Sonication-polished Anodic TiO 2 Nanotube Array-Based Photoanode for Efficient Solar Energy Conversion
Kai Gu,Peng Zhong,Mengqi Guo,Jie Ma,Qi Jiang,Shan Zhang,Xuejiao Zhou,Yong Xie,Xiaohua Ma,Yang Wang
DOI: https://doi.org/10.1007/s10008-016-3301-9
IF: 2.747
2016-01-01
Journal of Solid State Electrochemistry
Abstract:In this work, the capping layer atop anodic TiO2 nanotube arrays (NTAs), which hinders filling of other guest materials and transport of charge carriers, is discerned to be TiO2 nanotapes. Then, it is completely removed by a novel sonication-polishing (SP) treatment, after which Sb2S3 is subsequently introduced to fill the nanotubes by chemical bath deposition. The morphological, structural, and optical properties of the SP-treated TiO2 NTAs and TiO2 NTAs/Sb2S3 heterogeneous structures are characterized systematically. The results indicate that SP treatment opens the tops of nanotubes with diameters of ∼120 nm, which endure a phase conversion from amorphous to anatase after calcination at 450 °C; besides, stibnite Sb2S3 with a band gap of ∼1.75 eV inside the TiO2 networks is formed upon heat treatment at 330 °C in Ar, which enhances the absorption in visible light range. The photoelectrochemical (PEC) and photovoltaic properties for the SP-treated TiO2 NTAs are investigated. Results shows that the photoresponse of TiO2 NTAs is improved by the SP treatment, and the photocurrent for the TiO2 NTAs/Sb2S3 electrode is substantially enhanced as compared to the bare TiO2 one. A high efficiency of 6.28 % is achieved in a TiO2 NTAs/Sb2S3 PEC cell. In addition, charge recombination in the photoanode of dye-sensitized solar cells (DSSCs) is observed to be greatly retarded by using the SP-treated TiO2 NTAs as compared to TiO2 nanoparticles (NPs). Thus, the SP anodic TiO2 NTAs are promising in applications in various PEC areas such as photocatalysis and sensitized solar cells.