Ultrafast Oxidative Desulfurization of Diesel Fuels by Mass Transfer Enhancement of Polyoxometalate Modified Alumina Catalysts
Yubing Liu,Jinfeng Chu,Lifei Lian,Xiang Chen,Sai An,Lanlan Hong,Dongqi Wang,Wei Chen
DOI: https://doi.org/10.1021/acs.energyfuels.0c03673
2021-01-19
Abstract:Deep desulfurization of fuels has long been and remains to be a highly challenging issue. In this work, a trilacunary polyoxometalate of Na<sub>12</sub>[α-P<sub>2</sub>W<sub>15</sub>O<sub>56</sub>]·24H<sub>2</sub>O (P<sub>2</sub>W<sub>15</sub>) was covalently tethered onto the γ-Al<sub>2</sub>O<sub>3</sub> sphere, to which different alkyl chains (C<sub><i>n</i></sub>, <i>n</i> = 8, 12, or 18) were grafted, leading to the formation of the Al<sub>2</sub>O<sub>3</sub>-P<sub>2</sub>W<sub>15</sub>-C<i><sub>n</sub></i>. When the Al<sub>2</sub>O<sub>3</sub>-P<sub>2</sub>W<sub>15</sub>-C<sub><i>n</i></sub> were applied to catalyze oxidative desulfurization reaction of dibenzothiophene (DBT) in the presence of H<sub>2</sub>O<sub>2</sub>, it displayed high efficiency for removal of sulfur content in 9 min under optimized conditions at 60 °C. In addition, the Al<sub>2</sub>O<sub>3</sub>-P<sub>2</sub>W<sub>15</sub>-C<sub><i>n</i></sub> exhibited excellent structural stability during the catalytic reaction and can be used to remove 4,6-dimethyldibenzothiophene (4,6-DMDBT) and benzothiophene (BT) from fuel oils. The excellent performance of Al<sub>2</sub>O<sub>3</sub>-P<sub>2</sub>W<sub>15</sub>-C<sub>18</sub> was verified by sulfur removal for an actual diesel sample. Molecular dynamics simulations indicated that DBT showed strong tendency to be adsorbed on active sites, while DBTO<sub>2</sub> (dibenzothiophene sulfone) can be desorbed much easier. This work opens up a new avenue for further study on oxidative desulfurization catalytic materials and the influence of catalyst structure on mass transfer.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.0c03673?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.0c03673</a>.Characteristics of the simulated systems (Table S1), FT-IR spectra of catalysts (Figures S1 and S2), SEM and TEM images of catalysts (Figure S3), SEM-EDS of Al<sub>2</sub>O<sub>3</sub>-P<sub>2</sub>W<sub>15</sub>-C<sub>18</sub> (Figure S4), textural properties of catalysts (Table S2), effect of temperature and amount of catalyst on sulfur removal of DBT (Figure S5), GC-FID analysis (Figure S6), effect of temperature and amount of H<sub>2</sub>O<sub>2</sub> on sulfur removal of diesel fuel (Figure S7), comparison of catalytic oxidative desulfurization of real diesel and gasoline fuels by different immobilized catalytic systems (reported in literature) and the Al<sub>2</sub>O<sub>3</sub>-P<sub>2</sub>W<sub>15</sub>-C<sub>18</sub> from the present study (Table S3), and the image of solubility about DBT and DBTO<sub>2</sub> in octadecyltrichlorosilane (Figure S8) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.0c03673/suppl_file/ef0c03673_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
energy & fuels,engineering, chemical