Abstract:Magnetic nanoparticles (MNPs) modified simultaneously with amorphous Fe and Mn oxides (Mag-Fe-Mn) were synthesized to remove arsenite [As(III)] from water. Mag-Fe-Mn particles were fabricated through heterogeneous nucleation technique by employing the maghemite as the magnetic core and Fe Mn binary oxide (FMBO) as the coating materials. Powder X-ray diffraction, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and transmission electron microscopy were utilized to characterize the hybrid material. With a saturation magnetization of 23.2 emu/g, Mag-Fe-Mn particles with size of 20 -50 nm could be easily separated from solutions with a simple magnetic process in short time (within 5 min). At pH 7.0, 200 mu g/L of As(III) could be easily decreased to below 10 mu g/L by Mag-Fe-Mn particles (0.1 g/L) within 20 min. As(III) could be effectively removed by Mag-Fe-Mn particles at initial pH range from 4 to 8 and the residual As was completely oxidized to less toxic arsenate [As(V)]. The co-occurring redox reactions between Mn oxide and As(III) was confirmed by XPS analysis. Chloride, sulfate, bicarbonate, and nitrate at common concentration range had negligible influence on As(III) removal, whereas, silicate and phosphate reduced the As(III) removal by competing with arsenic species for adsorption sites. As(M) removal was not obviously affected by natural organic matter (up to 8 mg/L as TOC). Mag-Fe-Mn could be regenerated with ternary solution of NaOH, NaCl, and NaClO. Throughout five consecutive cycles, the adsorption and desorption efficiencies maintained above 98% and 87%, respectively. Mag-Fe-Mn had a larger adsorption capacity for As(III) (47.76 mg/g) and could remove trace As(III) more thoroughly than MNPs modified solely with either Fe or Mn oxide due to the synergistic effect of the coating Fe and Mn oxides. This research extended the potential applicability of FMBO to a great extent and provided a convenient approach to efficiently remove trace As(III) from water. (C) 2013 Elsevier Ltd. All rights reserved.

Efficient Removal of Free and Nitrilotriacetic Acid Complexed Cd(II) from Water by Poly(1-Vinylimidazole)-grafted Fe3O4@SiO2 Magnetic Nanoparticles.

Fast and Effective Removal of Cadmium Ion from Water Using Chitosan Encapsulated Magnetic Fe 3 O 4 Nanoparticles

Removal of Hg(II) by poly(1-vinylimidazole)-grafted Fe3O4@SiO2 magnetic nanoparticles.

Efficient Removal of Trace Arsenite Through Oxidation and Adsorption by Magnetic Nanoparticles Modified with Fe-Mn Binary Oxide

Novel magnetically separable anhydride-functionalized Fe3O4@SiO2@PEI-NTDA nanoparticles as effective adsorbents: synthesis, stability and recyclable adsorption performance for heavy metal ions

Enhanced adsorptive removal of Cr(III) from the complex solution by NTA-modified magnetic mesoporous microspheres

Enhanced Removal of Cd(II) Ions from Aqueous Media via Adsorption on Facilely Synthesized Copper Ferrite Nanoparticles

Degradation of diclofenac sodium with low concentration from aqueous milieu through polydopamine-chitosan modified magnetic adsorbent-assisted photo-Fenton process

Efficient Removal of Cd(II) by Core-Shell Fe3O4@polydopamine Microspheres from Aqueous Solution

Removal of arsenate by cetyltrimethylammonium bromide modified magnetic nanoparticles.

Removal of Arsenic Contaminants with Magnetic Γ-Fe2o3 Nanoparticles

Enhanced Adsorptive Removal of Cr (VI) from Plating Industry Wastewater Using CoFe2O4/CTAB Magnetic Nanocomposites

High-efficient Technique to Simultaneous Removal of Cu(II), Ni(II) and Tannic Acid with Magnetic Resins: Complex Mechanism Behind Integrative Application

Highly efficient removal of bivalent heavy metals from aqueous systems by magnetic porous Fe3O4-MnO2: Adsorption behavior and process study

As(V) adsorption by a novel core-shell magnetic nanoparticles prepared with Iron-containing water treatment residuals

Removal of As(V) from aqueous solution using modified Fe3O4 nanoparticles

High-efficiency removal of Cd(ii) and As(iii) from irrigation water using a S–Fe–C composite: performance and mechanisms

Enhanced Removal of Edta-Chelated Cu(Ii) by Polymeric Anion-Exchanger Supported Nanoscale Zero-Valent Iron

Synthesis of magnetic Fe3O4@SiO2 nanoparticles decorated with polyvinyl alcohol for Cu(II) and Cd(II) ions removal from aqueous solution

Highly selective and ultrafast removal of cadmium and copper from water by magnetic core-shell microsphere

Efficient removal of cadmium ions from water by adsorption on a magnetic carbon aerogel