Effect of Rhbmp-2/Plla Composite Coating on Peri-Implant Bone Healing

DU Bing,ZHOU Lei,LI Junzheng
DOI: https://doi.org/10.3969/j.issn.1674-4659.2014.07.0832
2014-01-01
Abstract:Objective To observe the osteoinductivity of the recombinant human bone morphogenetic protein-2/polylactic acid (rhBMP-2/PLA) composite coating and its effect on peri-implant bone healing. Methods Pure titanium implants were manufactured by precision lathe cutting machine, and PLA coatings were prepared with emulsion solvent evaporation. rhBMP-2/PLA-coated implants were constructed by freeze-drying technique. Nine Japanese rabbits were involved in the study. Three implant holes were prepared in each femur, and rhBMP-2/PLA coated implants and pure titanium implants were implanted randomly. 4, 8, 12 weeks after implantation, animals were killed and all specimens were studied by X-ray, histological observation and immunohistochemical analysis of collagen typeⅴto compare the difference in the bone healing condition around implants between the two groups. Results X-ray tests indicated that in 4th, 8th, 12th week, peri-implant bone density continuously increased in two groups. In 4th and 8th week, the density in the rhBMP-2/PLA group was significantly higher than that in the pure titanium implant group (P<0.05). And in 12th week, the density in the rhBMP-2/PLA group was a little higher than that in the pure titanium implant group (P>0.05). Histological observations revealed woven bone formation and a layer of tightly packed osteoblasts in the interface between implant and bone in rhBMP-2/PLA group in 4th week, whereas only small amount of woven bone and proliferation of osteoblasts could be seen in the pure titanium group. In 8th weeks, the formation of woven bone and degree of calcification increased and lamellar bone appeared in the rhBMP-2/PLA group. And in the pure titanium group, there only existed focal woven bone and low degree of calcification. In 12th week, lamellar bone continued increasing and bone marrow cavity expanded and Haversian system were formed. In the pure titanium group, lamellar bone and trabecular structure also appeared. Conclusions rhBMP-2/PLA composite coating with good osteoinductivity can promote the early-staged peri-implant bone healing.
What problem does this paper attempt to address?