Surfactant-free Hydrothermal Synthesis of Cu2ZnSnS4 (CZTS) Nanocrystals with Photocatalytic Properties

Jing Wang,Peng Zhang,Xuefeng Song,Lian Gao

DOI: https://doi.org/10.1039/c4ra03444a

IF: 4.036

2014-01-01

RSC Advances

Abstract:CZTS nanocrystals possessing an average size of 12 nm have been prepared using a surfactant-free hydrothermal method and their photocatalytic properties tested both in thin films and in slurry systems.

What problem does this paper attempt to address?

Facile synthesis of ultrafine Cu2ZnSnS4 nanocrystals by hydrothermal method for use in solar cells

Wenchao Liu,Binglei Guo,Cheeleung Mak,Aidong Li,Xiaoshan Wu,Fengming Zhang

DOI: https://doi.org/10.1016/j.tsf.2012.11.073

IF: 2.1

2013-01-01

Thin Solid Films

Abstract:We introduce a hydrothermal method for synthesizing ultrafine earth abundant Cu2ZnSnS4 (CZTS) nanocrystals with an average size of 5–6nm using simple Cu(II), Zn(II), Sn(II) inorganic salt and thiourea as precursor. X-ray diffraction, Raman spectrum and transmission electron microscopy studies indicate that CZTS nanocrystals with pure kesterite structure have been synthesized at temperature as low as 180°C. The band-gap energy determined from the absorbance spectrum is 1.47eV, suggesting that as-synthesized CZTS nanocrystals are very suitable for photovoltaic applications.
Surfactant-Tuned Phase Structure and Morphologies of Cu 2 ZnSnS 4 Hierarchical Microstructures and Their Visible-Light Photocatalytic Activities

Yaxin Guo,Jie Wei,Yalong Liu,Tiantian Yang,Zhuo Xu

DOI: https://doi.org/10.1186/s11671-017-1868-4

2017-01-01

Nanoscale Research Letters

Abstract:Cu 2 ZnSnS 4 (CZTS) hierarchical microstructures were synthesized by using a facile and nontoxic hydrothermal route, which were characterized by X-ray powder diffraction (XRD), scanning electron microscope (SEM), Raman spectra, and UV–Vis absorption spectra. The results and analysis show that surfactants used in the hydrothermal process have significant effect on the phase structures, morphologies, and photocatalytic activities of CZTS powders. Especially, the well-crystallized and pure kesterite CZTS hierarchical microstructures were synthesized with the addition of high-concentration tartaric acid (TA) in the hydrothermal process. A nucleation–dissolution–recrystallization mechanism was discussed, and the photocatalytic activities of CZTS hierarchical microstructures for the degradation of rhodamine B (RhB) were also evaluated. We argue that the crystalline structure and particle morphology have played key roles on the photocatalytic properties of CZTS crystals. A considerably high photocatalytic efficiency of 51.66% after 4 h irradiation was obtained in pure kesterite CZTS hierarchical microstructures, which suggests that CZTS would be a promising candidate of photocatalyst.
Surfactant-Tuned Phase Structure and Morphologies of Cu2ZnSnS4 Hierarchical Microstructures and Their Visible-Light Photocatalytic Activities

