 performance were investigated. The presence of TBAQ could improve oxygen reduction activity, H2O2 selectivity and hydrophobicity to improve H2O2 production. Suitable current (50 mA) and initial pH benefited the enhancement in H2O2 production. The CNT-GDE containing 2% TBAQ showed better H2O2 production performance with good stability when comparing with literature, indicating promising for electro-Fenton application.

electrochemistry
Cathodic Hydrogen Peroxide Electrosynthesis Using Anthraquinone Modified Carbon Nitride on Gas Diffusion Electrode

Qianhong Zhu,Zhenhua Pan,Shu Hu,Jae-Hong Kim

DOI: https://doi.org/10.1021/acsaem.9b01445

IF: 6.4

2019-11-13

ACS Applied Energy Materials

Abstract:Electrochemical synthesis of hydrogen peroxide from oxygen and water can be a cost-effective and energy-efficient alternative to the traditional approach which requires high energy input and expensive noble metal catalysts and has a large CO2 footprint. The availability of selective electrocatalysts and performance validation of a device represent current research needs toward this goal. Herein, we report an efficient electrocatalytic system for hydrogen peroxide production based on anthraquinone molecular catalysts which are tethered onto carbon nitride (C3N4) conductive supports. Anthraquinone enables highly selective synthesis of hydrogen peroxide via two-electron oxygen reduction. The optimal electrolyte pH was identified to both facilitate H2O2 electrochemical synthesis and minimize H2O2 decomposition. The anthraquinone-functionalized C3N4 supports were then adapted into a gas diffusion cathode configuration to greatly enhance the mass transport of oxygen reactants. The device fabricated in this study achieved an optimal H2O2 production rate of 60.1 mmol gcatalyst–1 h–1 at a maximum Faradaic efficiency of 42.2%.

materials science, multidisciplinary,chemistry, physical,energy & fuels
Electrical Activation of Hydrogen Peroxide for Organic Contaminant Degradation Using an Improved Gas Diffusion Cathode

Luo Haijian,Li Chaolin,Sun Xue,Jiang Jiao

DOI: https://doi.org/10.2991/iceep-17.2017.77

2017-01-01

Abstract:Electrochemical degradation technology, being an environment-friendly way for the elimination of a broad-range of organic contaminants from water, is limited by low efficiency and high cost. In this study, an improved gas diffusion electrode (GDE) was constructed by rolling carbon black and polytetrafluoroethylene as conductive catalyst layer to improve the hydrogen peroxide production. The maximum concentration of 259.6 mM was obtained after 60 min, which is roughly eight times higher than the value obtained using the traditional reference cathode. Experiments indicated that the degradation of phenol in the electrochemical process was dominated by radical based mechanisms, which was obtained by the electro-generation and the subsequent electro-activation of hydrogen peroxide at the cathode interface.
Use of Gas Diffusion Electrode for the In Situ Generation of Hydrogen Peroxide in an Electrochemical Flow-By Reactor

Rafael M. Reis,André A. G. F. Beati,Robson S. Rocha,Mônica H. M. T. Assumpção,Mauro C. Santos,Rodnei Bertazzoli,Marcos R. V. Lanza,André A. G. F. Beati,Mônica H. M. T. Assumpção

DOI: https://doi.org/10.1021/ie201317u

2011-12-07

Abstract:Hydrogen peroxide is a powerful oxidant that finds application in several areas, but most particularly in the treatment of industrial wastewaters. The aim of the present study was to investigate the effects of applied potential and electrolyte flow conditions on the in situ generation of hydrogen peroxide in an electrochemical flow-by reactor with a gas diffusion electrode (GDE). The electrolyses were performed in an aqueous acidic medium using a GDE constructed with conductive black graphite and polytetrafluoroethylene (80:20 w/w). Under laminar flow conditions (flow rate = 50 L/h), hydrogen peroxide was formed in a maximum yield of 414 mg/L after 2 h at −2.25 V vs Pt //Ag/AgCl (global rate constant = 3.1 mg/(L min); energy consumption = 22.1 kWh/kg). Under turbulent flow (300 L/h), the maximum yield obtained was 294 mg/L after 2 h at −1.75 V vs Pt//Ag/AgCl (global rate constant = 2.5 mg/(L min); energy consumption = 30.1 kWh/kg).

