Abstract:For CO2 methanation reaction, a Mg species is often utilized as the alkaline promotor for Ni based catalysts to enhance the low-temperature catalytic activity. Herein, based on a pioneer ordered mesoporous NiO-Al2O3 catalyst, a Mg alkaline promotor had been incorporated into the ordered mesoporous framework via a one-pot evaporation induced self-assembly (EISA) strategy. As a result, the ordered mesoporous NiO-MgO-Al2O3 composite oxides with Mg/Al molar ratios in a wide range (0-10%) were successfully fabricated and directly utilized as the catalysts for CO2 methanation reaction. These mesoporous catalysts were carefully characterized by X-ray diffraction, N-2 adsorption-desorption, transmission electron microscopy, selected area electron diffraction, energy dispersive spectrometer, X-ray photoelectron spectroscopy, H-2 temperature-programmed reduction, and CO2 temperature-programmed desorption measurements. It was found that the ordered mesoporous materials with large specific surface areas (180.8-232.8 m(2) g(-1)), big pore volumes (0.37-0.43 cm(3) g(-1)), and narrow pore size distributions (around 9.5 nm) could be successfully retained after the calcination at 700 degrees C. The highly dispersed Ni species were strongly interacted with the mesoporous framework in the form of NiAl2O4 spinel. The incorporation of the Mg progressively increased the surface basicity of these catalysts, which could intensify the chemisorption and activation of CO2 during the CO2 methanation reaction. Therefore, the low-temperature catalytic activity was significantly enhanced. The "volcano-shape curve" relationship between the Mg/Al molar ratio and catalytic activity had been interestingly observed, suggesting only appropriate surface basicity could obtain the optimum catalytic activity. Besides, there was no evident deactivation over these mesoporous catalysts after 50 h long-term stability tests due to the confinement effect of the mesoporous framework. Therefore, the present ordered mesoporous NiO-MgO-Al2O3 materials could be considered as a series of potential catalyst candidates for CO2 methanation.

CO2reforming of Methane over Mg-promoted Ni/SiO2catalysts: the Influence of Mg Precursors and Impregnation Sequences

Meso-porous Ni/Mg/Al catalysts for methane reforming with CO2

Carbon dioxide reforming of methane over MgO-promoted Ni/SiO2 catalysts with tunable Ni particle size

Carbon Dioxide Reforming of Methane over Ni Supported SiO2: Influence of the Preparation Method on the Resulting Structural Properties and Catalytic Activity

Durable Ni/Mgo Catalysts For Co2 Reforming Of Methane: Activity And Metal-Support Interaction

Synthesis, Characterization and Catalytic Performance of MgO-coated Ni/SBA-15 Catalysts for Methane Dry Reforming to Syngas and Hydrogen

Production of Synthesis Gas Via Methane Reforming with Co2 on Ni/Sio2 Catalysts Promoted by Alkali and Alkaline Earth Metals

Carbon Dioxide Reforming of Methane over Ordered Mesoporous NiO–MgO–Al2O3 Composite Oxides

Highly dispersed Ni/MgO-mSiO2 catalysts with excellent activity and stability for dry reforming of methane

CO2 Reforming with Methane Reaction over Ni@SiO2 Catalysts Coupled by Size Effect and Metal-Support Interaction

Alkaline-promoted Ni based ordered mesoporous catalysts with enhanced low-temperature catalytic activity toward CO2 methanation

Low-temperature CO2 Reforming of Methane on Zr-promoted Ni/SiO2 Catalyst

Effects of Promoters and Preparation Procedures on Reforming of Methane with Carbon Dioxide over Ni/Al2O3 Catalyst

CO2 Methanation over Ni/Mg@MCM-41 Prepared by In-Situ Synthesis Method

Ni/SiO<sub>2</sub>Catalyst Prepared with Nickel Nitrate Precursor for Combination of CO<sub>2</sub>Reforming and Partial Oxidation of Methane: Characterization and Deactivation Mechanism Investigation

A highly active Ni catalyst supported on Mg-substituted LaAlO3 for carbon dioxide reforming of methane

Carbon Dioxide Reforming of Methane over Ni-based Catalyst

Combined Steam and CO2 Reforming of Methane over Ni-Based CeO2-MgO Catalysts: Impacts of Preparation Mode and Pd Addition

Ni/SiO2 Catalyst Prepared with Nickel Nitrate Precursor for Combination of CO2 Reforming and Partial Oxidation of Methane: Characterization and Deactivation Mechanism Investigation

Optimizing CO2 methanation: effect of surface basicity and active phase reducibility on Ni-based catalysts

Preparation of Ni-Co/SiO2 catalyst by ammonia reflux impregnation and its CH4-CO2 reforming reaction performance