Abstract:The surfactant-free emulsion polymerization (SFEP) of styrene and methyl methacrylate carried out in the aqueous solution of poly (ethylene glycol) (PEG) was studied. With high power optical microscope, Coulter counter and transmission electron microscopy,particle size, particle size distribution and zeta potential were measured in the process of polymerization. It is interesting to observe that the polymer particle size experiences a process from small to large, which can be more than 1000 mu m, and then from large to small, which is back to a range of 0. 04 0 similar to 0. 18 mu m. When the particle size returns to nanometer scale, the system has an obvious temperature rising. This phenomenon is different from the traditional nucleation mechanism of SFEP. The particle, which is formed by the homogeneous nucleation or oligomer micelle nucleation mechanism that is popularly received as traditional nucleation mechanism of SFEP, usually has a trend to become bigger and bigger to the end in the process of SFEP. It is obviously found that the freshly formed particles are first coalesced to form a particle pile, which is bigger than 1000 mu m and even seen with eyes, and then corrupted into tinny ones, which are smaller than 0. 04 mu m and even beyond the ability of high power optical microscope. With transmission electron microscopy (TEM), it was clearly proven the existence of paricle pile which was composed of a lot of little particles ranging from 40 nm to 80 nm. And by use of Coulter zeta potential measurement, it was found that the zeta potential of particles had a trend from low to high level, and experenced abruptly increase in zeta potential at 60 min which was just the time that the little particle seperated from the paricle pile. This phenomenan was very different from the system that SEEP was carryed out in water without PEG, in which the zeta potential of particle was keeping about -50 mV and just changed a little after 50 min. It was reasonble to think that the potential increase was the driving force to make the little particles to escape from the particle pile. Therefore, the mechanism of coalescence-separate nucleation is proposed.

Regulating the size and molecular weight of polymeric particles by 1,1-diphenylethene controlled soap-free emulsion polymerization

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

Size Control of Polymeric Particle in Soap-Free Emulsion Polymerization

Preparation of monodisperse polystyrene microspheres with different functional groups using soap-free emulsion polymerization

Control of Diffusion/Barrier Effects of Polymer-Coated Particles and the Strengthening of Ethylene Polymerization Reactor

PARTICAL SIZE EVOLUTION IN SURFACTANT-FREE EMULSION COPOLYMERIZATION OF STYRENE AND METHYL METHACRYLATE IN AQUEOUS SOLUTION OF POLY ( ETHYLENE GLYCOL)

Alkyne-rich patchy polymer colloids prepared by surfactant-free emulsion polymerization

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Synthesis of micron-sized polymeric particles in soap-free emulsion polymerization using oil-soluble initiators and electrolytes

Styrene mini-emulsion polymerization co-stabilized by predissolved fluoropolymer

Characterization and Particle Size Control of Acrylic Polymer Latex Prepared with Green Surfactants

Affecting the size of polystyrene nanoparticles by adding monomer in two stages

Study on Soap-free P（MMA-EA-AA/MAA） Latex Particles with Narrow Size Distribution

Mini-emulsion formation and polymerization of styrene

Effects of Poly(ethylene Glycol) Molecular Weight on the Stability of Surfactant-Free Emulsion Polymerization System Consisting of Styrene and Methyl Methacrylate

Study of the Amount of Surfactant in the Core-Shell Emulsion Polymerization

Mechanism and Process of the Redispersion of the Aggregated Nano-Sio2 Particles During Emulsion Polymerization of Styrene

STUDY ON THE FORMATION MECHANISM OF MONODISPERSE PARTICLES IN THE EMULSIFIER-FREE EMULSION POLYMERIZATION OF METHYL METHACRYLATE AND BUTYL ACRYLATE

Model System for Surfactant-Free Emulsion Copolymerization of Hydrophobic and Hydrophilic Monomers in Aqueous Solution

Preparation and Characterization of Affinity Polymer Basic Microspheres by Soap-Free Emulsion Polymerization