Yaxin Guo,Jie Wei,Yalong Liu,Tiantian Yang,Zhuo Xu

DOI: https://doi.org/10.1186/s11671-017-1868-4

Nanoscale Res Lett

Abstract:Cu2ZnSnS4 (CZTS) hierarchical microstructures were synthesized by using a facile and nontoxic hydrothermal route, which were characterized by X-ray powder diffraction (XRD), scanning electron microscope (SEM), Raman spectra, and UV-Vis absorption spectra. The results and analysis show that surfactants used in the hydrothermal process have significant effect on the phase structures, morphologies, and photocatalytic activities of CZTS powders. Especially, the well-crystallized and pure kesterite CZTS hierarchical microstructures were synthesized with the addition of high-concentration tartaric acid (TA) in the hydrothermal process. A nucleation-dissolution-recrystallization mechanism was discussed, and the photocatalytic activities of CZTS hierarchical microstructures for the degradation of rhodamine B (RhB) were also evaluated. We argue that the crystalline structure and particle morphology have played key roles on the photocatalytic properties of CZTS crystals. A considerably high photocatalytic efficiency of 51.66% after 4 h irradiation was obtained in pure kesterite CZTS hierarchical microstructures, which suggests that CZTS would be a promising candidate of photocatalyst.
Colloidal Cu2ZnSnS4 nanocrystals generated by a facile route using ethylxanthate molecular precursors

yufeng liu,meiying ge,yang yue,yan sun,yizheng wu,xin chen,ning dai

DOI: https://doi.org/10.1002/pssr.201004528

2011-01-01

Abstract:We have demonstrated a flexible method for preparing Cu2ZnSnS4 (CZTS) nanocrystals by use of zinc ethylxanthate (Zn(ex)(2)) and copper ethylxanthate (Cu(ex)(2)). TEM, SEM, XRD, UV-vis, EDS, XPS and TG-DTA indicate that the CZTS nanocrystals have been successfully synthesized. As air-stable molecular precursors, Zn(ex)(2) and Cu(ex)(2) can optimize the synthesis of quaternary CZTS nanocrystals because Cu(ex)(2) and Zn(ex)(2) facilitate the formation of homogeneous precursor solutions including all precursors and then for the flexible production of CZTS nanocrystals in homogeneous reaction solutions. (C) 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Facile hydrothermal synthesis of hydrotropic Cu2ZnSnS 4 nanocrystal quantum dots: Band-gap engineering and phonon confinement effect

Wenchao Liu,Binglei Guo,Xiaoshan Wu,F. M. Zhang,C. L. Mak,K. H. Wong

DOI: https://doi.org/10.1039/c3ta00357d

IF: 11.9

2013-01-01

Journal of Materials Chemistry A

Abstract:We developed a facile hydrothermal method for synthesizing ultrafine size-controllable earth-abundant Cu2ZnSnS4 (CZTS) nanocrystals using simple Cu(II), Zn(II) and Sn(II) inorganic salts and thiourea in a mixed ethylenediamine and di-water solution as precursors. X-ray diffraction, Raman scattering and transmission electron microscopy confirm that pure kesterite structure CZTS nanocrystals have been synthesized at temperatures as low as 180 degrees C. Broadening of Raman peaks and blue-shift of the absorption edge is attributed to quantum confinement within the nanocrystals. The hydrophilism and tunable band-gap of the CZTS nanocrystals show the potential applications of the nanocrystals for biological labelling and quantum dot based solar cells.
Surfactant-Free Synthesis of Single-Crystalline Bi4Ti3O12 Nanosheets with Excellent Visible-Light Photocatalytic Activity

Wan Jiang,Tongzhou Chen,Xin Yang,Luoyuan Ruan,Yong Liu,Xianqian Meng,Gang Xu,Gaorong Han

DOI: https://doi.org/10.1007/s10563-019-09279-z

2019-01-01

Catalysis Surveys from Asia

Abstract:Single-crystalline Bi4Ti3O12 nanosheets with a thickness less than 10 nm and a lateral size larger than 20 μm have successfully synthesized via a surfactant-free hydrothermal route by employing K2Ti6O13 nanofibers prepared in advance as titanium sources. The as-prepared samples were characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy (TEM), high-resolution TEM, and selected area electron diffraction, respectively. The results revealed that the single-crystalline Bi4Ti3O12 nanosheets are dominated with (010) facets. In general, the slow exfoliation of TiO6 octahedron lamella and the fast combination of the subnitrate radicals with the Bi3+ ions situated in (010) planes induce the crystallization of the single-crystalline Bi4Ti3O12 nanosheets. In addition, the as-prepared single-crystalline Bi4Ti3O12 nanosheets propose a narrowed gap of ca. 2.41 eV and after modified by Pt-quantum-dots exhibit excellent visible-light photocatalytic activity. It is believed that the surfactant-free in the hydrothermal system induce more amount of surface state responsible for the narrowed gap and the excellent visible-light photocatalytic activity.
A Facile Arrested Precipitation Method for Synthesis of Pure Wurtzite Cu2ZnSnS4 Nanocrystals Using Thiourea As a Sulfur Source

