Effect of Na Doping on the Photocatalytic Hydrogen Production of Ferroelectric K1-xNaxNbO3 Nanofibers
Tianjin Zhang,Shuya Huang,Dezhi Wang,Yuchen Lan,Xiao Liu,Fei Liu,Changlai Yuan
DOI: https://doi.org/10.1021/acs.jpcc.1c10127
2022-01-01
Abstract:Perovskite ferroelectric K1-xNaxNbO3 (x = 0, 0.05, 0.1, 0.3, 0.5, 0.7, and 1) nanofibers were prepared by electro-spinning. The effects of Na doping on the photocatalytic hydrogen production of K1-xNaxNbO3 were studied. The results revealed that the best hydrogen production rates were at x = 0.5, which were 230.12 and 0.66 mu mol.h(-1) under simulated sunlight and visible light irradiation, respectively. Conversely, the corresponding hydrogen production rates of pure KNbO3 were 155.90 and 0 mu mol.h(-1), respectively. Through an analysis of Mott-Schottky plots, ultraviolet-visible spectra, and X-ray diffraction Rietveld refinement, the negative shift of the conduction band edge and the distortion of the NbO6 octahedron may be the main reasons for the enhanced photocatalytic activity under simulated sunlight irradiation; the visible light response may be related to the shrinkage distortion of the NbO6 octahedron. Moreover, the rate at which K0.5Na0.5NbO3 nanofibers polarized under visible light irradiation was four times that without polarization, suggesting that the photogenerated carriers can be separated further by the internal depolarization field.