engineering, chemical
Oxygen-rich hierarchical activated coke-based gas diffusion electrode enables highly efficient H2O2 synthesis via O2 electroreduction

Wei Zhou,Liang Xie,Yan Wang,Yani Ding,Xiaoxiao Meng,Fei Sun,Jihui Gao,Guangbo Zhao

DOI: https://doi.org/10.1016/j.seppur.2022.122740

IF: 8.6

2023-02-01

Separation and Purification Technology

Abstract:Large-scale application of H2O2 production through 2-electron oxygen reduction reaction (2eORR) greatly depends on the cost of electrode materials and configuration. In this work, engineered coal-derived oxygen-rich hierarchical activated coke (AC), which is low-cost and highly tunable in porosity and surface chemistry, was used as catalyst to fabricate gas diffusion electrodes (GDEs) for efficient H2O2 production. Results showed that Fenton’s reagents treatment could significantly increase the contents of CO and –COOH on AC, leading to an increased hydrophilicity. However, the higher O contents do not necessarily enhance the selectivity of AC towards 2eORR (i.e., F-5-AC, F-10-AC), especially that F-20-AC exhibited a complete 4e pathway. GDEs were then fabricated with AC and oxidized AC as catalyst, key fabrication parameters including the PTFE binder and AC particle size, and operating parameters such as current intensity, electrolyte pH, and O2 flow rate were optimized. Up to 747 mg/L H2O2 were generated within 90 min. Results showed that oxidized AC exhibited a decreased H2O2 yield, due to the flooding of GDEs caused by super-hydrophilicity property. Finally, DFT calculations were employed to reveal the synergistic effect of different O groups considering the fact of high O contents on AC.

engineering, chemical
Highly Active and Cheap Graphite/polytetrafluoroethylene Composite Coating Cathodes for Electrogeneration of Hydrogen Peroxide

Wang Kang,Zhu Zhaolian,Xu Dan,Li Muyao,Yuan Shiyu,Wang Hailing

DOI: https://doi.org/10.1007/s10098-022-02323-z

IF: 4.3

2022-01-01

Clean Technologies and Environmental Policy

Abstract:Using cheap graphite powder as catalyst and polytetrafluoroethylene (PTFE) as binder, graphite/PTFE composite coating cathodes were fabricated for efficient electrochemical synthesis of hydrogen peroxide (H 2 O 2 ) in a no-diaphragm electrolysis system. A series of experiments were conducted to examine the influence of different factors, such as cathode thickness, cathode area, solution pH, and current density on H 2 O 2 electrogeneration. Adjusting the thickness and area of the cathode was demonstrated to be effective in optimizing the electrocatalytic properties in oxygen reduction reaction (ORR). Among the cathodes investigated, the cathode with the thickness of 0.75 mm and area of 16 cm 2 achieved the highest H 2 O 2 accumulation and current efficiency (CE). The H 2 O 2 accumulation reached 207.5 mg·L –1 and CE reached 34.1% in 180 min when the current density is 5 mA·cm −2 and the initial pH is 3.0. The present work successfully develops a simple approach to enhance the H 2 O 2 electrogeneration, as well as the corresponding CE, through optimization of cathode geometric parameters and operation conditions.
Insight into the Deterioration Mechanism of Gas Diffusion Electrode During Long-Term Electrosynthesis of Hydrogen Peroxide under Industrially Relevant Current Densities

