Synthesis And Optical Properties Of A Y-3(Al/Ga)(5)O-12:Ce3+,Cr3+,Nd(3+)Persistent Luminescence Nanophosphor: A Promising Near-Infrared-Ii Nanoprobe For Biological Applications
Luyan Wu,Jie Hu,Qilin Zou,Yaling Lin,Decai Huang,Dejian Chen,Hongyu Lu,Haomiao Zhu
DOI: https://doi.org/10.1039/d0nr03269g
IF: 6.7
2020-01-01
Nanoscale
Abstract:Persistent luminescence nanophosphors (PLNPs) emitting in the second near-infrared window (1000-1700 nm, NIR-II) are emerging as one promising class ofin vivobio-imaging agents due to their unique advantages including non-autofluorescence and low optical scattering in tissues. Currently, it remains a great challenge to synthesize nanosized lanthanide-doped inorganic NIR-II phosphors with a good persistent luminescence performance. Herein, we present a salt microemulsion method for synthesizing Ce3+, Cr3+, Nd(3+)codoped Y-3(Al/Ga)(5)O(12)nanocrystals, which generate multi-wavelength persistent luminescence in the visible (similar to 508 nm, 5d(1)-> 4f of Ce3+), the first near-infrared window (similar to 890 nm,F-4(3/2)->(4)I(9/2)of Nd3+) and NIR-II (similar to 1063 nm,F-4(3/2)->(4)I(11/2)of Nd3+) regions. Under illumination of a 410 nm diode (3 W) for 10 min, the observed duration time of NIR-II persistent luminescence is as long as 60 min at room temperature. Moreover, the persistent luminescence can be excited efficiently by multiple excitation sources including a blue diode, white LEDs and an X-ray generator, which is crucial for deep tissue imaging applications. By comparing the penetration depth between NIR-I and NIR-II persistent luminescence through chicken breast, we prove that NIR-II photons exhibit a deeper optical penetration length (3.9 mm) than that of the NIR-I ones (2.5 mm). In addition, the NIR signals can still be detected 3 min after ceasing the excitation source by a small animal imaging system (InGaAs detector) when the thickness of the covering chicken breast is 20 mm. These results show great promise for Y-3(Al/Ga)(5)O-12:Ce3+,Cr3+,Nd(3+)nanocrystals as a PLNP for bio-imaging applications with deep penetration depth and a high signal-to-noise ratio.