Abstract:In reinforced concrete structures, corrosion of the rebar produces 2–6 times more corrosion product than the original material, creating pressure on the surrounding concrete, leading to cracking. The study of corrosion and cracking in reinforced concrete structures is therefore of great importance for enhancing the durability of concrete. Unlike many previous studies, we used ribbed rebar similar to that used commercially and considered the mechanical behavior of the interface transition zone (ITZ) between the aggregate and mortar to simulate the processes of corrosion and cracking of reinforced concrete structures. We explored the failure mode of the interface layer under uniform corrosion and the influence of different factors on the corrosion expansion cracking and the shedding mode of a concrete cover. This was achieved by establishing a three-phase meso-scale model of concrete based on secondary development of ABAQUS, simulating the mechanical behavior of the ITZ using a cohesive element, and establishing a rust expansion cracking model for single and multiple rebars. The results showed that: (1) Under uniform rust expansion, concrete cracks are distributed in a cross pattern with a slightly shorter lower limb. (2) When the corrosion rate is low, the ITZ is not damaged. With an increase in the corrosion rate, the proportion of elements with tensile damage in the ITZ first increases and then decreases. (3) In the case of a single rebar, the larger the cover thickness, the higher the corrosion rate corresponding to ITZ failure, and the arrangement of the rebar has little influence on the ITZ failure mode. (4) In the case of multiple rebars, the concrete cover cracks when the rebar spacing is small, and wedge-shaped spalling occurs when the spacing is large.

Meso-scale Numerical Investigation on the Crack Process of Concrete Cover Induced by Rebar Non-Uniform Corrosion

State-of-art of corrosion-induced cracking of reinforced concrete structures

Meso-scale Numerical Investigation on Cracking of Cover Concrete Induced by Corrosion of Reinforcing Steel

Meso-scale numerical study on the non-uniform corrosion-induced cracking of confined concrete

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Investigation on Crack Propagation of Concrete Cover Induced by Non-Uniform Corrosion of Multiple Rebars

Finite Element Modeling of Concrete Cover Crack Propagation Due to Non-Uniform Corrosion of Reinforcement

Cracking of Cover Concrete Due to Non-Uniform Corrosion of Corner Rebar: A 3D Meso-Scale Study

Meso-scale corrosion expansion cracking of ribbed reinforced concrete based on a 3D random aggregate model

Analysis on the Cracking of Concrete Cover Due to Rebar Corrosion

Meso-scale finite element simulation of corrosion-induced cracking in reinforced concrete cover

Modeling the cracking of cover concrete due to non-uniform corrosion of reinforcement

Mesoscopic Simulation of Steel Rebar Corrosion Process in Concrete and Its Damage to Concrete Cover

Numerical-based method for calculating reinforcement corrosion at concrete cover cracking due to corrosion

Investigation on the cracking behavior of concrete cover induced by corner located rebar corrosion

Simulation and Experimental Verification of the Non-Uniform Corrosion Cracking Process of Reinforced Mortar Specimen

Mechanical properties and numerical simulation of crack interface in reinforced concrete

Investigating Non-Uniform Corrosion Induced Concrete Cover Cracking with a Fracture-Contact Coupled Computational Method

Experimental Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load