Chunya Li,Enna Ha,Wing-Leung Wong,Cuiling Li,Kam-Piu Ho,Kwok-Yin Wong

DOI: https://doi.org/10.1016/j.materresbull.2012.08.014

IF: 5.6

2012-01-01

Materials Research Bulletin

Abstract:A facile route for the synthesis of wurtzite Cu2ZnSnS4 (CZTS) nanocrystals was developed by an arrested precipitation method at 240°C under simple reaction conditions with diethanolamine as the solvent and thiourea as sulfur source. The structure and morphology of the CZTS nanocrystals were characterized by X-ray diffraction and transmission electron microscopy. Control experiments demonstrated that CZTS nanocrystals which are purely wurtzite structure are readily obtained. The average diameter of the bulk CZTS products is found to be 10±1.1nm. The estimated direct bandgap energy is 1.56eV, which indicates that the CZTS nanocrystals produced by this method possess promising applications in photovoltaic devices.
Cu2ZnSnS4 and Cu2ZnSn(S1−xSex)4 Nanocrystals: Room-Temperature Synthesis and Efficient Photoelectrochemical Water Splitting

Jun Xu,Zhengqiao Hu,Junjun Zhang,Wei Xiong,Lianling Sun,Lei Wan,Ru Zhou,Yang Jiang,Chun-Sing Lee

DOI: https://doi.org/10.1039/c7ta06628g

IF: 11.9

2017-01-01

Journal of Materials Chemistry A

Abstract:CZTS and CZTSSe nanocrystals have been synthesized by a simple metal complex solution mixing (Metcomix) process at room temperature and employed as efficient photoanodes for photoelectrochemical water splitting.
Phase-selective Hydrothermal Synthesis of Cu2ZnSnS4nanocrystals: the Effect of the Sulphur Precursor

Vincent Tiing Tiong,Yi Zhang,John Bell,Hongxia Wang

2014-01-01

Abstract:High quality Cu2ZnSnS4 (CZTS) films with uniform thickness and smooth surface were prepared using nanocrystals synthesized by a one-step hydrothermal method. It is found that the nature of the sulphur precursor used in the hydrothermal reaction influences both the compositional purity and the crystal structure of the synthesized hydrothermal product significantly. The CZTS material consisting of both wurtzite and kesterite crystal structures was obtained when using an organic sulfur precursor such as thioacetamide and thiourea in the precursor solution of the hydrothermal reaction while the pure kesterite phase CZTS nanocrystals were made when Na2S was employed as the sulphur precursor. CZTS thin films deposited on a Mo–soda lime glass substrate with uniform thickness (1.7 μm) were made by a simple doctor-blading method. The investigation of the effect of thermal treatment on the film has indicated that the wurtzite CZTS material was completely transformed to the kesterite phase when the material was annealed at 550 °C. Large grains (around 2 μm in size) were found on the surface of the CZTS film which was annealed at 600 °C. The evaluation of the photoresponse of the CZTS thin films has showed that a higher and very stable photocurrent was generated by the film annealed at 600 °C compared to the film annealed at 550 °C.
Solvothermal Synthesis of Cu2ZnSnS4 Nanocrystals by Using Metal Oxides

