Abstract:The effects of Gd concentration(0.1, 0.3, 0.7 wt%) on the microstructure, texture and mechanical properties of rolled and annealed Mg-2Zn-xGd sheets have been investigated aiming to develop low cost and high ductile Mg-Zn-Gd sheets. Dynamic recrystallization, static recrystallization and grain growth during hot rolling process and annealing process were delayed with increase of Gd concentration, leading to fine grain microstructure. The rolled 0.1 wt% Gd sheet showed strong basal texture which remained stable after annealing process and exhibited medium elongation of about 25%. In contrast, the rolled 0.3 wt% Gd sheet had weak basal texture which transformed to non-basal texture with double peaks tilted about +/- 48 degrees to the transverse direction due to the static recrystallization during annealing process. Consequently, the annealed sheets exhibited higher elongation of 40% along the rolling direction and 50% along the transverse direction due to the existence of non-basal texture. It is suggested that the minimum effective concentration for texture randomization in the Mg-2Zn-xGd alloy is about 0.3 wt%. Copyright 2013, National Engineering Research Center for Magnesium Alloys of China, Chongqing University. Production and hosting by Elsevier B. V. Open access under CC BY-NC-ND license.

Effects of Trace Gd Concentration on Texture and Mechanical Properties of Hot-Rolled Mg–2Zn–xGd Sheets