Novel quaternary ammonium functional addition-type norbornene copolymer as hydroxide-conductive and durable anion exchange membrane for direct methanol fuel cells

xiaohui he,jingyin liu,hongyu zhu,yan zheng,defu chen
DOI: https://doi.org/10.1039/c5ra09393g
IF: 4.036
2015-01-01
RSC Advances
Abstract:Novel quaternary ammonium functional addition-type norbornene copolymers (Q(Cn)P(BN/PhBN), n = 1, 6, 10, 12) with different alkyl side chain length comb-shaped structures or different contents of 2-(4-phenyl-butoxymethy-lene)-5-norbornene (PhBN) (22-77%) are synthesized via copolymerization of functionalized norbornenes, and their corresponding hydroxide-conductive anion exchange membranes (AEMs) with effective hydrophilic-hydrophobic separation are prepared and confirmed by TEM or SEM. The achieved AEMs show high ion exchange capacity (1.83 mmol g(-1)), as well as low methanol permeability (1.97-20.4 x 10(-7) cm(2) s(-1)), which are lower than that of Nafion (R). The ionic conductivity increases with the operation temperature increasing and is observed up to 4.14 x 10(-3) S cm(-1). The AEMs exhibit excellent dimensional stability with a swelling degree in plane between 0.9-3.3% and good chemical stability under 6 M NaOH solution even after a month. Membrane electrode assembly (MEA) is fabricated by using the alkalized Q(C12)P(BN/PhBN)-77 as the AEM and tested in an alkaline direct methanol fuel cell. The open circuit voltage (OVC) of 0.54 V and the maximum current density of 66 mW cm(-2) are achieved at 80 degrees C, respectively.
What problem does this paper attempt to address?