Erzhuo Zhao,Shiyi Wang,Gang Yu,Yujue Wang

DOI: https://doi.org/10.1016/j.electacta.2024.144835

IF: 6.6

2024-01-01

Electrochimica Acta

Abstract:The long-term stability of gas diffusion electrodes (GDEs) is critical for industrial H2O2 electrosynthesis from twoelectron oxygen reduction reaction (2e-ORR), but has rarely been investigated. Herein, we evaluated the stability of carbon black-polytetrafluoroethylene (CB-PTFE) based GDEs during H2O2 electrosynthesis in sodium sulfate (Na2SO4) electrolytes under industrially relevant conditions. Results show that the GDEs maintained stable H2O2 production with Faradaic efficiencies (FEs) of 75 % for 300 h under 150 mA/cm2. However, FEs then declined gradually to eventually 15 % at 840 h, after which the GDE failed due to water flooding. Increasing applied current density to 200 mA/cm2 accelerated the deterioration process and caused electrode failure after 350 h operation. Characterizations of the GDEs used for varying durations indicate that the deterioration of GDEs is mainly caused by oxidation of CB catalysts, defluorination of PTFE, and intercalation of Na in CB particles during H2O2 electrosynthesis. These three interrelating mechanisms gradually decreased the hydrophobicity, the 2e-ORR activity and selectivity of GDEs, and increased the porosity of GDEs. These changes in turn promoted H2O2 decomposition and progressive water intrusion into the internal pores of GDEs during H2O2 electrosynthesis, thus causing the gradual decreases of FEs and electrode flooding. Due to the gradual changes of GDE properties, it is challenging to maintain long-term stable H2O2 production under industrially relevant current densities. More studies are needed to improve the design and operation of GDEs to resolve the deterioration process of GDEs and thus extend their lifetime during H2O2 electrosynthesis.
Janus graphite felt cathode dramatically enhance the H2O2 yield from O2 electroreduction by the hydrophilicity-hydrophobicity regulation

Wei Zhou,Xiaoxiao Meng,Jihui Gao,Fei Sun,Guangbo Zhao

DOI: https://doi.org/10.1016/j.chemosphere.2021.130382

IF: 8.8

2021-09-01

Chemosphere

Abstract:<h2 class="section-title u-h3 u-margin-l-top u-margin-xs-bottom">s</h2>Hydrogen peroxide (H2O2) electrosynthesis from 2-electron O2 reduction reaction (2eORR) is widely regarded as a promising alternative to the current industry-dominant anthraquinone process. Design and fabrication of effective, low-cost carbon-based electrodes is one of the priorities. Many previous work well confirmed that hydrophilic carbon-based electrodes are preferable for 2eORR. Here, we proposed a strategy of hydrophilicity-hydrophobicity regulation. By using commercially available graphite felt (GF) as electrodes, we showed that both hydrophilic GF, hydrophobic GF, and Janus GF yielded significantly higher H2O2 production, which is 7.3 times, 7.6 times, and 7.7 times higher than the original GF, respectively. Results showed that currents and stirring rates affect the H2O2 yields. The enhancement of hydrophilic GF is due to the incorporation of oxygen-containing functional groups, while the hydrophobic and Janus GF comes from the locally confined O2 bubbles, which built a gas-liquid-solid interface inside GF and thus enhance the H2O2 formation kinetics. Finally, the effectiveness of the hydrophilicity-hydrophobicity regulation concept was tested in Electro-Fenton process by removing typical dyes and antibiotics. This work supply an effective but facile strategy to enhance the performance of carbon-based electrodes towards 2eORR by regulating the micro-environment of electrodes.

environmental sciences
Activated carbon filled in a microporous titanium-foam air diffusion electrode for boosting H2O2 accumulation

Fengxia Deng,Shilin Yang,Baojian Jing,Shan Qiu

DOI: https://doi.org/10.1016/j.chemosphere.2023.138147

IF: 8.8

Chemosphere

Abstract:In the electro-Fenton process, there still suffers concern of low H2O2 generation caused by inadequate mass transfer of oxygen and low selectivity of oxygen reduction reaction (ORR). To solve it, in this study, various particle sizes (850 μm, 150 μm, and 75 μm) of granular activated carbon filled in a microporous titanium-foam substate was used to develop a gas diffusion electrode (AC@Ti-F GDE). This facile-prepared cathode has seen a 176.15% improvement in H2O2 formation compared to the conventional one. Aside from a much higher oxygen mass transfer by creating gas-liquid-solid three-phase interfaces coupled with much high dissolved oxygen, the filled AC played a significant role in H2O2 accumulation. Among these particle sizes of AC, the one in 850 μm has observed the highest H2O2 accumulation, reaching 1487 μM in 2 h electrolysis. Because there is a balance between chemical nature for H2O2 formation and micropore-dominant porous structure for H2O2 decomposition, resulting in an electron transfer of 2.12 and H2O2 selectivity of 96.79% during ORR. In a word, the facial AC@Ti-F GDE configuration is promising for H2O2 accumulation.
Trans-electrode pressure of gas-diffusion electrodes significantly influencing the electrochemical hydrogen peroxide production

