Crystal Structure Refinement, Photoluminescence Properties and Energy Transfer of Multicolor Tunable Ca2Al2SiO7:Tm3+, Dy3+ for NUV White-Light-emitting Diodes.
Haiyan Jiao,Guoheng Zhang,Peiyu Wang,Qiong Chen,Liwei Liu,Cairang Limao,Yuhua Wang
DOI: https://doi.org/10.1016/j.saa.2019.117942
2020-01-01
Abstract:A promising phosphors Ca2Al2SiO7:Tm3+,Dy3+ were synthesized by conventional high temperature sintering. Phase identification, crystal structure refinement, luminescence properties, energy transfer mechanism of Tm3+ -> Dy3+, and CIE color coordinates were investigated systematically. The phase structure of prepared phosphors were confirmed by XRD analysis and structure refinement. From the results of photoluminescence, the CASO: Tm3+ phosphors showed intense blue light emission peaks at 454 nm (the transition from D-1(2) to F-3(4)), while CASO:Dy3+ phosphors exhibited predominant yellow light emission peaks at 581 nm (the transition from F-4(9/2) to H-6(13/2)), implying that the Dy3+ were located in the non-inverted symmetric site of the CASO host lattice. Meanwhile, the results exhibited that the optimal doping content of Dy3+ was 0.01, and the mechanism of concentration quenching was the nearest-neighbor ions interaction. The overlapped emission (Tm3+)/excitation (Dy3+) spectra, decay curves and the energy level scheme about CASO:Tm3+,Dy3+ confirmed the energy transfer of Tm3+ -> Dy3+. Moreover, by adjusting Tm3+/Dy3+ ions concentration, the intensities of yellow emission for Dy3+ and blue emission for Tm3+ could be adjusted to tune the emitting color of CASO:Tm3+, Dy3+. Excited by the most effective excitation wavelength at 355 nm, the CIE coordinates (0.3422, 0.3262) of phosphor CASO:0.01Tm(3+), 0.01Dy(3+) was closest to the coordinates of white chromaticity (0.33, 0.33). Results indicate that the potential value of phosphors Ca2Al2SiO7:Tm3+,Dy3+ are used as a single-phase color-adjustable phosphors for NUV pumped white-LEDs. (C) 2019 Elsevier B.V. All rights reserved.