Field emission properties of tungsten oxide nanowires prepared on ITO coated glass

paibin xie,daokun chen,guofu zhang,zhipeng zhang,fei liu,juncong she,shaozhi deng,ningsheng xu,jun chen

DOI: https://doi.org/10.1109/IVNC.2015.7225562

2015-01-01

Abstract:Patterned tungsten oxide (WO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> ) nanowires are grown on ITO glass substrate by a thermal oxidation without any catalyst. Field emission measurements show that the field emission current of WO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> nanowires can be dramatically enhanced by a conditioning process. After conditioning, the turn-on voltage of the WO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> nanowires decreases from 6.50 MV/m to 3.28 MV/m. The phenomenon is related the oxygen adsorbate on the surface of WO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> nanowires.