Abstract:Colloidal N-doped TiO2 nanocrystals are successfully synthesized by low-temperature direct nitridization in triethylamine solution during hydrolysis of tetrabutyl titanate, followed by acidic peptization at 70 degrees C. Through adjusting the acid concentration and peptization time, the N-doped samples consisting of different proportions of anatase and rutile phases are obtained. Several characterization techniques including X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and UV-vis diffuse reflectance spectroscopy are employed to determine the crystal phase, morphology, degree of nitrogen incorporation and optical properties of the products. The high resolution XPS spectrum of the N 1s region confirms the substitutional nitrogen doping of lattice oxygen in TiO2 crystals. For comparison, it is found that most of the N species are chemisorbed on the surface of TiO2 particles if the N-source is introduced after crystallization. The light response in the range of 400-500 nm is obviously improved by N doping, which facilitates the absorption of photons to produce e(-) -h(+) pairs under visible irradiation. On the other hand, nitrogen doping also inhibits the recombination of the photoinduced carriers and therefore increases the quantum efficiency of the TiO2 photocatalyst. As a result, the as-synthesized N-doped TiO2 nanomaterials exhibit higher photocatalytic activity both in the UV-and visible-light region in contrast to the non-doped TiO2. The hybrid containing 63.1% anatase shows the highest photocatalytic activity, which is due to a synergistic effect between anatase and rutile.

An N-Doped Anatase/Rutile Tio2 Hybrid from Low-Temperature Direct Nitridization: Enhanced Photoactivity under Uv-/Visible-Light

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Facile Synthesis of Anatase–Rutile Diphase N-doped TiO2 Nanoparticles with Excellent Visible Light Photocatalytic Activity

Enhanced Photocatalytic Activity of Nitrogen Doped Tio2 Anatase Nano-Particle under Simulated Sunlight Irradiation

Synthesis and Characterization of Nitrogen-Doped TiO2 Nanophotocatalyst with High Visible Light Activity

Synthesis and characterization of visible light responsive N–TiO2 mixed crystal by a modified hydrothermal process

N-Doped Tio2: Preparation By Hydrothermal Reaction-Thermolysis Process And Photocatalytic Activity

Enhanced Photoelectric Property and Visible Activity of Nitrogen Doped TiO2 Synthesized from Different Nitrogen Dopants

Preparation of Visible-Light Active N-doped Nano-Tio2 Photocatalyst by Hydrothermal Method

Facile Synthesis of Nitrogen-Doped Titanium Dioxide with Enhanced Photocatalytic Properties

Effective photocatalytic properties of N doped Titanium dioxide nanotube arrays prepared by anodization

Characterization and Mechanism Analysis of N Doped TiO2 with Visible Light Response and Its Enhanced Visible Activity

Synthesis of N-Doped TiO2 with Good Photocatalytic Property

Origin Of Photocatalytic Activity Of Nitrogen-Doped Tio2 Nanobelts

Preparation, Characterization and Visible Light Photocatalytic Activity of Nitrogen-Doped Tio2

Preparation and Characterization of N–I Co-Doped Nanocrystal Anatase TiO2 with Enhanced Photocatalytic Activity under Visible-Light Irradiation

A simple method to prepare nitrogen-doped titania oxides with high photocatalytic activity under visible light

Low Temperature Hydrothermal Synthesis of N-doped TiO2 Photocatalyst with High Visible-Light Activity

Preparation of Highly Visible-Light Active N-doped TiO2 Photocatalyst

Photoinduced Charge Carrier Properties and Photocatalytic Activity of N-Doped TiO 2 Nanocatalysts

Synthesis of Efficient N-Containing Tio2 Photocatalysts with High Anatase Thermal Stability and the Effects of the Nitrogen Residue on the Photoinduced Charge Separation