Abstract:Background Nickel-titanium (NiTi) archwires are considered the most attractive wires during the first stage of orthodontic treatment because of their unique properties throughout several generations. This study aimed to evaluate three different NiTi wires in terms of their elemental composition, transformation behavior, crystalline structure, and mechanical properties. Materials and methods The study used three different groups of NiTi archwires with dimensions of 0.016 x 0.022-inch (American Orthodontics®, Sheboygan, WI, USA). The first group included six superelastic NiTi archwires (NT3-SE®), with normal force and a stable structure that was not affected by temperature changes. The second group included six heat-activated NiTi archwires activated at 25°C (Thermal Ti-D®), with moderate force and a sensitive structure to thermal changes, especially at room temperature. The third group included six heat-activated NiTi archwires activated at 35°C (Thermal Ti-Lite®), with light force and a sensitive structure to thermal changes, especially at body temperature. X-ray fluorescence (XRF) was performed to determine wire element composition, whereas differential scanning calorimetry (DSC) was performed to determine the austenite finish temperature (Af). The X-ray diffraction (XRD) analysis was used to identify the crystalline structure at room temperature, and a three-point bending test was carried out under constant temperature (37°C) with respect to the instructions of ISO15841/DIS to evaluate the mechanical properties of these wires. Results The XRF analysis revealed that the superelastic NiTi archwires (NT3-SE) were composed of NiTi and chrome, whereas the heat-activated wires (Thermal Ti-D and Thermal Ti-Lite) were composed of NiTi and copper. The DSC showed the Af was at +16.84°C for the superelastic type (NT3-SE), +23°C for the heat-activated at 25°C (Thermal Ti-D), and +33.99°C for the heat-activated at 35°C (Thermal Ti-Lite). The XRD analysis identified the crystalline structure at room temperature for the superelastic type (NT3-SE) as austenite, while for thermal types (Thermal Ti-D and Thermal Ti-Lite) were a compound structure of austenite and martensite phase. Finally, the bending test showed that the highest forces were delivered from the superelastic type (NT3-SE), followed by heat-activated at 25°C (Thermal Ti-D), while the lowest forces were delivered from heat-activated at 35°C (Thermal Ti-Lite). There was no significant difference between the superelastic type (NT3-SE) and thermally activated type at 25°C (Thermal Ti-D), while there was a significant difference between the two previous types and the thermally activated type at 35°C (Thermal Ti-Lite) for all studied unloading points. Conclusions The thermal types of archwires (Thermal Ti-D and Thermal Ti-Lite) had lower unloading values in comparison with the superelastic type (NT3-SE). The elemental composition was different between the superelastic wires and the thermal ones. The superelastic wires were also different from the other two types in terms of crystalline structure. The three types of archwires had an activation degree located in the range of oral cavity variations.

Dental Arch Wires with Tooth-Like Color

Anodization of the dental arch wires

Surface Characterization of Anodized Dental Archwires and Miniscrews

Colorful Dental Archwires

Influence of Fluoride-Containing Acidic Artificial Saliva on the Mechanical Properties of Nickel-Titanium Orthodontics Wires.

Change of corrosion Oil nickel-titanium arch wires in oral environment

[Comparison of Mechanical Properties on Different Phase Transformation Points of Nickel-Titanium Orthodontic Wires].

Color Schemes And Biocompatibility Of Epoxy Resin/Polytetrafluorethylene Coat On The Surface Of Tini Arth Wires

Evaluating the Elemental Composition, Transformation Behavior, Crystalline Structure, and Mechanical Properties of Three 0.016-Inch by 0.022-Inch Nickel-Titanium Archwires: An In Vitro Study

Color stability and fluorescence of different orthodontic esthetic archwires

Bioinspired Superhydrophobic Ni–Ti Archwires with Resistance to Bacterial Adhesion and Nickel Ion Release

Effect of Anodization on Friction Behavior of Β‑titanium Orthodontic Archwires.

Superhydrophobic Archwires: Bioinspired Superhydrophobic Ni–Ti Archwires with Resistance to Bacterial Adhesion and Nickel Ion Release (Adv. Mater. Interfaces 7/2019)

A Comparative Evaluation of Surface Hardness and Nanomechanical Properties of Nickel-Titanium Orthodontic Wires: An In Vitro Study

Improvement of mechanical and biological properties of TiNi alloys by addition of Cu and Co to orthodontic archwires

Evaluation of surface roughness, cytotoxicity, and antibacterial effects of silver nanoparticle coating on copper nickel titanium orthodontic arch wires - in vitro study

New Bactericide Orthodonthic Archwire: NiTi with Silver Nanoparticles

[Differential Scanning Calorimetry Analyses of Phase Transformations in Different Nickel-Titanium Orthodontic Wires].

Microstructure of Surface and Subsurface Layers of a Ni-Ti Shape Memory Microwire.

Bio-inspired nanocomposite coatings on orthodontic archwires with corrosion resistant and antibacterial properties

The Effect of Cu-doping on the Corrosion Behavior of NiTi Alloy Arch Wires under Simulated Clinical Conditions