Anlin Xu,Ziyan Yang,Zhiyi Zhou,Pu Yang,Yang Yu,Jiayang Liu,Yunhai Zhang

DOI: https://doi.org/10.1016/j.chemosphere.2024.142464

IF: 8.8

2024-05-28

Chemosphere

Abstract:Hydrogen peroxide (H 2 O 2 ) synthesis by electrochemical two-electron oxygen reduction has garnered increasing interest as a wide range of potential applications. Gas diffusion electrodes (GDEs) can effectively promote the H 2 O 2 production efficiency by overcoming the oxygen mass transfer limitations but strongly influenced by the electrowetting process along the long-term operation. In this study, the effect of trans-electrode pressure (TEP) of GDE cathode on the electrowetting process was further elucidated. We controlled the TEP values of four types of GDEs: two Ni-based GDEs and two carbon cloth GDEs prepared by hot-pressing or brushing carbon black. SBA-15 was further used to regulate the microstructure of one Ni-based GDE. It was found that an optimal range of TEP occurred for all tested GDEs in terms of the max. concentration, the yield efficiency, the energy consumption, and the stability because TEP may change the triple-phase interface and influence the anti-electrowetting effect. The porosity of hot-pressed Ni GDE can maintain the TEP window and thus enhance the production of H 2 O 2 , likely via creating oxygen-containing functional groups and a bimodal pore structure on the electrode, revealed with several characterization techniques including SEM, CA, XPS, Raman spectra, CV and EIS. The porous Ni GDE presented an efficient and stable production of H 2 O 2 for 10 cycles: yielding H 2 O 2 at 4393.2 to 4602.2 mmol m -2 h -1 with current efficiencies of 94.2 ∼ 98.7%. The best accumulated H 2 O 2 concentration can reach up to 3.58 ωt% H 2 O 2 at 10 h. The results provide an important reference for the industrial scaleup of electro-production of H 2 O 2 with GDEs.

environmental sciences
Highly efficient electrosynthesis of hydrogen peroxide through the combination of side aeration and vacuum filtration modified graphite felt

Mingran Li,Huachun Lan,Xiaoqiang An,Xia Qin,Zilong Zhang,Tinghui Li

DOI: https://doi.org/10.1016/j.apcatb.2023.123125

2023-12-01

Abstract:The electrocatalytic activity towards two electron oxygen reduction reaction of graphite felt was advanced by incorporating carbon nitride, carbon nanotubes and polytetrafluoroethylene through vacuum filtration, which prevented the cleavage of O-O bond, facilitated the charge transfer, and established more three-phase active sites. To ameliorate the oxygen transfer process, the configuration of side-aeration was proposed, providing forced convection to reduce the thickness of diffusion layer, and increasing the dissolved oxygen. By simplified combination of refining the orientation of gas flow and modified graphite felt, the dual-chamber configuration rendered a qualitative leap in H2O2 generation capacity to 4.44–6.89 mg h−1 cm−2. The alkaline affinity of developed system was discussed in terms of a beneficial outer-sphere electron transfer pathway, the variation on adsorption strength of oxygenated species and working electrode potential range. Finally, Long-term operation stability and successful application in Electro-Fenton indicated great potential of developed system for H2O2 synthesis and environmental remediation.

chemistry, physical,engineering, chemical, environmental
Electrogeneration of H2O2 Using a Porous Hydrophobic Acetylene Black Cathode for Electro-Fenton Process