Xiaoli Peng,Wenbin Guo,Shu Zhang,Yong Xiang

DOI: https://doi.org/10.1109/isne.2014.6839335

2014-01-01

Abstract:In this study, Cu2ZnSnS4 (CZTS) has been fabricated via a low toxicity solvothermal process. Using Cu2O, ZnO, SnO, carbon disulfide and 1-butylamine as starting materials, single-phase CZTS nanoparticles are obtained through a solvothermal reaction at 200 °C for 24 h, and the Cu:Zn:Sn ratio in the as-synthesized CZTS was close to the expected stoichiometric ratio 2:1:1. We also investigated the structure and morphology properties of the as-synthesized CZTS nanoparticles through Xray diffraction and scanning electron microscope.
Synthesis of Surfactant-Free Self-Assembled and Size-Controlled Zns Mesoporous Nanospheres

Qian Zhang,Wenyang Chi,Weiwei Zhang,Chunyan Lv,Jixue Li

DOI: https://doi.org/10.1039/c1nj20727j

IF: 3.3

2012-01-01

New Journal of Chemistry

Abstract:High quality self-assembled ZnS mesoporous nanospheres have been successfully synthesized by a facile solvothermal method. The sample was synthesized using ethylene glycol aqueous solution without any surfactant assistance. Size and shape control of the ZnS mesoporous nanospheres is achieved by simple adjustments of the reactants' concentration. Investigation results show that ZnS spheres are made up of small ZnS nanocrystallites and show good photocatalytic activity in the degradation of MB under the irradiation of ultraviolet light because of their mesoporous structures.
Synthesis and Characterization of Cu 2 ZnSnS 4 from Cu 2 SnS 3 and ZnS Compounds

Shi-na Li,Rui-xin Ma,Dong-ran Li,Fan Yang,Xiao-yong Zhang,Xiang Li,Hong-min Zhu

DOI: https://doi.org/10.1007/s11801-015-5049-3

2015-01-01

Optoelectronics Letters

Abstract:The Cu 2 ZnSnS 4 (CZTS) powders are successfully synthesized by using ZnS and Cu 2 SnS 3 as raw materials directly without any intermediate phase at 450 °C for 3 h in Ar atmosphere. The crystalline structure, morphology and optical properties of the CZTS powders are characterized by X-ray diffraction (XRD), Raman spectrum, field emission scanning electron microscopy (FESEM) and ultraviolet-visible (UV-vis) spectrophotometer, respectively. The results show that the band gap of the obtained CZTS is 1.53 eV. The CZTS film is fabricated by spin coating a mixture of CZTS powders and novolac resin with a weight percentage of 30%. The photoelectrical properties of such CZTS films are measured, and the results show an incident light density of 100 mW·cm −2 with the bias voltage of 0.40 V, and the photocurrent density can approach 9.80×10 −5 A·cm 2 within 50 s, giving an on/off switching ratio of 1.64.
Cu2znsns4 Thin Films: Spin Coating Synthesis and Photoelectrochemistry

Jing Wang,Peng Zhang,Xuefeng Song,Lian Gao

DOI: https://doi.org/10.1039/c4ra01139b

IF: 4.036

2014-01-01

RSC Advances

Abstract:Cu2ZnSnS4 (CZTS) has attracted great interest in both photovoltaic and photoelectrochemical applications as a low cost and environmentally-friendly solar absorber material. The development of a facile and green chemical route for the preparation of a well crystallized and stable CZTS photoelectrode still remains a challenge. We present here the preparation of well crystallized CZTS thin films using a facile spin-coating method based on methanol solution and their applications as photoelectrocathodes for hydrogen production. The bare CZTS thin films demonstrate outstanding photoelectrochemical (PEC) efficiency and chemical stability, which are further improved by surface modification of CdS and TiO2 layers using chemical bath and atomic layer deposition, respectively. The incident-photon-to-current efficiency (IPCE) and long term photoelectrochemistry of the CZTS thin films are measured. The characterization of XRD, Raman, SEM, and UV-vis absorption is also performed.
Cu2ZnSnS4 Thin Film Fabricated by the Calcinated Nanocrystals

Jin Chen,Yu Sun,Jiaqi Ju,Fengchao Wang,Yan Jin,Canyun Zhang,Jinfang Kong,Xiaogai Peng,Chenfei Wang,Hengxing Dong,Qinmiao Chen,Xiaoming Dou

