Abstract:Black glaze and brown glaze porcelains were an important part of ancient Chinese iron-based high temperature glazes. The excavation of black glaze and brown glaze porcelains from the Yuan and Ming dynasties at the Qingliang Temple kiln site in Baofeng, Henan, China, in 2014, enriched the firing history of this kiln site and history of Chinese ceramics. In this study, black glaze and brown glaze porcelain samples from the Qingliang Temple kiln site from the Yuan and Ming dynasties were selected and analysed via optical microscopy, laser Raman spectroscopy, focused ion beam scanning electron microscopy combined with EDS and energy dispersive X-ray fluorescence to determine their microscopic morphology, microzone composition, microstructure and chemical composition. Moreover, the main wavelength range of the brown glaze porcelain samples were measured by UV–Vis–NIR spectrophotometer systems. The main conclusions of this study are as follows. The brown glaze porcelain from the Yuan and Ming dynasties at the Qingliang Temple kiln site has two different colour layers, with the surface is brown and the bottom is black. The presence of a glass phase and α-Fe2O3 phase in the black glaze porcelain samples, and a rare ε-Fe2O3 phase in the brown glaze porcelain samples. The brown colour was a result of ε-Fe2O3 precipitation, whilst the black base layer also enhanced the brown-colouring effect. Different glaze formulations were used for brown glazed porcelain, some of which were similar to those used for black glaze porcelain and derived from the transformation of black glaze porcelain through different firing atmospheres and cooling rates. Although the formula of the brown glaze porcelain samples exhibited differences, the main wavelength difference was not large, was within the 645–682 nm range and belonged to the visible red region.

Study on Ru: porcelain of Song Dynasty [Original title and text in Chinese]

Study on the coloring mechanism of the Ru celadon glaze in the Northern Song Dynasty

Comparative study on the Ru ware, Ru-type ware of Qingliangsi kiln and celadon of Zhanggongxiang kiln

PIXE Analysis of Ancient Chinese Qing Dynasty Porcelain

Some New Results of PIXE Study on Chinese Ancient Porcelain

A Preliminary Study on Fe Valence of Porcelain Glaze by XAFS

Maximization of the Blue-White Contrast of Ancient Porcelain Decorations from Jingdezhen Imperial Kiln by Co-spinel Formation

PIXE and FCA study on the provenance of proto-porcelain of Xia and Shang Dynasty unearthed from Erlitou and Yinxu sites, China

Chemical and Microstructural Comparison of the Export Porcelain from Five Different Kilns Excavated from Nanhai I Shipwreck

Discussion on Main Features of Official Kiln of Song Dynasty-Concurrently about the Blue Porcelain of Yuan Dynasty in Ruzhou Area

A STUDY OF ANCIENT CHINESE PORCELAIN WARES OF THE SONG‐YUAN DYNASTIES FROM CIZHOU AND DING KILNS WITH ENERGY DISPERSIVE X‐RAY FLUORESCENCE*

Research on the White Pottery, Stamped Hard Pottery, and Pro To-Porcelains Unearthed at Erlitou

EDXRF Analysis of Provenience Characteristics of Proto-Porcelains from Typical Kiln Sites in Southern China

Chemical Analysis of White Porcelains from the Ding Kiln Site, Hebei Province, China

A Study of the Component Elements and Distinctive Features of Porcelain in the Three Gorges Area

Compositional Analysis below the Production Region Level: A Case Study of Porcelain Production at Dehua, Fujian, China

Research on bluish‐white porcelain glazes of Fanchang kiln in China

Study on the developmental history of jun kiln

Comparative microstructural study of celadon excavated from Housi’ ao kiln site in China (Late Tang and Five Dynasties): Mi-se porcelain and ordinary Yue celadon

NON‐DESTRUCTIVE ANALYSIS OF ‘ORIGINAL’ SONG DYNASTY GUAN WARES AND LATER IMITATIONS FROM THE PALACE MUSEUM COLLECTIONS, BEIJING

Firing process and colouring mechanism of black glaze and brown glaze porcelains from the Yuan and Ming dynasties from the Qingliang Temple kiln in Baofeng, Henan, China