Linchao Li,Huili Hu,Xiangguo Teng,Yuanchun Yu,Yongming Zhu,Xiaoqiang Su

DOI: https://doi.org/10.1016/j.cep.2018.09.013

IF: 4.264

2018-01-01

Chemical Engineering and Processing - Process Intensification

Abstract:The aim of this work is to prepare a hydrophobic cathode equipped with quite a few cracks for gas transfer, which can prepare H2O2 in the course of electro-Fenton process. Scanning electron microscopy (SEM) and optical digital microscope are used to characterize the morphology of electrode, and an electrochemical workstation (CHI660e) is used to carry out all electrochemical studies with a conventional three-electrode system. The results demonstrate that the porous electrode is conducive to gas transmission with these cracks which can avoid the formation of bubbles. Additionally, the reaction is almost not affected by the content of dissolved oxygen and the gas flow with this structure. Under the conditions of 300 mA/cm(2) (current density), the H2O2 concentration is up to 14.4 mmol/L after 30 min electrolysis with current efficiency beyond 90%. Furthermore, the cathode is successfully applied to electro-Fenton process which reduced catalyst loading. The results indicate that total degradation of MO is observed at the first 10 min, and 81% of TOC can be removed when the dosage of catalyst is 0.4 mmol/L within 60 min.
Boosting Hydrogen Peroxide Accumulation by a Novel Air-Breathing Gas Diffusion Electrode in Electro-Fenton System

Yanshi Zheng,Junguo He,Shan Qiu,Dehai Yu,Yingshi Zhu,Heliang Pang,Jie Zhang

DOI: https://doi.org/10.1016/j.apcatb.2022.121617

2022-01-01

Abstract:Electro-Fenton (EF) is a promising electrochemical technology in degrading recalcitrant organic pollutants. However, the technology faces problems of high energy consumption, low cathodic oxygen transfer rate and low H2O2 production efficiency. Therefore, a novel air-breathing gas diffusion electrode (GDE) with multiform hydrophobic layers was prepared by a facile method. The novel GDE allows the air to diffuse to the triphase interface spontaneously, eliminating the cost of aeration. Also, the multiform hydrophobic layers can greatly improve the oxygen transfer rate and expand the triphase interfaces in the GDE, resulting in a high H2O2 accumulation of 44.30 mg L- 1 cm(-2) h(-1) without aeration, which was 18 times higher than that of the virgin cathode. A 100% degradation efficiency of sulfadiazine (SDZ) was achieved with the fabricated GDE in 10 min in EF system. Moreover, theoretical calculations were performed for accurately elucidating the SDZ degradation mechanism and pathway.
A novel dual gas diffusion electrodes system for efficient hydrogen peroxide generation used in electro-Fenton

Xinmin Yu,Minghua Zhou,Gengbo Ren,Liang Ma

DOI: https://doi.org/10.1016/j.cej.2014.11.053

IF: 15.1

2015-03-01

Chemical Engineering Journal

Abstract:Highly efficient H2O2 generation is greatly demanded in electro-Fenton process for organic pollutants degradation. In the present work, a novel H2O2 generation reactor using dual gas diffusion electrodes (GDEs) as cathodes was put forward, which was confirmed to be more cost-effective in H2O2 generation rate, O2 utilization efficiency and energy consumption in comparison with other carbonaceous materials and reactors. The catalyst layer in GDE was characterized and optimized, and the accumulation of H2O2 reached to 566mg/L in 0.05M Na2SO4 at a current density of 7.1mA/cm2 and air flow rate of 0.5L/min after 180min. The operational parameters such as current density, pH and air flow rate were optimized, and after 10 times used the production of H2O2 was confirmed to be stable. This novel reactor was tested to degrade tartrazine, and even for a high initial concentration of 1000mg/L, it could be completely decolorized within 60min while the TOC removal efficiency could reach 66.1% within 120min with a mineralization current efficiency of 65.1%, indicating its potential for the treatment of high-concentrated wastewaters.

engineering, chemical, environmental
Efficient electrosynthesis of H 2 O 2 through electrodeposition-modified cathode and side-aeration integration