DOI: https://doi.org/10.1002/crat.202000081

2020-01-01

Crystal Research and Technology

Abstract:In the present work, Cu2ZnSnS4 (CZTS) thin film is successfully prepared by the calcinated nanocrystals with screen‐printing approach. The dependences of the obtained samples’ properties on the annealing parameters of temperature and time are well studied via X‐ray diffraction, Raman, field emission scanning electron microscopy, ultraviolet‐visible‐infrared (UV‐vis‐IR) spectroscopy, energy‐dispersive X‐ray spectroscopy, and X‐ray photoelectron spectroscopy treatments. The results suggested that the best performances of prepared sample can be obtained at 600 °C for 20 min. The obtained sample features a kesterite CZTS phase, a surface morphology consisting of microns nanoparticles, a Cu‐rich and Zn‐rich chemical composition, and an ideal band gap of 1.4 eV. Additionally, the impurity phase of copper sulfide resulting from Cu‐rich composition is needed to further improve in the next work.
Cu2znsns4 Thin Film Solar Cells from Coated Nanocrystals Ink

Ening Gu,Chang Yan,Fangyang Liu,Yike Liu,Zhenghua Su,Kun Zhang,Zhiwei Chen,Jie Li,Yexiang Liu

DOI: https://doi.org/10.1007/s10854-014-2632-5

2015-01-01

Journal of Materials Science Materials in Electronics

Abstract:Earth abundant Cu2ZnSnS4 (CZTS) has triggered great attention in the field of low cost thin film solar cells. High-quality CZTS nanocrystals were synthesized by a facile solution method, with an average particle diameter about 12 nm and a direct band gap of 1.49 eV. And these nanocrystals were readily dispersed to form a colloidal ink, which was then used to prepare thin films by doctor blading approach. Effects of sulfurization temperature on those films’ composition, morphology and phase were studied. The obtained thin film, annealed under flow S/Ar atmosphere at 550 °C for 30 min, shows a dense smooth surface, a slightly Cu-poor and Zn-rich composition and the kesterite CZTS structure. Besides, this 550 °C annealed CZTS film was then fabricated into full photovoltaic device and a power conversion efficiency of 2.29 % has been achieved. Directions for further improvements have also been discussed and proposed.
Nanoparticle Based Preparation Method of Cu_2ZnSn(SSe)_4 Thin Films

Wei Ming,Du Qingyang,Liu Weifeng,Jiang Guoshun,Zhu Changfei

DOI: https://doi.org/10.3969/j.issn.1671-4776.2012.04.003

2012-01-01

Abstract:Cu2ZnSnS4(CZTS) nanoparticles were synthesised with the hot-injection method.These nanocrystals were dispersed in the organic solvent to form the stable ink,which was fabricated into the CZTS precursor thin film with the instillation method.X-ray diffraction(XRD),Raman scattering,transmission electron microscopy(TEM) and UV-visible(UV-VIS) spectroscopy were used to characterize the structure,morphology and direct band gap of the CZTS nano-particles,respectively.Raman study shows that the as-synthesised CZTS is a pure phase,without any existence of ZnS and Cu2SnS3.Fourier transition infrared spectroscopy(FTIR) and UV-VIS spectra indicate that the oleylamine(OLA) is the surface capping agent of the CZTS nanoparticle,whose band gap is 1.52 eV.The CZTSSe thin film was obtained through the sul-furization under the atmosphere of H2S and solid selenization under Se vapor for the CZTS precursor thin film.The result shows that the sulfurization can get a flattening surface,but the nanopraticles do not grow into large grains;while the solid selenization can get well crystallized CZTSSe thin films.
Facile synthesis of Cu2ZnSnS4 nanocrystals and its use for dye-sensitized solar cells applications

