Abstract:Porous carbon nitride (CN) spheres with partially crystalline frameworks have been successfully synthesized via a nanocasting approach by using spherical mesoporous cellular silica foams (MCFs) as a hard template, and ethylenediamine and carbon tetrachloride as precursors. The resulting spherical CN materials have uniform diameters of ca. 4 μm, hierarchical three-dimensional (3-D) mesostructures with small and large mesopores with pore diameters centered at ca. 4.0 and 43 nm, respectively, a relatively high BET surface area of ∼550 m2/g, and a pore volume of 0.90 cm3/g. High-resolution transmission electron microscope (HRTEM) images, wide-angle X-ray diffraction (XRD) patterns, and Raman spectra demonstrate that the porous CN material has a partly graphitized structure. In addition, elemental analyses, X-ray photoelectron spectra (XPS), Fourier transform infrared spectra (FT-IR), and CO2 temperature-programmed desorption (CO2-TPD) show that the material has a high nitrogen content (17.8 wt%) with nitrogen-containing groups and abundant basic sites. The hierarchical porous CN spheres have excellent CO2 capture properties with a capacity of 2.90 mmol/g at 25 °C and 0.97 mmol/g at 75 °C, superior to those of the pure carbon materials with analogous mesostructures. This can be mainly attributed to the abundant nitrogen-containing basic groups, hierarchical mesostructure, relatively high BET surface area and stable framework. Furthermore, the presence of a large number of micropores and small mesopores also enhance the CO2 capture performance, owing to the capillary condensation effect.

Synthesis of N-doped hierarchical carbon spheres for CO2 capture and supercapacitors

Nitrogen enriched porous carbon spheres: attractive materials for supercapacitor electrodes and CO2 adsorption

A general strategy to synthesize high-level N-doped porous carbons via Schiff-base chemistry for supercapacitors

Fabricating Self-Templated and N-doped Hierarchical Porous Carbon Spheres Via Microfluidic Strategy for Enhanced CO2 Capture

Core–shell N-doped Carbon Spheres for High-Performance Supercapacitors

N, S Co-doped hierarchical porous carbon rods derived from protic salt: Facile synthesis for high energy density supercapacitors

Nitrogen-doped hierarchically porous carbon spheres for low concentration CO2 capture

Controllable synthesis of N-doped hollow-structured mesoporous carbon spheres by an amine-induced Stöber-silica/carbon assembly process

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Core-Shell Nitrogen-Doped Carbon Hollow Spheres/Co 3 O 4 Nanosheets as Advanced Electrode for High-Performance Supercapacitor.

Ultrahigh Surface Area N-Doped Hierarchically Porous Carbon for Enhanced CO2 Capture and Electrochemical Energy Storage

Sustainable Nitrogen-Containing Hierarchical Porous Carbon Spheres Derived from Sodium Lignosulfonate for High-Performance Supercapacitors

Facile synthesis of porous carbon nitride spheres with hierarchical three-dimensional mesostructures for CO 2 capture

A Facile Route for Nitrogen-Doped Hollow Graphitic Carbon Spheres with Superior Performance in Supercapacitors

Synthesis of nitrogen-doped hollow carbon nanospheres for CO2 capture.

Synthesis of Nitrogen-Doped Carbon Spheres Using the Modified Stöber Method for Supercapacitors

Soft-template Assisted Hydrothermal Synthesis of Size-Tunable, N-doped Porous Carbon Spheres for Supercapacitor Electrodes

Synthesis and electrochemical performance of cobalt oxide/nitrogen-doped mesoporous composite carbon sphere

Highly Active N,S Co-Doped Hierarchical Porous Carbon Nanospheres from Green and Template-Free Method for Super Capacitors and Oxygen Reduction Reaction

N-Doped Yolk–Shell Carbon Nanospheres with “Carbon Bridges” for Supercapacitors

Template-free and large-scale synthesis of hierarchical dandelion-like NiCo 2 O 4 microspheres for high-performance supercapacitors