Yumei Yang,Xia Qin

DOI: https://doi.org/10.1016/j.jece.2024.112809

IF: 7.7

2024-04-21

Journal of Environmental Chemical Engineering

Abstract:Electro-Fenton (EF) process, featuring in-situ hydrogen peroxide (H 2 O 2 ) production, has received increasing attention for its efficacy in degrading organic pollutants. However, challenges such as low oxygen utilization efficiency and high energy consumption persist. In this study, a novel Carbon Black-loaded Carbon Felt (CB-CF) electrode using the electrophoretic deposition (EPD) technique was prepared to boost the efficiency of H 2 O 2 production. Various aeration patterns and aeration gas were systematically introduced to assess the oxygen utilization pathway and improve oxygen utilization efficiency. The CB-CF cathode, forming an efficient triphase interface, coupled with the side-oxygen mode, demonstrates rapid H 2 O 2 production (48.82 mg/h) at a remarkably low energy consumption (14.46kWh·kg −1 ) with the current density of 15 mA/cm 2 . The fabricated CB-CF exhibited exceptional performance, achieving over 90% degradation efficiency of Fulvic Acid (FA) within 60 minutes in the EF system. Stability experiments underscored the impact of current density and hydrophobicity on the electrode but revealed that PTFE recoating effectively preserves stability. Furthermore, the straightforward and efficient electrode preparation process, combined with the favorable electrochemical properties of CB-CF, positions it as a promising candidate for large-scale applications in H 2 O 2 electro-synthesis and environmental remediation.

engineering, chemical, environmental

In Situ Electrosynthesis of Hydrogen Peroxide with an Improved Gas Diffusion Cathode by Rolling Carbon Black and PTFE

In Situ Generation of Hydrogen Peroxide Using Polymetallic-Doped G-C3n4 for Pollutant Removal

Novel Gas Diffusion Electrode System for Effective Production of Hydrogen Peroxide

Solvent Engineering of Oxygen‐Enriched Carbon Dots for Efficient Electrochemical Hydrogen Peroxide Production (small 43/2023)

Electrogeneration of hydrogen peroxide in gas diffusion electrodes modified with tert-butyl-anthraquinone on carbon black support

High effective generation of hydrogen peroxide by adjusting three-phase interfaces of gas diffusion electrode during the oxygen reduction reaction

Improving the yield of hydrogen peroxide on gas diffusion electrode modified with tert-butyl-anthraquinone on different carbon support

Cathodic Hydrogen Peroxide Electrosynthesis Using Anthraquinone Modified Carbon Nitride on Gas Diffusion Electrode

Electrical Activation of Hydrogen Peroxide for Organic Contaminant Degradation Using an Improved Gas Diffusion Cathode

Use of Gas Diffusion Electrode for the In Situ Generation of Hydrogen Peroxide in an Electrochemical Flow-By Reactor

Oxygen-rich hierarchical activated coke-based gas diffusion electrode enables highly efficient H2O2 synthesis via O2 electroreduction

Highly Active and Cheap Graphite/polytetrafluoroethylene Composite Coating Cathodes for Electrogeneration of Hydrogen Peroxide

Insight into the Deterioration Mechanism of Gas Diffusion Electrode During Long-Term Electrosynthesis of Hydrogen Peroxide under Industrially Relevant Current Densities

Janus graphite felt cathode dramatically enhance the H2O2 yield from O2 electroreduction by the hydrophilicity-hydrophobicity regulation

Activated carbon filled in a microporous titanium-foam air diffusion electrode for boosting H2O2 accumulation

Trans-electrode pressure of gas-diffusion electrodes significantly influencing the electrochemical hydrogen peroxide production

Highly efficient electrosynthesis of hydrogen peroxide through the combination of side aeration and vacuum filtration modified graphite felt

Electrogeneration of H2O2 Using a Porous Hydrophobic Acetylene Black Cathode for Electro-Fenton Process

Boosting Hydrogen Peroxide Accumulation by a Novel Air-Breathing Gas Diffusion Electrode in Electro-Fenton System

A novel dual gas diffusion electrodes system for efficient hydrogen peroxide generation used in electro-Fenton

Efficient electrosynthesis of H 2 O 2 through electrodeposition-modified cathode and side-aeration integration