Lixia Li,BinLei Zhang,Meng Cao,Yan Sun,Jiang Jiang,P. F. Hu,Yue Shen,Linjun Wang

DOI: https://doi.org/10.1016/j.jallcom.2012.10.068

IF: 6.2

2013-01-01

Journal of Alloys and Compounds

Abstract:Cu2ZnSnS4 (CZTS) nanocrystals were synthesized with a simple solution method. The effects of the amount of oleylamine, the quantity of zinc salt precursor and reaction time on the structure, composition, morphology and optical properties of the nanocrystals were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy dispersive X-ray analysis (EDX) measurements. The zinc content in the nanocrystals increases with the increasing of the amount of oleylamine and the quantity of ZnCl2 precursor. But the particle sizes were influenced mainly by the reaction time. For dye-sensitized solar cells (DSSCs) using CZTS nanocrystals as the dye layer, the JSC was greatly decreased with the increasing of the sizes of the nanocrystals. Synthesis of small and uniformly dispersed CZTS nanocrystals was beneficial to enhance the power conversion efficiency of the DSSCs. © 2012 Elsevier B.V. All rights reserved.
Phase-controlled synthesis of Cu2ZnSnS4 nanocrystals: the role of reactivity between Zn and S.

Yu Zou,Xiong Su,Jiang Jiang

DOI: https://doi.org/10.1021/ja405962k

IF: 15

2013-01-01

Journal of the American Chemical Society

Abstract:Cu2ZnSnS4 (CZTS) nanocrystals with different morphologies and phases have been synthesized in hot organic solvents such as dodecanethiol and oleylamine. The crystallographic phases could be controlled by the sulfur precursor and the ligand species of the metal salts used for the synthesis. When a highly reactive sulfur precursor and metal acetates were used, wurtzite CZTS nanocrystals were obtained. On the other hand, using a low-reactivity sulfur precursor or metal chlorides produced CZTS nanocrystals in a kesterite phase. The experimental results from systematic investigations that the reaction rate between Zn and S precursors played a determining role for the growth of CZTS nanocrystals with different crystalline phases. A relatively faster reaction between Zn and S precursors in comparison to the Sn-S reaction favored the formation of a metastable wurtzite phase, which could be accelerated by increasing the reactivity of the S precursor. This work provided a safe and economical way to synthesize high-quality phase-controlled Cu2ZnSnS4 nanocrystals, especially wurtzite nanorods, for potential photovoltaic applications. Moreover, preliminary results show that the proposed mechanism also applies to the phase-controlled synthesis of other quaternary Cu2MSnS4 (M = Cd2+, Mn2+) nanocrystals.
Colloidal Nanocrystals of Orthorhombic Cu2znges4: Phase-Controlled Synthesis, Formation Mechanism and Photocatalytic Behavior

Cong-Min Fan,Michelle D. Regulacio,Chen Ye,Suo Hon Lim,Shun Kuang Lua,Qing-Hua Xu,Zhili Dong,An-Wu Xu,Ming-Yong Han

DOI: https://doi.org/10.1039/c4nr07012g

IF: 6.7

2015-01-01

Nanoscale

Abstract:The orthorhombic polymorph of Cu2ZnGeS4 (CZGS) is a metastable wurtzite-derived phase that can only be prepared in the bulk form by extensive heating at high temperatures (≥790 °C) when using the conventional solid-state reaction route. By employing a facile solution-based synthetic strategy, we were able to obtain phase-pure orthorhombic CZGS in nanocrystalline form at a much lower reaction temperature. Prior to this work, the colloidal synthesis of single-phase orthorhombic CZGS on the nanoscale has never been reported. We find that the use of an appropriate combination of coordinating solvents and precursors is crucial to the sole formation of this metastable phase in solution. A possible formation mechanism is proposed on the basis of our experimental results. Because CZGS consists of environmentally benign metal components, it is regarded as a promising alternative material to the technologically useful yet toxic cadmium-containing semiconductors. The orthorhombic CZGS nanocrystals display strong photon absorption in the visible spectrum and are photocatalytically active in dye degradation under visible-light illumination.
Efficient Thermolysis Route To Monodisperse Cu2znsns4 Nanocrystals With Controlled Shape And Structure

Xiaoyan Zhang,Guobiao Guo,Cheng Ji,Kai Huang,Chenyang Zha,Yifeng Wang,Liming Shen,Arunava Gupta,Ningzhong Bao

DOI: https://doi.org/10.1038/srep05086

IF: 4.6

2014-01-01

Scientific Reports

Abstract:Monodisperse Cu2ZnSnS4 (CZTS) nanocrystals with tunable shape, crystalline phase, and composition are synthesized by efficient thermolysis of a single source precursor of mixed metal-oleate complexes in hot organic solvents with dissolved sulfur sources. Suitable tuning of the synthetic conditions and the Cu/(Zn + Sn) ratio of the precursor has enabled precise control of the crystalline phase in the form of kesterite, or a newly observed wurtzite structure. Nanocrystals with morphology in the form of spherical, rice-like, or rod-like shapes are obtained over a wide range of compositions (0.5 <= Cu/(Zn + Sn) <= 1.2). Both the final products and intermediates for each shape exhibit consistent composition and structure, indicating homogenous nucleation and growth of single-phase nanocrystals. Thin films prepared from colloidal nanocrystal suspensions display interesting shape-dependent photoresponse behavior under white light illumination from a solar simulator.

Surfactant-free Hydrothermal Synthesis of Cu2ZnSnS4 (CZTS) Nanocrystals with Photocatalytic Properties

Facile synthesis of ultrafine Cu2ZnSnS4 nanocrystals by hydrothermal method for use in solar cells

Surfactant-Tuned Phase Structure and Morphologies of Cu 2 ZnSnS 4 Hierarchical Microstructures and Their Visible-Light Photocatalytic Activities

Surfactant-Tuned Phase Structure and Morphologies of Cu2ZnSnS4 Hierarchical Microstructures and Their Visible-Light Photocatalytic Activities

Colloidal Cu2ZnSnS4 nanocrystals generated by a facile route using ethylxanthate molecular precursors

Facile hydrothermal synthesis of hydrotropic Cu2ZnSnS 4 nanocrystal quantum dots: Band-gap engineering and phonon confinement effect

Surfactant-Free Synthesis of Single-Crystalline Bi4Ti3O12 Nanosheets with Excellent Visible-Light Photocatalytic Activity

A Facile Arrested Precipitation Method for Synthesis of Pure Wurtzite Cu2ZnSnS4 Nanocrystals Using Thiourea As a Sulfur Source

Cu2ZnSnS4 and Cu2ZnSn(S1−xSex)4 Nanocrystals: Room-Temperature Synthesis and Efficient Photoelectrochemical Water Splitting

Phase-selective Hydrothermal Synthesis of Cu2ZnSnS4nanocrystals: the Effect of the Sulphur Precursor

Solvothermal Synthesis of Cu2ZnSnS4 Nanocrystals by Using Metal Oxides

Synthesis of Surfactant-Free Self-Assembled and Size-Controlled Zns Mesoporous Nanospheres

Synthesis and Characterization of Cu 2 ZnSnS 4 from Cu 2 SnS 3 and ZnS Compounds

Cu2znsns4 Thin Films: Spin Coating Synthesis and Photoelectrochemistry

Cu2ZnSnS4 Thin Film Fabricated by the Calcinated Nanocrystals

Cu2znsns4 Thin Film Solar Cells from Coated Nanocrystals Ink

Nanoparticle Based Preparation Method of Cu_2ZnSn(SSe)_4 Thin Films

Facile synthesis of Cu2ZnSnS4 nanocrystals and its use for dye-sensitized solar cells applications

Phase-controlled synthesis of Cu2ZnSnS4 nanocrystals: the role of reactivity between Zn and S.

Colloidal Nanocrystals of Orthorhombic Cu2znges4: Phase-Controlled Synthesis, Formation Mechanism and Photocatalytic Behavior

Efficient Thermolysis Route To Monodisperse Cu2znsns4 Nanocrystals With Controlled Shape And Structure